Abstract Metal–organic frameworks (MOFs) are promising materials for electrocatalysis; however, lack of electrical conductivity in the majority of existing MOFs limits their effective utilization in the field. Herein, an excellent catalytic activity of a 2D copper (Cu)‐based conductive MOF, copper tetrahydroxyquinone (CuTHQ), is reported for aqueous CO2reduction reaction (CO2RR) at low overpotentials. It is revealed that CuTHQ nanoflakes (NFs) with an average lateral size of 140 nm exhibit a negligible overpotential of 16 mV for the activation of this reaction, a high current density of ≈173 mA cm−2at −0.45 V versus RHE, an average Faradaic efficiency (F.E.) of ≈91% toward CO production, and a remarkable turnover frequency as high as ≈20.82 s−1. In the low overpotential range, the obtained CO formation current density is more than 35 and 25 times higher compared to state‐of‐the‐art MOF and MOF‐derived catalysts, respectively. The operando Cu K‐edge X‐ray absorption near edge spectroscopy and density functional theory calculations reveal the existence of reduced Cu (Cu+) during CO2RR which reversibly returns to Cu2+after the reaction. The outstanding CO2catalytic functionality of conductive MOFs (c‐MOFs) can open a way toward high‐energy‐density electrochemical systems.
more »
« less
Non‐Aqueous Electrochemical CO 2 Reduction to Multivariate C 2 ‐Products Over Single Atom Catalyst at Current Density up to 100 mA cm −2
Abstract Electrochemical CO2reduction reaction (CO2‐RR) in non‐aqueous electrolytes offers significant advantages over aqueous systems, as it boosts CO2solubility and limits the formation of HCO3−and CO32−anions. Metal–organic frameworks (MOFs) in non‐aqueous CO2‐RR makes an attractive system for CO2capture and conversion. However, the predominantly organic composition of MOFs limits their electrical conductivity and stability in electrocatalysis, where they suffer from electrolytic decomposition. In this work, electrically conductive and stable Zirconium (Zr)‐based porphyrin MOF, specifically PCN‐222, metalated with a single‐atom Cu has been explored, which serves as an efficient single‐atom catalyst (SAC) for CO2‐RR. PCN‐ 222(Cu) demonstrates a substantial enhancement in redox activity due to the synergistic effect of the Zr matrix and the single‐atom Cu site, facilitating complete reduction of C2species under non‐aqueous electrolytic conditions. The current densities achieved (≈100 mA cm−2) are 4–5 times higher than previously reported values for MOFs, with a faradaic efficiency of up to 40% for acetate production, along with other multivariate C2products, which have never been achieved previously in non‐aqueous systems. Characterization using X‐ray and various spectroscopic techniques, reveals critical insights into the role of the Zr matrix and Cu sites in CO2reduction, benchmarking PCN‐222(Cu) for MOF‐based SAC electrocatalysis.
