Materials with high thermal conductivity (κ) are of technological importance and fundamental interest. We grew cubic boron nitride (cBN) crystals with controlled abundance of boron isotopes and measured κ greater than 1600 watts per meter-kelvin at room temperature in samples with enriched 10 B or 11 B. In comparison, we found that the isotope enhancement of κ is considerably lower for boron phosphide and boron arsenide as the identical isotopic mass disorder becomes increasingly invisible to phonons. The ultrahigh κ in conjunction with its wide bandgap (6.2 electron volts) makes cBN a promising material for microelectronics thermal management, high-power electronics, and optoelectronics applications.
more »
« less
This content will become publicly available on October 13, 2026
Extended wavelength photodiodes in the B-III–V material system
Highly mismatched B-III–V alloys present a promising avenue for near-infrared (NIR), direct bandgap optoelectronics that can be integrated on GaAs or Si, owing to their ability to vary bandgap and lattice constant independently. Here, we report the epitaxial growth, fabrication, and characterization of nearly strain-free, all-BGaInAs, p-i-n photodiodes on GaAs substrates grown by molecular beam epitaxy. Incorporating boron effectively reduced the strain in InGaAs, yielding nearly lattice-matched BGaInAs layers with high surface quality, as confirmed by high-resolution x-ray diffraction and atomic force microscopy measurements. Strong photoluminescence (PL) intensity was observed for BGaInAs with up to 3.2% B (7% In). The operating wavelength consistently extended with increasing boron and indium incorporation as evidenced by PL and external quantum efficiency measurements, which agree with density functional theory predictions. Altogether, these results highlight precise control of the operating wavelength and suggest highly substitutional boron incorporation. BGaInAs photodiodes with low boron and indium concentrations demonstrated high sensitivity with low dark current. We also report the effective thermal conductivity of the BGaInAs p-i-n structures and find that the thermal conductivity is largely insensitive to boron content with dominant effects from the indium content. Altogether, these findings underscore the potential for strain-free BGaInAs photodiodes as promising candidates for high-performance NIR optoelectronics.
more »
« less
- Award ID(s):
- 2122041
- PAR ID:
- 10693262
- Publisher / Repository:
- AIP Publishing
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 127
- Issue:
- 15
- ISSN:
- 0003-6951
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Highly mismatched semiconductor alloys (HMAs) offer unusual combinations of bandgap and lattice constant, which are attractive for myriad applications. Dilute borides, such as BGa(In)As, are typically assumed to be HMAs. BGa(In)As can be grown in higher alloy compositions than Ga(In)NAs with comparable bandgaps, potentially enabling routes to lattice-matched telecom lasers on Si or GaAs. However, BGa(In)As remains relatively unexplored, especially with large fractions of indium. Density functional theory with HSE06 hybrid functionals was employed to study BGaInAs with 4%–44% In and 0%–11% B, including atomic rearrangement effects. All compositions showed a direct bandgap, and the character of the lowest conduction band was nearly unperturbed with the addition of B. Surprisingly, although the bandgap remained almost constant and the lattice constant followed Vegard's law with the addition of boron, the electron effective mass increased. The increase in electron effective mass was higher than in conventional alloys, though smaller than those characteristics of HMAs. This illustrates a particularly striking finding, specifically that the compositional space of BGa(In)As appears to span conventional alloy and HMA behavior, so it is not well-described by either limit. For example, adding B to GaAs introduces additional states within the conduction band, but further addition of In removes them, regardless of the atomic arrangement.more » « less
-
We investigated the pressure-dependent exciton absorption and photoluminescence (PL) properties of colloidal InAs/ZnSe core/shell quantum dots (QDs) emitting near-infrared (NIR) photons, an environmentally friendly alternative to heavy-metal-containing NIR QDs. A detailed analysis of exciton absorption and emission spectra was conducted in the pressure range of 0–10 GPa, focusing on the energy shifts, PL intensity, and lineshape changes with pressure. The pressure coefficients for exciton absorption and PL peaks were ∼70% of the bulk InAs value, with enhanced bandgap nonlinearity tentatively attributed to the higher bulk modulus of QDs compared to bulk material. The pressure-induced shifts in exciton absorption and PL peaks were reversible upon compression and decompression, with no indication of the semiconductor-to-metallic phase transition observed in bulk InAs around 7 GPa. However, PL intensity exhibited partial irreversibility, suggesting defect formation at the core/shell interface under pressure. From the findings of this study, along with previous high-pressure studies on molecular beam epitaxy-grown InAs QDs on GaAs, we infer the importance of the shell in determining the pressure response of exciton absorption and PL in core/shell QD structures with non-negligible interfacial strain and wave function spill into the shell.more » « less
-
Abstract Space missions critically rely on sensors that operate throughout the near‐ to longwave infrared (NIR – LWIR, λ = 0.9–14 µm) regions of the electromagnetic spectrum. These sensors capture data beyond the capabilities of traditional optical tools and sensors, critical for the detection of thermal emissions, conducting atmospheric studies, and surveillance. However, conventional NIR‐LWIR detectors depend on bulky, cryogenically cooled semiconductors, making them impractical for broader space‐based applications due to their high cost, size, weight, and power (C‐SWaP) demands. Here, an IR photodetector using a solution‐processed narrow bandgap conjugated polymer is demonstrated. This direct bandgap photoconductor demonstrates exceptional infrared sensitivity without cooling and has minimal changes in figures‐of‐merit after substantial ionizing radiation exposure up to 1,000 krad – equivalent to three years in the most intense low Earth orbit (LEO). Its performance and resilience to radiation notably surpass conventional inorganic detectors, with a 7.7 and 98‐fold increase in radiation hardness when compared to epitaxial mercury cadmium telluride (HgCdTe) and indium gallium arsenide (InGaAs) photodiodes, respectively, offering a more affordable, compact, and energy‐efficient alternative. This class of organic semiconductors provides a new frontier for C‐SWaP optimized IR space sensing technologies, enabling the development of new spacecraft and missions with enhanced observational capabilities.more » « less
-
The increasing complexity of semiconductor devices fabricated from wide-bandgap and ultra-wide-bandgap materials demand advanced thermal management solutions to mitigate heat buildup, a major cause of device failure. High thermal conductivity materials are thus becoming crucial for thermal management. Cubic boron arsenide (c-BAs) has emerged as a promising candidate. However, challenges remain in synthesizing high-quality crystals with low defect concentrations, high homogeneous thermal conductivity, and high yields using the conventional chemical vapor transport method. In this study, we report the synthesis of high-yield c-BAs single crystals using the Bridgman method. The crystals exhibit high uniformity, reduced defect densities, and lower carrier concentrations as confirmed through x-ray diffraction, Raman spectroscopy, temperature-dependent photoluminescence, and electrical transport measurements. Our work represents a significant step toward scalable production of high-quality c-BAs for industrial applications, offering a practical solution for improving thermal management in next-generation electronic devices.more » « less