skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Achieving semi-metallic conduction in Al-rich AlGaN: Evidence of Mott transition
The development of high performance wide-bandgap AlGaN channel transistors with high current densities and reduced Ohmic losses necessitates extremely highly doped, high Al content AlGaN epilayers for regrown source/drain contact regions. In this work, we demonstrate the achievement of semi-metallic conductivity in silicon (Si) doped N-polar Al0.6Ga0.4N grown on C-face 4H-SiC substrates by molecular beam epitaxy. Under optimized conditions, the AlGaN epilayer shows smooth surface morphology and a narrow photoluminescence spectral linewidth, without the presence of any secondary peaks. A favorable growth window is identified wherein the free electron concentration reaches as high as ∼1.8 × 1020 cm−3 as obtained from Hall measurements, with a high mobility of 34 cm2/V·s, leading to a room temperature resistivity of only 1 mΩ·cm. Temperature-dependent Hall measurements show that the electron concentration, mobility, and sheet resistance do not depend on temperature, clearly indicating dopant Mott transition to a semi-metallic state, wherein the activation energy (Ea) falls to 0 meV at this high value of Si doping for the AlGaN films. This achievement of semi-metallic conductivity in Si doped N-polar high Al content AlGaN is instrumental for advancing ultrawide bandgap electronic and optoelectronic devices.  more » « less
Award ID(s):
2011839
PAR ID:
10541052
Author(s) / Creator(s):
; ; ; ; ;
Publisher / Repository:
American Institute of Physics Publishing
Date Published:
Journal Name:
Applied Physics Letters
Volume:
124
Issue:
24
ISSN:
0003-6951
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; (, Applied Physics Letters)
    N-polar AlGaN is an emerging wide-bandgap semiconductor for next-generation high electron mobility transistors and ultraviolet light emitting diodes and lasers. Here, we demonstrate the growth and characterization of high-quality N-polar AlGaN films on C-face 4H-silicon carbide (SiC) substrates by molecular beam epitaxy. On optimization of the growth conditions, N-polar AlGaN films exhibit a crack free, atomically smooth surface (rms roughness ∼ 0.9 nm), and high crystal quality with low density of defects and dislocations. The N-polar crystallographic orientation of the epitaxially grown AlGaN film is unambiguously confirmed by wet chemical etching. We demonstrate precise compositional tunability of the N-polar AlGaN films over a wide range of Al content and a high internal quantum efficiency ∼74% for the 65% Al content AlGaN film at room temperature. Furthermore, controllable silicon (Si) doping in high Al content (65%) N-polar AlGaN films has been demonstrated with the highest mobility value ∼65 cm2/V-s observed corresponding to an electron concentration of 1.1 × 1017 cm−3, whereas a relatively high mobility value of 18 cm2/V-s is sustained for an electron concentration of 3.2 × 1019 cm−3, with an exceptionally low resistivity value of 0.009 Ω·cm. The polarity-controlled epitaxy of AlGaN on SiC presents a viable approach for achieving high-quality N-polar III-nitride semiconductors that can be harnessed for a wide range of emerging electronic and optoelectronic device applications. 
    more » « less
  2. ; ; ; ; ; ; ; (, Applied Physics Letters)
    Polarization-induced carriers play an important role in achieving high electrical conductivity in ultrawide bandgap semiconductor AlGaN, which is essential for various applications ranging from radio frequency and power electronics to deep UV photonics. Despite significant scientific and technological interest, studies on polarization-induced carriers in N-polar AlGaN are rare. We report the observation and properties of polarization-induced two-dimensional electron gases (2DEGs) in N-polar AlGaN/AlN heterostructures on single-crystal AlN substrates by systematically varying the Al content in the 8 nm top layers from x = 0 to x = 0.6, spanning energy bandgaps from 3.56 to 4.77 eV. The 2DEG density drops monotonically with increasing Al content, from 3.8 × 1013/cm2 in the GaN channel, down to no measurable conductivity for x = 0.6. Alloy scattering limits the 2DEG mobility to below 50 cm2/V s for x = 0.49. These results provide valuable insights for designing N-polar AlGaN channel high electron mobility transistors on AlN for extreme electronics at high voltages and high temperatures, and for UV photonic devices. 
    more » « less
  3. ; ; ; (, Applied Physics Letters)
    Obtaining uniform silicon concentration, especially with low concentrations (ranging from 1 × 1016 to 1 × 1018 cm−3) by molecular beam epitaxy, has been challenging due to oxidation of a silicon solid source in the oxide environment. In this work, Si doping of β-Ga2O3 (010) films by diluted disilane as the Si source is investigated using hybrid plasma-assisted molecular beam epitaxy. The impact of growth temperature, disilane source concentration, and disilane flow rate on Si incorporation was studied by secondary ion mass spectrometry. Uniform Si concentrations ranging from 3 × 1016 to 2 × 1019 cm−3 are demonstrated. Si-doped β-Ga2O3 films with different silicon concentrations were grown on Fe-doped β-Ga2O3 (010) substrates. The electron concentration and mobility were determined using van de Pauw Hall measurements. A high mobility of 135 cm2/V s was measured for an electron concentration of 3.4 × 1017 cm−3 at room temperature. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, Applied Physics Letters)
    The ultra-wide bandgap of Al-rich AlGaN is expected to support a significantly larger breakdown field compared to GaN, but the reported performance thus far has been limited by the use of foreign substrates. In this Letter, the material and electrical properties of Al 0.85 Ga 0.15 N/Al 0.6 Ga 0.4 N high electron mobility transistors (HEMT) grown on a 2-in. single crystal AlN substrate are investigated, and it is demonstrated that native AlN substrates unlock the potential for Al-rich AlGaN to sustain large fields in such devices. We further study how Ohmic contacts made directly to a Si-doped channel layer reduce the knee voltage and increase the output current density. High-quality AlGaN growth is confirmed via scanning transmission electron microscopy, which also reveals the absence of metal penetration at the Ohmic contact interface and is in contrast to established GaN HEMT technology. Two-terminal mesa breakdown characteristics with 1.3  μm separation possess a record-high breakdown field strength of ∼11.5 MV/cm for an undoped Al 0.6 Ga 0.4 N-channel layer. The breakdown voltages for three-terminal devices measured with gate-drain distances of 4 and 9  μm are 850 and 1500 V, respectively. 
    more » « less
  5. ; ; ; ; ; ; ; ; (, Applied Physics Letters)
    The polarization difference and band offset between Al(Ga)N and GaN induce two-dimensional (2D) free carriers in Al(Ga)N/GaN heterojunctions without any chemical doping. A high-density 2D electron gas (2DEG), analogous to the recently discovered 2D hole gas in a metal-polar structure, is predicted in a N-polar pseudomorphic GaN/Al(Ga)N heterostructure on unstrained AlN. We report the observation of such 2DEGs in N-polar undoped pseudomorphic GaN/AlGaN heterostructures on single-crystal AlN substrates by molecular beam epitaxy. With a high electron density of ∼4.3 ×1013/cm2 that maintains down to cryogenic temperatures and a room temperature electron mobility of ∼450 cm2/V s, a sheet resistance as low as ∼320 Ω/◻ is achieved in a structure with an 8 nm GaN layer. These results indicate significant potential of AlN platform for future high-power RF electronics based on N-polar III-nitride high electron mobility transistors. 
    more » « less