more »
« less
- PAR ID:
- 10600231
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small
- Volume:
- 21
- Issue:
- 18
- ISSN:
- 1613-6810
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Utilizing metal–organic frameworks (MOFs) as reinforcing fillers for polymer composites is a promising strategy because of the low density, high specific modulus, and tunable aspect ratio (AR). However, it has not been demonstrated for the MOF-reinforced polymer composite using MOFs with high AR and polymer-grafted surface, both of which are extremely important factors for efficient load transfer and favorable particle–matrix interaction. To this end, we designed an MOF–polymer composite system using high AR MOF PCN-222 as the mechanical reinforcer. Moreover, we developed a synthetic route to graft poly(methyl methacrylate) (PMMA) from the surface of PCN-222 through surface-initiated atomic transfer radical polymerization (SI-ATRP). The successful growth of PMMA on the surface of PCN-222 was confirmed via proton nuclear magnetic resonance and infrared spectroscopy. Through thermogravimetric analysis, the grafting density was found to be 0.18 chains/nm2. The grafted polymer molecular weight was controlled ranging from 50.3 to 158 kDa as suggested by size exclusion chromatography. Finally, we fabricated MOF–polymer composite films by the doctor-blading technique and measured the mechanical properties through the tension mode of dynamic mechanical analysis. We found that the mechanical properties of the composites were improved with increasing grafted PMMA molecular weight. The maximum reinforcement, a 114% increase in Young’s modulus at 0.5 wt % MOF loading in comparison to pristine PMMA films, was achieved when the grafted molecular weight was higher than the matrix molecular weight, which was in good agreement with previous literature. Moreover, our composite presents the highest reinforcement measured via Young’s modulus at low weight loading among MOF-reinforced polymer composites due to the high MOF AR and enhanced interface. Our approach offers great potential for lightweight mechanical reinforcement with high AR MOFs and a generalizable grafting-from strategy for porphyrin-based MOFs.more » « less
-
Abstract Electrochemical CO2reduction (CO2RR) on copper (Cu) shows promise for higher‐value products beyond CO. However, challenges such as the limited CO2solubility, high overpotentials, and the competing hydrogen evolution reaction (HER) in aqueous electrolytes hinder the practical realization. We propose a functionalized ionic liquid (IL) which generates ion‐CO2adducts and a hydrogen bond donor (HBD) upon CO2absorption to modulate CO2RR on Cu in a non‐aqueous electrolyte. As revealed by transient voltammetry, electrochemical impedance spectroscopy (EIS), and in situ surface‐enhanced Raman spectroscopy (SERS) complemented with image charge augmented quantum‐mechanical/molecular mechanics (IC‐QM/MM) computations, a unique microenvironment is constructed. In this microenvironment, the catalytic activity is primarily governed by the IL and HBD concentrations; former controlling the double layer thickness and the latter modulating the local proton availability. This translates to ample CO2availability, reduced overpotential, and suppressed HER where C4products are obtained. This study deepens the understanding of electrolyte effects in CO2RR and the role of IL ions towards electrocatalytic microenvironment design.more » « less
-
Abstract Hybrid organic‐inorganic heterogeneous catalytic interfaces, where traditional catalytic materials are modified with self‐assembled monolayers (SAMs), create promising features to control a wide range of catalytic processes through the design of dual organic‐inorganic active sites and the induced confinement effect. To provide a fundamental insight, we investigated CO2electroreduction into valuable C2chemicals (CO2RR‐to‐C2) over SAM‐modulated Cu. Our theoretical results show that 1/4 monolayer aminothiolates improve the stability, activity and selectivity of CO2RR‐to‐C2by: (1) decreasing surface energy to suppress surface reconstruction; (2) facilitating CO2activation and C−C coupling through dual organic‐inorganic (i. e., −NH, Cu) active sites; (3) promoting C−C coupling via confinement effects that enlarge the adsorption energy difference between CO*and COH*; (4) inducing local electric fields to Cu surface and changing its dipole moment and polarizability to be in favor of C−C coupling under electrode/electrolyte interfacial electric field.more » « less
-
Abstract Charge‐separated metal–organic frameworks (MOFs) are a unique class of MOFs that can possess added properties originating from the exposed ionic species. A new charge‐separated MOF, namely, UNM‐6 synthesized from a tetrahedral borate ligand and Co2+cation is reported herein. UNM‐6 crystalizes into the highly symmetricP43nspace group with fourfold interpenetration, despite the stoichiometric imbalance between the B and Co atoms, which also leads to loosely bound NO3−anions within the crystal structure. These NO3−ions can be quantitatively exchanged with various other anions, leading to Lewis acid (Co2+) and Lewis base (anions) pairs within the pores and potentially cooperative catalytic activities. For example, UNM‐6‐Br, the MOF after anion exchange with Br−anions, displays high catalytic activity and stability in reactions of CO2chemical fixation into cyclic carbonates.more » « less