Magnetic properties and interfacial phenomena of epitaxial perovskite oxides depend sensitively on parameters such as film thickness and strain state. In this work, epitaxial La 0.67 Sr 0.33 CoO 3 (LSCO)/La 0.67 Sr 0.33 MnO 3 (LSMO) bilayers were grown on NdGaO 3 (NGO) and LaAlO 3 (LAO) substrates with a fixed LSMO thickness of 6 nm, and LSCO thickness (t LSCO ) varying from 2 to 10 nm. Soft x-ray magnetic spectroscopy revealed that magnetically active Co 2+ ions that strongly coupled to the LSMO layer were observed below a critical t LSCO for bilayers grown on both substrates. On LAO substrates, this critical thickness was 2 nm, above which the formation of Co 2+ ions was quickly suppressed leaving only a soft LSCO layer with mixed valence Co 3+ /Co 4+ ions. The magnetic properties of both LSCO and LSMO layers displayed strong t LSCO dependence. This critical t LSCO increased to 4 nm on NGO substrates, and the magnetic properties of only the LSCO layer displayed t LSCO dependence. A non-magnetic layer characterized by Co 3+ ions and with a thickness below 2 nm exists at the LSCO/substrate interface for both substrates. The results contribute to the understanding of interfacial exchange spring behavior needed for applications in next generation spintronic and magnetic memory devices.
more »
« less
Tuning In-Plane Magnetic Anisotropy and Interfacial Exchange Coupling in Epitaxial La 2/3 Sr 1/3 CoO 3 /La 2/3 Sr 1/3 MnO 3 Heterostructures
Controlling the in-plane magnetocrystalline anisotropy and interfacial exchange coupling between ferromagnetic (FM) layers plays a key role in next-generation spintronic and magnetic memory devices. In this work, we explored the effect of tuning the magnetocrystalline anisotropy of La2/3Sr1/3CoO3 (LSCO) and La2/3Sr1/3MnO3 (LSMO) layers and the corresponding effect on interfacial exchange coupling by adjusting the thickness of the LSCO layer (tLSCO). The epitaxial LSCO/LSMO bilayers were grown on (110)o-oriented NdGaO3 (NGO) substrates with a fixed LSMO (top layer) thickness of 6 nm and LSCO (bottom layer) thicknesses varying from 1 to 10 nm. Despite the small difference (∼0.2%) in lattice mismatch between the two in-plane directions, [001]o and [11̅0]o, a pronounced in-plane magnetic anisotropy was observed. Soft X-ray magnetic circular dichroism hysteresis loops revealed that for tLSCO ≤ 4 nm, the easy axes for both LSCO and LSMO layers were along the [001]o direction, and the LSCO layer was characterized by magnetically active Co2+ ions that strongly coupled to the LSMO layer. No exchange bias effect was observed in the hysteresis loops. In contrast, along the [11̅0]o direction, the LSCO and LSMO layers displayed a small difference in their coercivity values, and a small exchange bias shift was observed. As tLSCO increased above 4 nm, the easy axis for the LSCO layer remained along the [100]o direction, but it gradually rotated to the [11̅0]o direction for the LSMO layer, resulting in a large negative exchange bias shift. Therefore, we provide a way to control the magnetocrystalline anisotropy and exchange bias by tuning the interfacial exchange coupling between the two FM layers.
