Abstract Determining suitable dopants with optimized doping concentration is critical to design efficient water splitting photocatalysts. However, there is currently a lack of fundamental knowledge to guide this process. Herein, we examine the impact of Al3+, Mg2+, and Ga3+on the photocatalytic performance of SrTiO3and propose a defect compensation model to understand the doping effect. Doped SrTiO3crystals were grown hydrothermally and treated in molten SrCl2. The hydrogen production rates from 50 catalysts produced in this way were measured with a high‐throughput parallelized and automated photochemical reactor (PAPCR). The investigation revealed that all three dopants significantly enhance the photocatalytic reactivity. According to Brouwer diagrams computed using available reaction constants, the optimum reactivity is achieved when the concentration of acceptor dopants fully compensates the oxygen vacancy donors. The improved reactivity can be attributed to the reduction in free electron concentration, resulting in a space charge layer that is 1000 times longer. Consequently, this situation enhances the number of photogenerated charge carriers capable of being separated by the band bending and transported to the surface.
more »
« less
This content will become publicly available on August 1, 2026
Influence of Al‐doped SrTiO 3 cores on hydrogen evolution from SrTiO 3 /TiO 2 core‒shell catalysts
Abstract The hydrogen produced by Al‐doped SrTiO3/TiO2core‒shell catalysts with a range of Al‐doped SrTiO3cores and the same TiO2shell are compared. The study included SrTiO3cores doped with different amounts of Al (0, 1, 2, or 3 mol%) added at different points in the synthesis (prior to or during the molten salt treatment) and at different temperatures (900°C, 1000°C, and 1100°C). It was found that core‒shell catalysts with different cores had hydrogen generation rates that varied by a factor of more than 40 and varied with the processing parameters in the same way as the hydrogen generation rates of the cores alone. The best catalysts had 2 or 3 mol% added Al, added during treatment in a SrCl2molten salt at 1000°C or 1100°C. Because the core absorbs most of the light, its ability to separate and transport photogenerated charge carriers dominates the properties of the core‒shell catalyst. This indicates that, to optimize the properties of core‒shell catalysts, it is essential to optimize the properties of the core. While the shell can be important to protect the core from degradation, it is not as important to the overall reactivity as the core.
more »
« less
- Award ID(s):
- 2016267
- PAR ID:
- 10612025
- Publisher / Repository:
- Wiley
- Date Published:
- Journal Name:
- Journal of the American Ceramic Society
- Volume:
- 108
- Issue:
- 8
- ISSN:
- 0002-7820
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Chromium-doped SrTiO 3 nanocrystals of perovskite structure type and 45 nm (±15 nm) edge lengths were obtained by hydrothermal synthesis in water from titanium oxide, strontium hydroxide, and chromium( iii ) nitrate. According to XPS, the majority of the surface chromium (68.3%) is present in the 3+ state and the remainder (32.2%) in the 6+ state. Optical spectroscopy confirms a broad absorption at 2.3–2.9 eV from Cr(3+) dopant states, in addition to the 3.2 eV band edge of the SrTiO 3 host. After modification with Pt nanoparticles, Cr-doped SrTiO 3 nanocrystals catalyze photochemical H 2 evolution from aqueous methanol under visible light illumination (>400 nm) and with an apparent quantum yield of 0.66% at 435 nm. According to surface photovoltage spectroscopy (SPS), Cr-doped SrTiO 3 nanocrystals deposited onto gold substrates are n-type and have an effective band gap of 1.75 eV. SPS and transient illumination experiments at 2.50 eV reveal an anomalous surface photovoltage that increases with prior light exposure to values of up to −6.3 V. This photovoltage is assigned to ferroelectric polarization of the material in the space charge layer at the Au/SrTiO 3 :Cr interface. The polarization is stable for 24 h in vacuum but disappears after 12 h when samples are stored in air. The electric polarizability of SrTiO 3 :Cr is confirmed when films are exposed to static electric fields (1.20 MV m −1 ) in a fixed capacitor configuration. The discovery of a ferroelectric effect in Cr-doped SrTiO 3 could be significant for the development of improved photocatalysts for the conversion of solar energy into fuel.more » « less
