In this work, we performed in situ nanoindentation in TEM to capture the real-time 〈c + a〉 dislocation and twinning activities in pure Mg during loading and unloading. We demonstrated that the screw component of 〈c + a〉 dislocations glides continuously, while the edge components rapidly become sessile during loading. The twin tip propagation is intermittent, whereas the twin boundary migration is more continuous. During unloading, we observed the elastic strain relaxation causes both 〈c + a〉 dislocation retraction and detwinning. Moreover, we note that the plastic zone comprised of 〈c + a〉 dislocations in Mg is well-defined, which contrasts with the diffused plastic zones observed in face-centered cubic metals under the nanoindentation impressions. Additionally, molecular dynamics simulations were performed to study the formation and evolution of deformation-induced crystallographic defects at the early stages of indentation. We observed that, in addition to 〈a〉 dislocations, the I1 stacking fault bounded with a 〈1/2c+p〉 Frank loop can be generated from the plastic zone ahead of the indenter, and potentially serve as a nucleation source for abundant 〈c + a〉 dislocations observed experimentally. These new findings are anticipated to provide new knowledge on the deformation mechanisms of Mg, which are difficult to obtain through conventional ex situ approaches. These observations may serve as a baseline for simulation work that investigate the dynamics of 〈c + a〉 dislocation slip and twinning in Mg and alloys.
more »
« less
This content will become publicly available on October 1, 2026
Hardness anisotropy in Mg: The influence of extension twining and 〈c + a〉 dislocation activity under nanoindentations
Nanoindentation was performed on individual grains of a polycrystalline Mg sample with c-axis declination angles ranging from parallel (0°) to perpendicular (90°) to the c-axis. Hardness was highest at ∼0°, decreased up to ∼55°, and then increased at ∼90° to an intermediate level. At ∼0°, high-density 〈c + a〉 dislocations extended deep into the crystal, contributing to high hardness. At ∼55°, 〈c + a〉 dislocations were confined near the indent, and occasional extension twinning reoriented the crystal to ∼45°, promoting 〈a〉 slip in both matrix and twin, leading to low hardness. At ∼90°, extension twinning reoriented the crystal to ∼0°, inducing texture hardening and intermediate hardness. Despite the complex stress state in nanoindentation, which fundamentally differs from the uniaxial stress in bulk tensile and compression tests, the combined contributions of dislocation and twinning still give rise to measurable hardness anisotropy, suggesting nanoindentation as a high-throughput technique for probing orientation-dependent mechanical behavior in Mg.
more »
« less
- Award ID(s):
- 2144973
- PAR ID:
- 10608400
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Scripta Materialia
- Volume:
- 267
- Issue:
- C
- ISSN:
- 1359-6462
- Page Range / eLocation ID:
- 116832
- Subject(s) / Keyword(s):
- Mg Nanoindentation Dislocations Twinning Hardness anisotropy
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Schuh, Christopher A (Ed.)The {-1012} tensile twins terminating inside the grains of a deformed Mg-Y alloy were investigated by transmission electron microscopy. The crystallographic features of terminating twins and associated slip structures were quantified and correlated. The local stresses developed at a terminating {-1012} twin were computed using crystal plasticity simulations in order to interpret the observed slip patterns. Results indicate that both basal and matrix glide were involved in accommodating the plastic stresses developed in the vicinity of terminating twins. Along the twin boundary, the defect contrast consistent with that of lattice dislocations and twinning partials was observed. Based on these observations, a dislocation reaction is proposed that establishes an interrelationship between the observed matrix glide and {-1012} twinning in Mg-Y alloys.more » « less
-
null (Ed.)An in situ optical microscopy combined with ex situ electron backscatter diffraction testing was applied to a pristine single-crystal magnesium specimen under monotonic tension along the c-axis. An intrusion-like co-zone twin-twin structure is observed for the first time at the micron scale. In situ observation reveals that the intrusion-like twin-twin structure consists of multiple twin-twin boundaries (TTBs) and incoherent twin boundaries (I-CTBs) following energetically favorable formation sequences. The initial interaction results in the impinging TTBI and the acute-angle TTBA. In the local junction region on the obtuse angle side, the impinging twinning dislocations (TDs) further deposit near TTBI due to the preferred local twinning shear stress, leading to the incoherent curve of the impinging twin boundary adjacent to TTBI. Shortly after, the barrier twin boundary on the obtuse angle side migrates and encompasses the incoherent impinging twin boundary. The combination of sequential TTBI, TTBA, and I-CTBs formed locally on the obtuse angle side shapes the final configuration of the intrusion-like twin-twin structure at the micron scale.more » « less
-
Recent molecular dynamics simulations revealed that 〈 c + a 〉 dislocations in Mg were prone to dissociation on the basal plane, thus becoming sessile. Basal dissociation of 〈 c + a 〉 dislocations is significant because it is a major factor in the limited ductility and high work-hardening in Mg. We report an in situ transmission electron microscopy study of the deformation process using an H-bar-shaped thin foil of Mg single crystal designed to facilitate 〈 c + a 〉 slip, observe 〈 c + a 〉 dislocation activity, and establish the validity of the largely immobile 〈 c + a 〉 dislocations caused by the predicted basal dissociation. In addition, through detailed observations on the fine movement of some 〈 c + a 〉 dislocations, it was revealed that limited bowing out movement for some non-basal portions of 〈 c + a 〉 dislocations was possible; under certain circumstances, i.e., through attraction and reaction between two 〈 c + a 〉 dislocations on the same pyramidal plane, at least portions of the sessile configuration were observed to be reversed into a glissile one.more » « less
-
Amorphous/crystalline high-entropy-alloy (HEA) composites show great promise as structural materials due to their exceptional mechanical properties. However, there is still a lack of understanding of the dynamic nanoindentation response of HEA composites at the atomic scale. Here, the mechanical behavior of amorphous/crystalline HEA composites under nanoindentation is investigated through a large-scale molecular dynamics simulation and a dislocation-based strength model, in terms of the indentation force, microstructural evolution, stress distribution, shear strain distribution, and surface topography. The results show that the uneven distribution of elements within the crystal leads to a strong heterogeneity of the surface tension during elastic deformation. The severe mismatch of the amorphous/crystalline interface combined with the rapid accumulation of elastic deformation energy causes a significant number of dislocation-based plastic deformation behaviors. The presence of surrounding dislocations inhibits the free slip of dislocations below the indenter, while the amorphous layer prevents the movement or disappearance of dislocations towards the substrate. A thin amorphous layer leads to great indentation force, and causes inconsistent stacking and movement patterns of surface atoms, resulting in local bulges and depressions at the macroscopic level. The increasing thickness of the amorphous layer hinders the extension of shear bands towards the lower part of the substrate. These findings shed light on the mechanical properties of amorphous/crystalline HEA composites and offer insights for the design of high-performance materials.more » « less