more »
« less
- Award ID(s):
- 1745450
- PAR ID:
- 10540532
- Publisher / Repository:
- American Chemical Society
- Date Published:
- Journal Name:
- ACS Applied Materials & Interfaces
- Volume:
- 15
- ISSN:
- 1944-8244
- Page Range / eLocation ID:
- 53086-53095
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Perovskite oxides are gaining significant attention for use in next-generation magnetic and ferroelectric devices due to their exceptional charge transport properties and the opportunity to tune the charge, spin, lattice, and orbital degrees of freedom. Interfaces between perovskite oxides, exemplified by La1−xSrxCoO3−δ/La1−xSrxMnO3−δ (LSCO/LSMO) bilayers, exhibit unconventional magnetic exchange switching behavior, offering a pathway for innovative designs in perovskite oxide-based devices. However, the precise atomic-level stoichiometric compositions and chemophysical properties of these interfaces remain elusive, hindering the establishment of surrogate design principles. We leverage first-principles simulations, evolutionary algorithms, and neural network searches with on-the-fly uncertainty quantification to design deep learning model ensembles to investigate over 50,000 LSCO/LSMO bilayer structures as a function of oxygen deficiency (δ) and strontium concentration (x). Structural analysis of the low-energy interface structures reveals that preferential segregation of oxygen vacancies toward the interfacial La0.7Sr0.3CoO3−δ layers causes distortion of the CoOx polyhedra and the emergence of magnetically active Co2+ ions. At the same time, an increase in the Sr concentration and a decrease in oxygen vacancies in the La0.7Sr0.3MnO3−δ layers tend to retain MnO6 octahedra and promote the formation of Mn4+ ions. Electronic structure analysis reveals that the nonuniform distributions of Sr ions and oxygen vacancies on both sides of the interface can alter the local magnetization at the interface, showing a transition from ferromagnetic (FM) to local antiferromagnetic (AFM) or ferrimagnetic regions. Therefore, the exotic properties of La1−xSrxCoO3−δ/La1−xSrxMnO3−δ are strongly coupled to the presence of hard/soft magnetic layers, as well as the FM to AFM transition at the interface, and can be tuned by changing the Sr concentration and oxygen partial pressure during growth. These insights provide valuable guidance for the precise design of perovskite oxide multilayers, enabling tailoring of their functional properties to meet specific requirements for various device applications.more » « less
-
Abstract The Ruddlesden‐Popper 5diridate Sr2IrO4is an antiferromagnetic Mott insulator with the electronic, magnetic, and structural properties highly intertwined. Voltage control of its magnetic state is of intense fundmenatal and technological interest but remains to be demonstrated. Here, the tuning of magnetotransport properties in 5.2 nm Sr2IrO4via interfacial ferroelectric PbZr0.2Ti0.8O3is reported. The conductance of the epitaxial PbZr0.2Ti0.8O3/Sr2IrO4heterostructure exhibits ln(T) behavior that is characteristic of 2D correlated metal, in sharp contrast to the thermally activated behavior followed by 3D variable range hopping observed in single‐layer Sr2IrO4films. Switching PbZr0.2Ti0.8O3polarization induces nonvolatile, reversible resistance modulation in Sr2IrO4. At low temperatures, the in‐plane magnetoresisance in the heterostructure transitions from positive to negative at high magnetic fields, opposite to the field dependence in single‐layer Sr2IrO4. In the polarization down state, the out‐of‐plane anisotropic magnetoresistanceRAMRexhibits sinusoidal angular dependence, with a 90° phase shift below 20 K. For the polarization up state, unusual multi‐level resistance pinning appears inRAMRbelow 30 K, pointing to enhanced magnetocrystalline anisotropy. The work sheds new light on the intriguing interplay of interface lattice coupling, charge doping, magnetoelastic effect, and possible incipient ferromagnetism in Sr2IrO4, facilitating the functional design of its electronic and material properties.more » « less
-
NiCo2O4 (NCO) films grown on MgAl2O4 (001) substrates have been studied using magnetometry and x-ray magnetic circular dichroism based on x-ray absorption spectroscopy and spin-polarized inverse photoemission spectroscopy with various thicknesses down to 1.6 nm. The magnetic behavior can be understood in terms of a layer of optimal NCO and an interfacial layer (1.2 ± 0.1 nm), with a small canting of magnetization at the surface. The thickness dependence of the optimal layer can be described by the finite-scaling theory with a critical exponent consistent with the high perpendicular magnetic anisotropy. The interfacial layer couples antiferromagnetically to the optimal layer, generating exchange-spring styled magnetic hysteresis in the thinnest films. The non-optimal and measurement-speed-dependent magnetic properties of the interfacial layer suggest substantial interfacial diffusion.more » « less
-
The ability to control and manipulate magnetic anisotropy in the colossal magnetoresistive (CMR) oxide (La,Sr)MnO3 (LSMO) is critical for its implementation in magnetic memory applications. In this work, we employ the planar Hall effect (PHE) as a powerful tool to probe the magnetic anisotropy in LSMO thin films and nanostructures, where the magnetization is too small to be detected by conventional magnetometry techniques. By analyzing the angular- and magnetic field-dependences of the PHE, we deduced an in-plane biaxial magnetocrystalline anisotropy (MCA) energy of ~1.2x10^5 erg/cm^2 in LSMO thin films fully strained on (001) SrTiO3 substrates. Creating nanoscale periodic depth modulation in LSMO establishes a uniaxial anisotropy with substantially enhanced MCA energy density, which is attributed to a high strain gradient sustained in the nanostructure. The energy competition between the biaxial and uniaxial MCA leads to multi-level resistance switching behavior in properly engineered LSMO nanostructures, which can be utilized to design the switching dynamics in magnetic memory devices. Our work points to the critical role of epitaxial strain in determining the MCA in CMR oxides, and provides an effective material strategy for engineering the magnetic properties of LSMO for novel spintronic applications with high thermal stability and high density data storage.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1021/acsami.3c10376