Polymer infiltrated nanoporous gold is prepared by infiltrating polymer melts into a bicontinuous, nanoporous gold (NPG) scaffold. Polystyrene (PS) films with molecular weights (Mw) from 424 to 1133 kDa are infiltrated into a NPG scaffold (∼120 nm), with a pore radius (Rp) and pore volume fraction of 37.5 nm and 50%, respectively. The confinement ratios (Γ=RgRp) range from 0.47 to 0.77, suggesting that the polymers inside the pores are moderately confined. The time for PS to achieve 80% infiltration (τ80%) is determined using in situ spectroscopic ellipsometry at 150 °C. The kinetics of infiltration scales weaker with Mw, τ80%∝Mw1.30±0.20, than expected from bulk viscosity Mw3.4. Furthermore, the effective viscosity of the PS melt inside NPG, inferred from the Lucas–Washburn model, is reduced by more than one order of magnitude compared to the bulk. Molecular dynamics simulation results are in good agreement with experiments predicting scaling as Mw1.4. The reduced dependence of Mw and the enhanced kinetics of infiltration are attributed to a reduction in chain entanglement density during infiltration and a reduction in polymer–wall friction with increasing polymer molecular weight. Compared to the traditional approach involving adding discrete particles into the polymer matrix, these studies show that nanocomposites with higher loading can be readily prepared, and that kinetics of infiltration are faster due to polymer confinement inside pores. These films have potential as actuators when filled with stimuli-responsive polymers as well as polymer electrolyte and fuel cell membranes.
more »
« less
This content will become publicly available on April 15, 2026
Polymer–Wall Interactions Slow Infiltration Dynamics in Bicontinuous, Nanoporous Structures
Polymer infiltration is studied in a bicontinuous, nanoporous gold (NPG) scaffold. For poly(2-vinylpyridine) (P2VP) with molecular weights (M_w) from 51k to 940k Da, infiltration is investigated in a NPG with fixed pore radius (R_p= 34 nm) under moderate confinement (Γ = R_g/R_p ) 0.18 to 0.78. The time for 80% infiltration (τ_(80%)) scales as M_w^1.43, similar to PS, but weaker than bulk behavior. Infiltration of P2VP is slower than PS due to stronger P2VP-wall interactions resulting in a physisorbed P2VP layer. This interpretation is supported by the similar scaling of τ_(80%) for P2VP and PS, as well as Molecular Dynamics (MD) simulations. Simulations show that infiltration time scales as M_w^1.43and that infiltration slows as the polymer-wall attraction increases. As M_w increases, the effective viscosity transitions from greater than to less than the bulk viscosity due to pore narrowing and a reduction entanglement density. These studies provide new insight for polymer behavior under confinement and a new route for preparing nanocomposites at high filler loadings.
more »
« less
- Award ID(s):
- 2407300
- PAR ID:
- 10598403
- Publisher / Repository:
- ACS
- Date Published:
- Journal Name:
- Macromolecules
- Volume:
- 58
- Issue:
- 10
- ISSN:
- 0024-9297
- Page Range / eLocation ID:
- 5058 to 5070
- Subject(s) / Keyword(s):
- Nanocomposite, adsorption, infiltration
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
POLYMER INFILTRATED NANOPOROUS GOLD: KINETICS AND OPTICAL PROPERTIES OF NOVEL POLYMER NANOCOMPOSITESOne of the biggest challenges in the field of polymer nanocomposites (PNCs) is to disperse high nanofiller loadings into the polymeric matrix. The high loading and uniform dispersion are limited by the unfavored polymer/nanofiller thermodynamics and the tendency for nanofiller to aggregate. In this thesis, these are circumvented by using nanoporous gold (NPG) as a scaffold for polymers to fill. The ultra-high loading (>50 vol%) is achieved by infiltrating polymer melts into NPG to produce a polymer infiltrated nanoporous gold (PING) composite. This novel composite provides promises for the next generation advanced materials for coating, optical sensors, actuators, and batteries. This thesis contributes to the better understanding of polymer kinetics under moderate confinement by varying the interfacial energy between polymer and pore wall and investigating the temperature dependence of infiltration. Confinement enhances polymer kinetics while decreasing the infiltration time dependence on Mw due to the combined effect of loss in entanglement and adsorbed chain fraction. When polymer and the wall interfacial energy is stronger, a physiosorbed layer forms, resulting in slower kinetics compared to that for weaker interfacial energy. The temperature dependence of the polymer kinetics inside NPG follows the bulk WLF behavior at lower confinement degrees, while the kinetics deviate from the bulk WLF at higher confinement levels due to the decrease in thermal expansion