%AKopaczek, Jan%ALi, Han%AYumigeta, Kentaro%ASailus, Renee%ASayyad, Mohammed%AMoosavy, Seyed%AKudrawiec, Robert%ATongay, Sefaattin%BJournal Name: Journal of Materials Chemistry C; Journal Volume: 10; Journal Issue: 33 %D2022%I %JJournal Name: Journal of Materials Chemistry C; Journal Volume: 10; Journal Issue: 33 %K %MOSTI ID: 10376457 %PMedium: X %TPressure-induced suppression of charge density phases across the entire rare-earth tritellurides by optical spectroscopy %XThe rare-earth tritellurides (RTe 3 ) are a distinct class of 2D layered materials that recently gained significant attention due to hosting such quantum collective phenomena as superconductivity or charge density waves (CDWs). Many members of this van der Waals (vdW) family crystals exhibit CDW behavior at room temperature, i.e. , RTe 3 compound where R = La, Ce, Pr, Nd, Sm, Gd, and Tb. Here, our systematic studies establish the CDW properties of RTe 3 when the vdW spacing/interaction strength between adjacent RTe 3 layers is engineered under extreme hydrostatic pressures. Using a non-destructive spectroscopy technique, pressure-dependent Raman studies first establish the pressure coefficients of phonon and CDW amplitude modes for a variety of RTe 3 materials, including LaTe 3 , CeTe 3 , PrTe 3 , NdTe 3 , SmTe 3 , GdTe 3 , and TbTe 3 . Results further show that the CDW phase is eventually suppressed at high pressures when the interlayer spacing is reduced and interaction strength is increased. Comparison between different RTe 3 materials shows that LaTe 3 with the largest thermodynamic equilibrium interlayer spacing (smallest chemical pressure) exhibits the most stable CDW phases at high pressures. In contrast, CDW phases in late RTe 3 systems with the largest internal chemical pressures are suppressed easily with applied pressure. Overall results provide comprehensive insights into the CDW response of the entire RTe 3 series under extreme pressures, offering an understanding of CDW formation/engineering in a unique class of vdW RTe 3 material systems. %0Journal Article