-
Abstract Converting CO2to value‐added chemicals,e. g., CH3OH, is highly desirable in terms of the carbon cycling while reducing CO2emission from fossil fuel combustion. Cu‐based nanocatalysts are among the most efficient for selective CO2‐to‐CH3OH transformation; this conversion, however, suffers from low reactivity especially in the thermodynamically favored low temperature range. We herein report ultrasmall copper (Cu) nanocatalysts supported on crystalline, mesoporous zinc oxide nanoplate (Cu@mZnO) with notable activity and selectivity of CO2‐to‐CH3OH in the low temperature range of 200–250 °C. Cu@mZnO nanoplates are prepared based on the crystal‐crystal transition of mixed Cu and Zn basic carbonates to mesoporous metal oxides and subsequent hydrogen reduction. Under the nanoconfinement of mesopores in crystalline ZnO frameworks, ultrasmall Cu nanoparticles with an average diameter of 2.5 nm are produced. Cu@mZnO catalysts have a peak CH3OH formation rate of 1.13 mol h−1per 1 kg under ambient pressure at 246 °C, about 25 °C lower as compared to that of the benchmark catalyst of Cu−Zn−Al oxides. Our new synthetic strategy sheds some valuable insights into the design of porous catalysts for the important conversion of CO2‐to‐CH3OH.more » « less
-
Abstract This study presented the use of SrTiO3/Y2O3nanoparticles for the reinforcement of dental poly(methyl methacrylate) (PMMA) to enhance its mechanical properties important for everyday use of denture base materials. The average crystallite size of prepared nanoparticles was 19.9 nm. The influence of 0.5, 1.0, and 1.5 wt% SrTiO3/Y2O3loading on absorbed impact energy, microhardness and tensile properties was investigated. Scanning electron microscopy of the composite fracture surface revealed multiple toughening mechanisms, with agglomerates directly included in the crack pinning, indicating improvement in mechanical performance. Dynamic mechanical analysis proved that agglomerates improved the elastic behavior of PMMA and confirmed the absence of a residual monomer. After the incorporation of SrTiO3/Y2O3, the mechanical properties of composites showed a high increase compared to neat PMMA. The optimal concentration of nanoparticles was 1 wt%, for which the microhardness, modulus of elasticity, and absorbed impact energy were higher by 218.4%, 65.8% and 135.6%, respectively. With such a high increase, this research showed that SrTiO3/Y2O3represents an efficient filler which use does not have to be limited to dental materials. HighlightsSrTiO3/Y2O3hybrid nanoparticles were prepared.PMMA‐SrTiO3/Y2O3composite showed increase in impact resistance up to 135.4%.Elastic behavior of PMMA was improved.With 1 wt% of SrTiO3/Y2O3, microhardness increased by 218.4%.more » « less
-
Abstract This work investigates the effects of doping on both the thermodynamics and kinetics of sintering in aluminum‐doped yttrium oxide nanoparticles (Al‐doped Y2O3), with the objective of delineating their interdependent effects at different stages of the process. Direct measurements of surface and grain boundary energies using differential scanning calorimetry showed that Al‐doping decreases both interfacial energies, leading to an increase in dihedral angle (from 152.7 ± 5.6° to 165.8 ± 5.5°) and, therefore, sintering stress. Densification and grain growth analyses showed that despite this increase in sintering stress, the onset of sintering is delayed for the Al‐doped samples, demonstrating that a large dihedral angle is a necessary but not sufficient condition for densification. The measurements of activation energies for densification and grain growth point out that Al suppresses grain boundary mobility by increasing the activation energy from 400 to 448 kJ/mol, hindering densification at the intermediate stages of sintering. At temperatures above 1150℃, grain growth is activated in the Al‐doped samples, which rapidly releases the accumulated sintering stress and exhibits a higher densification rate than in undoped Y2O3. This study demonstrates a complex interconnectivity between the thermodynamics and kinetics at different temperature ranges of sintering and reinforces the need for a comprehensive description for proper design of sintering aids.more » « less