%AAmin Shikder, Md [Department of Mechanical and Industrial Engineering, University of Illinois at Chicago, Chicago, USA]%AAmin Shikder, Md [Department of Mechanical and Industrial Engineering; University of Illinois at Chicago; Chicago; USA]%AMaksud, Mahjabin [Department of Mechanical and Industrial Engineering, University of Illinois at Chicago, Chicago, USA]%AMaksud, Mahjabin [Department of Mechanical and Industrial Engineering; University of Illinois at Chicago; Chicago; USA]%AVasudevamurthy, Gokul [General Atomics Corporation, San Diego, USA]%AVasudevamurthy, Gokul [General Atomics Corporation; San Diego; USA]%AByles, Bryan [Department of Materials Science and Engineering, Drexel University, Philadelphia, USA]%AByles, Bryan W. [Department of Materials Science and Engineering; Drexel University; Philadelphia; USA]%ACullen, David [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, USA]%ACullen, David [Materials Science and Technology Division; Oak Ridge National Laboratory; Oak Ridge; USA]%AMore, Karren [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, USA]%AMore, Karren [Center for Nanophase Materials Sciences; Oak Ridge National Laboratory; Oak Ridge; USA]%APomerantseva, Ekaterina [Department of Materials Science and Engineering; Drexel University; Philadelphia; USA]%APomerantseva, Ekaterina [Department of Materials Science and Engineering, Drexel University, Philadelphia, USA]%ASubramanian, Arunkumar [Department of Mechanical and Industrial Engineering, University of Illinois at Chicago, Chicago, USA]%ASubramanian, Arunkumar [Department of Mechanical and Industrial Engineering; University of Illinois at Chicago; Chicago; USA]%BJournal Name: Nanoscale Advances; Journal Volume: 1; Journal Issue: 1; Related Information: CHORUS Timestamp: 2019-01-15 05:41:43 %D2019%IRoyal Society of Chemistry (RSC) %JJournal Name: Nanoscale Advances; Journal Volume: 1; Journal Issue: 1; Related Information: CHORUS Timestamp: 2019-01-15 05:41:43 %K %MOSTI ID: 10075634 %PMedium: X %TBrittle fracture to recoverable plasticity: polytypism-dependent nanomechanics in todorokite-like nanobelts %X

This paper shows polytypism dependent nanomechanics in todorokite-like nanobelts and reveals a plastic recovery regime in nanobelts with larger-width tunnel grains.

%0Journal Article