Zinc (Zn) alloys, particularly those incorporating magnesium (Mg), have been explored as potential bioabsorbable metals. However, there is a continued need to enhance the corrosion characteristics of Zn-Mg alloys to fulfill the requirements for biodegradable implants. This work involves a corrosion behavior comparison between severe-plastic-deformation (SPD) processed cast Zn-Mg alloys and their hybrid counterparts, having equivalent nominal compositions. The SPD processing technique used was high-pressure torsion (HPT), and the corrosion behavior was studied as a function of the number of turns (1, 5, 15) for the Zn-3Mg (wt.%) alloy and hybrid and as a function of composition (Mg contents of 3, 10, 30 wt.%) for the hybrid after 15 turns. The results indicated that HPT led to multimodal grain size distributions of ultrafine Mg-rich grains containing MgZn2 and Mg2Zn11 nanoscale intermetallics in a matrix of coarser dislocation-free Zn-rich grains. A greater number of turns resulted in greater corrosion resistance because of the formation of the intermetallic phases. The HPT hybrid was more corrosion resistant than its alloy counterpart because it tended to form the intermetallics more readily than the alloy due to the inhomogeneous conditions of the materials before the HPT processing as well as the non-equilibrium conditions imposed during the HPT processing. The HPT hybrids with greater Mg contents were less corrosion resistant because the addition of Mg led to less noble behavior. 

β-titanium (β-Ti) alloys are useful in diverse industries because their mechanical properties can be tuned by transforming the metastable β phase into other metastable and stable phases. Relationships between lattice parameter and β-Ti alloy concentrations have been explored, but the lattice parameter evolution during β-phase transformations is not well understood. In this work, the β-Ti alloys, Ti-11Cr, Ti-11Cr-0.85Fe, Ti-11Cr-5.3Al, and Ti-11Cr-0.85Fe-5.3Al (all in at.%), underwent a 400 °C aging treatment for up to 12 h to induce the β-to-ω and β-to-α phase transformations. Phase identification and lattice parameters were measured in situ using high-temperature X-ray diffraction. Phase compositions were measured ex situ using atom probe tomography. During the phase transformations, Cr and Fe diffused from the ω and α phases into the β matrix, and the β-phase lattice parameter exhibited a corresponding decrease. The decrease in β-phase lattice parameter affected the α- and ω-phase lattice parameters. The α phase in the Fe-free alloys exhibited α-phase c/a ratios close to those of pure Ti. A larger β-phase composition change in Ti-11Cr resulted in larger ω-phase lattice parameter changes than in Ti-11Cr-0.85Fe. This work illuminates the complex relationship between diffusion, composition, and structure for these diffusive/displacive transformations.