coefficient. Those fundamental studies on polymer kinetics enable the optimization of preparing PING composites for the use of industrial scale applications and encourage additional studies such as ion conductivities of PING. The optical properties study established UV-Vis spectroscopy as a new approach to track polymer kinetics while simultaneously broadening the potential PING applications to optically responsive membranes. This thesis presents a pathway of fabricating PING composite while kinetics studies as well as the optical study enable scientists to better understand polymers behavior under confinement and advance the toolbox for creating interconnected polymer/filler systems at high filler concentrations.more » « less
-
We explore the effect of confinement and polymer–nanoparticle interactions on the viscosity of unentangled polymers undergoing capillary rise infiltration (CaRI) in dense packings of nanoparticles. In CaRI, a polymer is thermally induced to wick into the dense packings of nanoparticles, leading to the formation of polymer-infiltrated nanoparticle films, a new class of thin film nanocomposites with extremely high concentrations of nanoparticles. To understand the effect of this extreme nanoconfinement, as well as polymer–nanoparticle interactions on the polymer viscosity in CaRI films, we use two polymers that are known to have very different interactions with SiO 2 nanoparticles. Using in situ spectroscopic ellipsometry, we monitor the polymer infiltration process, from which we infer the polymer viscosity based on the Lucas–Washburn model. Our results suggest that physical confinement increases the viscosity by approximately two orders of magnitude. Furthermore, confinement also increases the glass transition temperature of both polymers. Thus, under extreme nanoconfinement, the physical confinement has a more significant impact than the polymer–nanoparticle interactions on the viscosity of unentangled polymers, measured through infiltration dynamics, as well as the glass transition temperature. These findings will provide fundamental frameworks for designing processes to enable the fabrication of CaRI nanocomposite films with a wide range of nanoparticles and polymers.more » « less
-
Abstract The effect of nanoconfinement on the kinetics of benzyl methacrylate radical polymerization is investigated using differential scanning calorimetry. Controlled pore glass (CPG), ordered mesoporous carbons, and mesoporous silica are used as confinement media with pore sizes from 2 to 8 nm. The initial polymerization rate in CPG and mesoporous silica increases relative to the bulk and increases linearly with reciprocal pore size; whereas, the rate in the carbon mesopores decreases linearly with reciprocal pore size; the changes are consistent with the rate being related to the ratio of the pore surface area to pore volume. Induction times are longer for nanoconfined polymerizations, and in the case of CPG and carbon mesopores, autoacceleration occurs earlier, presumably due to the limited diffusivity and lower termination rates for the confined polymer chains. The molecular weight of the polymer synthesized in the nanopores is generally higher than that obtained in the bulk except at the lowest temperatures investigated. The equilibrium conversion under nanoconfinement decreases with decreasing temperature and with confinement size, exhibiting what appears to be a floor temperature at low temperatures.more » « less
-
Broadband dielectric spectroscopy is employed to probe dynamics in low molecular weight poly(cis-1,4-isoprene) (PI) confined in unidirectional silica nanopores with mean pore diameter, D, of 6.5nm. Three molecular weights of PI (3, 7 and 10kg/mol) were chosen such that the ratio of D to the polymer radius of gyration, Rg, is varied from 3.4, 2.3 to 1.9, respectively. It is found that the mean segmental relaxation rate remains bulk-like but an additional process arises at lower frequencies with increasing molecular weight (decreasing D/Rg). In contrast, the mean relaxation rates of the end-to-end dipole vector corresponding to chain dynamics are found to be slightly slower than that in the bulk for the systems approaching D/Rg ∼ 2, but faster than the bulk for the polymer with the largest molecular weight. The analysis of the spectral shapes of the chain relaxation suggests that the resulting dynamics of the 10 kg/mol PI confined at length-scales close to that of the Rg are due to non-ideal chain conformations under confinement decreasing the chain relaxation times. The understanding of these faster chain dynamics of polymers under extreme geometrical confinement is necessary in designing nanodevices that contain polymeric materials within substrates approaching the molecular scale.more » « less