Epitaxial (Ti1−
This content will become publicly available on May 23, 2025
The highest ambient‐pressure Tc among binary compounds is 40 K (MgB2). Higher Tc is achieved in high‐pressure hydrides or multielement cuprates. Alternatively, are explored superconducting properties of binary, metastable sub‐oxides, that may emerge under extremely low oxygen partial pressure. The emphasis is on the rock‐salt structure, which is known to promote superconductivity, and exploring AlO, ScO, TiO, and NbO. Dynamic lattice stability is achieved by introducing metal and oxygen vacancies in the fashion of Nb1−
- Award ID(s):
- 2132647
- PAR ID:
- 10533989
- Publisher / Repository:
- Wiley
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract x Mgx )0.25Al0.75N(0001)/Al2O3(0001) layers are used as a model system to explore how Fermi‐level engineering facilitates structural stabilization of a host matrix despite the intentional introduction of local bonding instabilities that enhance the piezoelectric response. The destabilizing octahedral bonding preference of Ti dopants and the preferred 0.67 nitrogen‐to‐Mg ratio for Mg dopants deteriorate the wurtzite AlN matrix for both Ti‐rich (x < 0.2) and Mg‐rich (x ≥ 0.9) alloys. Conversely,x = 0.5 leads to a stability peak with a minimum in the lattice constant ratioc /a , which is caused by a Fermi‐level shift into the bandgap and a trend toward nondirectional ionic bonding, leading to a maximum in the expected piezoelectric stress constante 33. The refractive index and the subgap absorption decrease withx , the optical bandgap increases, and the elastic constant along the hexagonal axisC 33= 270 ± 14 GPa remains composition independent, leading to an expected piezoelectric constantd 33= 6.4 pC N−1atx = 0.5, which is 50% larger than for the pure AlN matrix. Thus, contrary to the typical anticorrelation between stability and electromechanical coupling, the (Ti1−x Mgx )0.25Al0.75N system exhibits simultaneous maxima in the structural stability and the piezoelectric response atx = 0.5. -
more » « less
Abstract The chemical stability of 2D MXene nanosheets in aqueous dispersions must be maintained to foster their widespread application. MXene nanosheets react with water, which results in the degradation of their 2D structure into oxides and carbon residues. The latter detrimentally restricts the shelf life of MXene dispersions and devices. However, the mechanism of MXene degradation in aqueous environment has yet to be fully understood. In this work, the oxidation kinetics is investigated of Ti3C2T
x and Ti2CTx in aqueous media as a function of initial pH values, ionic strengths, and nanosheet concentrations. The pH value of the dispersion is found to change with time as a result of MXene oxidation. Specifically, MXene oxidation is accelerated in basic media by their reaction with hydroxyl anions. It is also demonstrated that oxidation kinetics are strongly dependent on nanosheet dispersion concentration, in which oxidation is accelerated for lower MXene concentrations. Ionic strength does not strongly affect MXene oxidation. The authors also report that citric acid acts as an effective antioxidant and mitigates the oxidation of both Ti3C2Tx and Ti2CTx MXenes. Reactive molecular dynamic simulations suggest that citric acid associates with the nanosheet edge to hinder the initiation of oxidation. -
more » « less
Abstract High entropy oxides (HEOs) have garnered much interest due to their available high degree of tunability. Here, we study the local structure of (MgNiCuCoZn)0.167(MnCr)0.083O, a composition based on the parent HEO (MgNiCuCoZn)0.2O. We synthesized a series of thin films via pulsed laser deposition at incremental oxygen partial pressures. X‐ray diffraction shows lattice parameters to decrease with increased pO2 pressures until the onset of phase separation. X‐ray absorption fine structure shows that specific atomic species in the composition dictate the global structure of the material as Cr, Co, and Mn shift to energetically favorable coordination with increasing pressure. Transmission electron microscopy analysis on a lower‐pressure sample exhibits a rock salt structure, but the higher‐pressure sample reveals reflections reminiscent of the spinel structure. In all, these findings give a more complete picture of how (MgNiCuCoZn)0.167(MnCr)0.083O forms with varying initial conditions and advances fundamental knowledge of cation behavior in high entropy oxides.
-
more » « less
Abstract MXenes offer high metallic conductivity and redox capacitance that are attractive for high‐power, high‐energy storage devices. However, they operate limitedly under high anodic potentials due to irreversible oxidation. Pairing them with oxides to design asymmetric supercapacitors may expand the voltage window and increase the energy storage capabilities. Hydrated lithium preintercalated bilayered V2O5(
δ ‐Lix V2O5·n H2O) is attractive for aqueous energy storage due to its high Li capacity at high potentials; however, its poor cyclability remains a challenge. To overcome its limitations and achieve a wide voltage window and excellent cyclability, it is combined with V2C and Nb4C3MXenes. Asymmetric supercapacitors employing lithium intercalated V2C (Li‐V2C) or tetramethylammonium intercalated Nb4C3(TMA‐Nb4C3) MXenes as the negative electrode, and aδ ‐Lix V2O5·n H2O composite with carbon nanotubes as the positive electrode in 5m LiCl electrolyte operate over wide voltage windows of 2 and 1.6 V, respectively. The latter shows remarkably high cyclability—capacitance retention of ≈95% after 10 000 cycles. This work highlights the importance of selecting appropriate MXenes to achieve a wide voltage window and a long cycle life in combination with oxide anodes to demonstrate the potential of MXenes beyond Ti3C2in energy storage. -
null (Ed.)A systematic study of (1− x )Pb(Fe 0.5 Nb 0.5 )O 3 – x BiFeO 3 ( x = 0–0.5) was performed by combining dielectric and electromechanical measurements with structural and microstructural characterization in order to investigate the strengthening of the relaxor properties when adding BiFeO 3 into Pb(Fe 0.5 Nb 0.5 )O 3 and forming a solid solution. Pb(Fe 0.5 Nb 0.5 )O 3 crystalizes in monoclinic symmetry exhibiting ferroelectric-like polarization versus electric field ( P–E ) hysteresis loop and sub-micron-sized ferroelectric domains. Adding BiFeO 3 to Pb(Fe 0.5 Nb 0.5 )O 3 favors a pseudocubic phase and a gradual strengthening of the relaxor behavior of the prepared ceramics. This is indicated by a broadening of the peak in temperature-dependent permittivity, narrowing of P–E hysteresis loops and decreasing size of ferroelectric domains resulting in polar nanodomains for x = 0.20 composition. The relaxor behavior was additionally confirmed by Vogel–Fulcher analysis. For the x ≥ 0.30 compositions, broad high-temperature anomalies are observed in dielectric permittivity versus temperature measurements in addition to the frequency-dispersive peak located close to room temperature. These samples also exhibit pinched P–E hysteresis loops. The observed pinching is most probably related to the reorganization of polar nanoregions under the electric field as shown by synchrotron X-ray diffraction measurements as well as by piezo-response force microscopy analysis, while in part affected by the presence of charged point defects and anti-ferroelectric order, as indicated from rapid cooling experiments and high-resolution transmission electron microscopy, respectively.more » « less