Search for: All records

Abstract Mg₄(TiZnSn)₃, a rare-earth-free Mg-based multi-principal element alloy, was synthesized via high-energy ball milling and cold compaction. Potentiodynamic polarization in 0.1 M NaCl revealed spontaneous passivation with a corrosion current density of 8.96 ± 0.83 µA/cm²and a nobler than Mg corrosion potential of -1058.35 ± 15.91 mV_SCE. X-ray photoelectron spectroscopy confirmed the formation of a mixed oxide film containing ZnO, SnO₂, and TiO₂, contributing to the observed passivity. The alloy also exhibited improved mechanical performance, with a hardness of 5.06 ± 0.41 GPa and Young’s modulus of 109.24 ± 10 GPa. These results demonstrate that tailored multi-element alloying and powder metallurgy can synergistically enhance both corrosion resistance and mechanical properties in Mg alloys. 

Magnesium-containing multi-principal element alloys (MPEAs) are promising for lightweight applications due to their low density, high specific strength, and biocompatibility. This study examines two Mg-Ti-Zn alloy compositions, equal molar MgTiZn (TZ) and Mg4TiZn (4TZ), synthesized via ball milling followed by spark plasma sintering, focusing on their microstructures and corrosion behaviors. X-ray diffraction and transmission electron microscopy revealed the formation of intermetallic phases, including Ti2Zn and Mg21Zn25 in TZ, while 4TZ exhibited a predominantly Mg-rich phase. Potentiodynamic polarization and immersion tests in 0.1 M NaCl solution showed that both alloys had good corrosion resistance, with values of 3.65 ± 0.65 µA/cm2 for TZ and 4.58 ± 1.64 µA/cm2 for 4TZ. This was attributed to the formation of a TiO2-rich surface film in the TZ, as confirmed by X-ray photoelectron spectroscopy (XPS), which contributed to enhanced passivation and lower corrosion current density. Both alloys displayed high hardness, 5.5 ± 1.0 GPa for TZ and 5.1 ± 0.9 GPa for 4TZ, and high stiffness, with Young’s modulus values of 98.2 ± 11.2 GPa for TZ and 100.8 ± 9.6 GPa for 4TZ. These findings highlight the potential of incorporating Ti and Zn via mechanical alloying to improve the corrosion resistance of Mg-containing MPEAs and Mg-based alloys. 

Abstract The effect of V addition on the hardness and corrosion of aluminum alloy 2024 (AA2024) produced by high‐energy ball milling has been investigated. High‐energy ball milled alloys exhibited enhanced solid solubility of alloying elements and ultrafine grains. The addition of V improved the corrosion resistance of the AA2024 alloy, which was attributed to the deposition of V on the cathodic particles and therefore decrease in their ability to sustain large cathodic currents. 

In this study, a compact cold sprayed (CS) Ti coating was deposited on Mg alloy using a high pressure cold spray (HPCS) system. The wear and corrosion behavior of the CS Ti coating was compared with that of CS Al coating and bare Mg alloy. The Ti coating yielded lower wear rate compared to Al coating and Mg alloy. Electrochemical impedance spectroscopy (EIS) and cyclic potentiodynamic polarization (CPP) tests revealed that CS Ti coating can substantially reduce corrosion rate of AZ31B in chloride containing solutions compared to CS Al coating. Interestingly, Ti-coated Mg alloy demonstrated negative hysteresis loop, depicting repassivation of pits, in contrast to AZ31B and Al-coated AZ31B with positive hysteresis loops where corrosion potential (Ecorr) > repassivation potential (Erp); indicating irreversible growth of pits. AZ31B and Al-coated AZ31B were most susceptible to pitting corrosion, while Ti-coated Mg alloy indicated noticeable resistance to pitting in 3.5 wt % NaCl solution. In comparison to Al coating, Ti coating considerably separated the AZ31BMg alloy surface from the corrosive electrolyte during long term immersion test for 11 days. 

SUMMARY Medicago truncatulais a model legume for fundamental research on legume biology and symbiotic nitrogen fixation.Tnt1, a retrotransposon from tobacco, was used to generate insertion mutants inM. truncatulaR108. Approximately 21 000 insertion lines have been generated and publicly available.Tnt1retro‐transposition event occurs during somatic embryogenesis (SE), a pivotal process that triggers massive methylation changes. We studied the SE ofM. truncatulaR108 using leaf explants and explored the dynamic shifts in the methylation landscape from leaf explants to callus formation and finally embryogenesis. Higher cytosine methylation in all three contexts of CG, CHG, and CHH patterns was observed during SE compared to the controls. Higher methylation patterns were observed in assumed promoter regions (~2‐kb upstream regions of transcription start site) of the genes, while lowest was recorded in the untranslated regions. Differentially methylated promoter region analysis showed a higher CHH methylation in embryogenesis tissue samples when compared to CG and CHG methylation. Strong correlation (89.71%) was identified between the differentially methylated regions (DMRs) and the site ofTnt1insertions inM. truncatulaR108 and stronger hypermethylation of genes correlated with higher number ofTnt1insertions in all contexts of CG, CHG, and CHH methylation. Gene ontology enrichment and KEGG pathway enrichment analysis identified genes and pathways enriched in the signal peptide processing, ATP hydrolysis, RNA polymerase activity, transport, secondary metabolites, and nitrogen metabolism pathways. Combined gene expression analysis and methylation profiling showed an inverse relationship between methylation in the DMRs (regions spanning genes) and the expression of genes. Our results show that a dynamic shift in methylation happens during the SE process in the context of CG, CHH and CHG methylation, and theTnt1retrotransposition correlates with the hyperactive methylation regions.