{"Abstract":["BSE mosaics of mushes and experimental products.\n\nAbstract: "We conducted experiments to study melt migration in crystal-rich mushes, with application to magma ascent within transcrustal magma reservoirs. Mushes with crystal volume fractions of 0.59 to 0.83 were prepared by hot-pressing crushed borosilicate glass mixed with different amounts quartz sand particles. Each experimental sample comprises stacked disks of mush and soda-lime glass, a proxy for crystal-free magma. Samples were subjected to confining pressures of 100 to 300 MPa and a temperature of 900°C (above the glass transition temperatures of the borosilicate and soda-lime glasses) for up to 6 h. The bottom and circumference of the mush and soda lime disks experience the confining pressure, but the top of the mush disks are at room pressure, resulting in a pore-pressure gradient across the mush layer. Following cooling and decompression, we determined the area fraction and morphology of soda-lime melt that migrated into the mush layer during experiments. Melt fraction is more strongly correlated to crystal fraction than pore-pressure gradient, increasing with crystal fraction before sharply decreasing as crystal fractions exceed 0.8. This change at 0.8 coincides with the transition from crystals in the mush moving during soda-lime migration to crystals forming a continuous rigid network. In our experiments, melt migration occurred by viscous fingering, but near the mobile-to-rigid transition, melt migration is enhanced by additional capillary action. Our results indicate that magma migration may peak when rigid mushes \u201cunlock\u201d to become mobile. This transition may mark an increase in magma migration, a potential precursor to volcanic unrest and eruption."\n\nImaging: "Transverse sections cut from the top and/or bottom of the vacuum hot-pressed mushes were polished, carbon-coated, and imaged in BSE mode using the JEOL JXA-8530FPlus Electron Probe Microanalyzer (EPMA) at UMN (15 kV, 10 nA). About ten 50x magnification images were taken per sample and then compiled into BSE mosaics using Affinity Designer. The different compositions of the borosilicate glass and crystalline materials are distinguishable by greyscale in BSE images. [...] Following each experiment, sample assemblies were cut longitudinally along the cylindrical axis to produce sections for microstructural analysis. Scored samples (pHi-19s, Int-20s, Lo-21s) were cut again to produce sections tangential to the sample cylinder. Cut sections were vacuum impregnated with EpoFix resin and hand-polished on diamond lapping film from 30 to 0.5 μm grit. Polished and carbon-coated samples were imaged in BSE mode in the EPMA at UMN (15 kV, 10 nA). The different compositions of the soda-lime glass, borosilicate glass, and crystalline materials are distinguishable by greyscale in BSE images. Twenty to forty 50x magnification images were taken per sample and then compiled into sample-scale BSE mosaics using Affinity Designer.""]}
more »
« less
This content will become publicly available on March 21, 2026
Effect of metallic silver particles on the luminescence spectrum of Sm3+ -doped oxide glass
Tellurium oxide-based glasses were made by the melt quenching technique. Appropriate quantities of the chemicals were weighed, mixed/ ground, and then melted above the melting point for an hour. Samarium and Silver compound were added to the starting chemicals. The melt was poured into an aluminum mold to get different shapes and sizes. The spectroscopic characterization of the samples was done by using different laser excitation sources. Silver metallic particles were induced by heat treating the glass above its glass transition temperature. Absorption and emission measurements revealed enhanced characteristics.
