The future of aerospace structures is highly dependent on the advancement of reliable and high-performance materials, such as composite materials and metals. Innovation in high resolution non-invasive evaluation of these materials is needed for their qualification and monitoring for structural integrity. Aluminum oxide (or α-alumina) nanoparticles present photoluminescent properties that allow stress and damage sensing via photoluminescence piezospectroscopy. This work describes how these nanoparticles are added into a polymer matrix to create functional coatings that monitor the damage of the underlying composite or metallic substrates. Different volume fractions of α-alumina nanoparticles in the piezospectroscopic coatings were studied for determining the sensitivity of the coatings and successful damage detection was demonstrated for an open-hole tension composite substrate as well as 2024 aluminum tensile substrates with a subsurface notch.
more »
« less
Measurements for stress sensing of composites using tailored piezospectroscopic coatings
Chromium-doped α-alumina is naturally photo-luminescent with spectral properties that are characterized by R-lines with two distinct peaks known as R1 and R2. When the material is subjected to stress, shifts in the R-lines occur, which is known as the piezospectroscopic (PS) effect. Recent work has shown that improved sensitivity of the technique can be achieved through a configuration of nanoparticles within a polymer matrix, which can be applied to a structure as a stress-sensing coating. This study demonstrates the capability of PS coatings in mechanical tests and investigates the effect of nanoparticle volume fraction on sensing performance. Here, measurements of spectral shifts that capture variation in stress of the coating during mechanical testing and in the region of substrate damage showed that stress contours are more noticeable on a soft laminate than hard laminate. It was found that the 20 % volume fraction PS coating showed the most distinct features of all the coatings tested with the highest signal-to-noise ratio and volume fraction of α-alumina. Post failure assessment of the PS coatings verified that the coatings were intact and peak shifts observed during mechanical testing were due to the stress in the substrate. The results suggest the ability to design and tailor the “sensing” capability of these nanoparticles and correlate the measured stress variations with the presence of stress and damage in underlying structures. This study is relevant to nondestructive evaluation in the aerospace industry, where monitoring signs of damage is of significance for testing of new materials, quality control in manufacturing and inspections during maintenance.
more »
« less
- Award ID(s):
- 1701983
- PAR ID:
- 10597282
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- AIP Advances
- Volume:
- 9
- Issue:
- 5
- ISSN:
- 2158-3226
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Self-sufficient and non-contact sensors play multiple roles in lunar, planetary exploration, and Earth structures. These sensors allow engineers to accurately examine structural integrity and defects on mechanical components for optimal operations. Structural integrity allows the industry to ensure the safety and capacity of key structures. Materials like α-alumina can be employed as sensors due to the photoluminescent properties that they possess. Piezospectroscopy is a non-destructive evaluation (NDE) method capable of capturing in-situ stress using α-alumina due to the chromium ion impurities that it contains. The chromium ion impurities carry spectral characteristics, that when excited with an Nd: YAG laser (532 nm), demonstrate capabilities for structural integrity monitoring. In this work, a 3D printing method is developed to autonomously create sensors that are compatible with use in space environments. The 3D printing method intends to provide the industry flexible and adaptive solutions for structural integrity monitoring. This method includes a modified Fused Deposition Method printer by exchanging its original nozzle with a syringe base nozzle. The printing parameters such as printing speed, printing bed temperature, coating thickness, and syringe volume are determined during the testing process. Challenges include achieving uniform integration and nanoparticle dispersion as well as adhesion between the matrix and the substrates. The parameters to encounter these challenges will depend on the materials used. Experiments with three different volume fractions (VF) of α-alumina within an epoxy were performed to address the printing challenges. The sensors were applied to nine specimens, three of each VF but with varying deposition rates after the mixture process. These experiments considered the mixing and deposition method while testing the dispersion within the α-alumina and the epoxy matrix. The substrates, on which the epoxy matrix was deposited, underwent a surface treatment to ensure adhesion between the substrate and the sensor matrix. During this experiment, the epoxy matrix was deposited with a syringe onto a substrate and cured at room temperature. The specimens were tested with a tensile load using an electromechanical MTS. While the samples are tensile loaded, the sensors were characterized via photoluminescent piezo spectroscopy to determine which VF demonstrates the best stress sensing capabilities, along with the adhesion between the matrix and the substrate. The data collected allows the optimal VF to be established for future applications.more » « less
-
In this study, hydrophilic silica nanoparticles (Si NPs) were used to modify α-alumina tubular membranes to improve their performance in terms of flux, oil rejection, and anti-fouling properties. Our work focuses on enhancing membrane performance, particularly for difficult applications such as produced water treatment. The prepared membranes were applied for oil-in-water emulsion treatment. After coating hydrophilic Si NPs, the oil contact angle improved from 133.8° to 171.4°. To prevent Si NPs from leaching off the surface of α-alumina tubular membranes, polyvinyl alcohol was used to coat the membranes as a pre-treatment step before Si NP modification. After coating the membrane with Si NPs, the roughness of the membrane surface decreased, likely leading to less fouling. After coating Si NPs, Total Organic Carbon rejection increased from 93.1% for pristine α-alumina tubular membranes to 97.7% for silica-modified membranes because of hydrophilic improvements of the modified membranes. The Si NP coating improved the anti-fouling property of membranes with the flux recovery ratio increasing from 71.3% for pristine α-alumina tubular membranes to 85.9% for silica-modified membranes. Scanning Electron Microscopy, Energy- dispersive X-ray spectroscopy, oil contact angle, and Atomic Force Microscopy characterization tests were done. The tests showed successful Si NPs impregnation and altered wettability.more » « less
-
null (Ed.)Processing and characterization for zirconia toughened alumina (ZTA) coatings on Ti6Al4V (Ti64) alloy by directed energy deposition (DED)-based additive manufacturing (AM) is presented here. The objective of the study was to achieve a dense ZTA coating with the intent of providing an alternative to fully ceramic implants for articulating surfaces of total hip arthroplasty (THA). Preliminary work resulted in failed samples due to cracking, porosity, and delamination. After careful parameter optimization, a Ti64+5wt.%ZTA (5ZTA) composition produced a metallurgically sound and coherent coating with minimal porosity. Additionally, bulk structures were also feasible with the optimized coating parameters. Characterization of the 5ZTA composition displayed a 27.0% increase in hardness, 25% reduction in normalized wear rate, an increase in contact resistance during in vitro tribological testing along with a faster surface re-passivation post-tribological testing.more » « less