more »
« less
- Award ID(s):
- 2331969
- PAR ID:
- 10591442
- Editor(s):
- Digonnet, Michel J; Jiang, Shibin
- Publisher / Repository:
- SPIE
- Date Published:
- Volume:
- 13362
- ISSN:
- 0277-786X
- ISBN:
- 9781510684720
- Page Range / eLocation ID:
- 1336214-6
- Subject(s) / Keyword(s):
- Tellurium oxide glass. absorption, fluorescence, lifetimes, nanoparticles, plasmonic effects
- Format(s):
- Medium: X
- Location:
- San Francisco, United States
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract We conducted experiments to study melt migration in crystal‐rich mushes, with application to magma ascent within transcrustal magma reservoirs. Mushes with crystal volume fractions of 0.59–0.83 were prepared by hot‐pressing crushed borosilicate glass mixed with different proportions of quartz sand particles. Each experimental sample comprises stacked disks of mush and soda‐lime glass, a proxy for crystal‐free magma. Samples were subjected to confining pressures of 100–300 MPa and a temperature of 900°C (above the glass transition temperatures of the borosilicate and soda‐lime glasses) for up to 6 h. The bottom and circumference of the mush and soda lime disks experience the confining pressure, but the top of the mush disks is at room pressure, resulting in a pore‐pressure gradient across the mush layer. Following cooling and decompression, we determined the area fraction and morphology of soda‐lime melt that migrated into the mush layer during experiments. Melt fraction is more strongly correlated to crystal fraction than pore‐pressure gradient, increasing with crystal fraction before sharply decreasing as crystal fractions exceed 0.8. This change at 0.8 coincides with the transition from crystals in the mush moving during soda‐lime migration to crystals forming a continuous rigid network. In our experiments, melt migration occurred by viscous fingering, but near the mobile‐to‐rigid transition, melt migration is enhanced by additional capillary action. Our results indicate that magma migration may peak when rigid mushes “unlock” to become mobile. This transition may mark an increase in magma migration, a potential precursor to volcanic unrest and eruption.more » « less
-
Abstract The preparation of 0.58 Li2S + 0.315 SiS2+ 0.105 LiPO3glass, and the impacts of polysulfide and P1Pdefect structure impurities on the glass transition temperature (Tg), crystallization temperature (Tc), working range (ΔT≡ Tc‐ Tg), fragility index, and the Raman spectra were evaluated using statistical analysis. In this study, 33 samples of this glass composition were synthesized through melt‐quenching. Thermal analysis was conducted to determine the glass transition temperature, crystallization temperature, working range, and fragility index through differential scanning calorimetry. The quantity of the impurities described above was determined through Raman spectroscopy peak analysis. Elemental sulfur was doped into a glass to quantify the wt% sulfur content in the glasses. Linear regression analysis was conducted to determine the impact of polysulfide impurities and P1Pdefect impurities on the thermal properties. Polysulfide impurities were found to decrease theTgat rate of nearly 12°C per 1 wt% increase in sulfur concentration. The sulfur concentration does not have a statistically significant impact on the other properties (α = 0.05). The P1Pdefect structure appears to decrease the resistance to crystallization of the glass by measurably decreasing the working range of the glasses, but further study is necessary to fully quantify and determine this.more » « less
-
The fish intestine is an important barrier for environmental toxicants, including metals and metal nanoparticles. Tracking chemical transformation at the interface between the intestinal epithelium and the intestinal lumen can inform us about chemicals' bio-reactivity and toxicity but is challenging due to the lack of appropriate models. To allow for such investigations, a model of the fish intestine derived from rainbow trout ( Oncorhynchus mykiss ), the RTgutGC cell line, was used. Cells were exposed to silver nitrate (AgNO 3 ) or citrate coated silver nanoparticles (cit-AgNPs) in Leibovitz's L-15 medium without amino acids and vitamins (L-15/ex), which allowed the determination of the extracellular silver species using a chemical equilibrium model. X-ray absorption spectroscopy (XAS) was used to track intracellular silver speciation. Cellular toxicity, silver accumulation, and metallothionein (MT) mRNA levels were also measured. Cells accumulated the same concentrations of silver when exposed to equimolar amounts ( i.e. 1, 5 and 10 μM) of AgNO 3 or cit-AgNPs. However, AgNO 3 was shown to be more toxic than cit-AgNPs. Intracellular silver speciation changed over time in both exposure series. After 1 hour, intracellular silver speciation was dominated by chloride complexation in both exposures. After 24 and 72 hours of exposure to cit-AgNPs, ∼7% of silver was complexed to cysteine, whereas the remaining silver was AgNPs. In cells exposed to AgNO 3 for 72 hours, 97% of Ag was complexed to cysteine. A significant increase, compared to controls, in metallothionein mRNA levels at 24 and 72 hours of exposure to AgNO 3 and cit-AgNPs can explain the formation of Ag–cysteine complexes. In summary, these data show that silver chloride species are bioavailable and that complexation to cysteine scavenges intracellular dissolved silver ions, thus preventing toxicity. Silver nanoparticles present a similar but attenuated toxic response to AgNO 3 . Thus, at least in acute exposures, existing risk assessment for dissolved silver species could be protective for nanosilver.more » « less