Search for: All records

Abstract C-axis aligned BaZrO₃(BZO) nanorods formed via strain-mediated self-assembly in BZO-doped YaBa₂Cu₃O_7-x(BZO/YBCO) nanocomposite films can provide strong pinning to the quantized magnetic vortices. While the strain initiated from the BZO/YBCO lattice mismatch plays a critical role in nucleation and evolution of the BZO nanorods, it also leads to a highly defective BZO/YBCO interface and hence reduced pinning efficiency of BZO nanorods. This work reports a recent study in probing the effect of BZO/YBCO interface on the pinning efficiency of the BZO nanorods as the interface is repaired dynamically during the BZO nanorod growth using Ca doping. Within the BZO doping range of 2-8 vol.%, significantly enhanced pinning efficiency of the BZO nanorods have been observed. A peak enhancement up to five-fold of critical current density at 9.0 T and 65-77 K has been obtained in the 6 vol.% BZO/YBCO nanocomposites after the interface repair. This result not only illustrates the critical importance of the BZO/YBCO interface in the pinning efficiency, but also provides a facile scheme to achieve such an interface to restore the pristine pinning efficiency of the BZO nanorods. 

High critical current (Ic) in high magnetic fields (B) with minimal variations with respect to the orientation of the B field is demanded by many applications such as high-field magnets for fusion systems. Motivated by this, this work studies 6 vol. % BaZrO3/YBa2Cu3O7 (BZO/YBCO) multilayer nanocomposite films by stacking two 10 nm thick Ca0.3Y0.7Ba2Cu3O7 (CaY-123) spacers with three BZO/YBCO layers of thickness varied from 50 to 330 nm to make the total film thickness of 150–1000 nm. The Ca diffusion from the spacers into BZO/YBCO was shown to dramatically enhance pinning efficiency of c-axis aligned BZO nanorods, which yields high and almost thickness independent critical current density (Jc) in the BZO/YBCO multilayer nanocomposite films. Remarkably, enhanced Jc was observed in these multilayer samples at a wide temperature range of 20–80 K and magnetic fields up to 9.0 T. In particular, the thicker BZO/YBCO multilayer films outperform their thinner counterparts in both higher value and less anisotropy of Jc at lower temperatures and higher fields. At 20 K and 9.0 T, Ic is up to 654 A/cm-width at B//c in the 6% multilayer (1000 nm) sample, which is close to 753 A/cm-width at B//ab due to the intrinsic pinning. This result illustrates the critical role of the Ca cation diffusion into the YBCO lattice in achieving high and isotropic pinning in thick BZO/YBCO multilayer films. 

One-dimensional artificial pinning centers (1D-APCs) in YBa2Cu3O7-x nanocomposite films provide strong collective pinning at magnetic field B//c-axis. In this work, we reveal a 1D-APC/YBa2Cu3O7-x interface is preferred for high pinning efficiency of individual 1D-APCs including BaHfO3 and BaZrO3. The coherent 1D-APC/YBa2Cu3O7-x interface may be obtained via either growth of the nanocomposite films at optimal condition or Ca-diffusion to dynamically reduce the interface strain during the nanocomposite film growth. Interestingly, the high pinning efficiency of the 1D-APCs with coherent interfaces with YBCO not only lead to a high critical current density (Jc) in magnetic fields up to 9.0 T at H//c-axis but also enhanced Jc over a larger angular range when H is away from H//c-axis up to θ=60-80 degree than that in the case the interface is defective. This result suggests the importance of understanding and engineering the APC/YBCO interface for optimal pinning in nanocomposite films. 

Abstract This work examines the pinning enhancement in BaZrO 3 (BZO) +Y 2 O 3 doubly-doped (DD) YBa 2 Cu 3 O 7 (YBCO) nanocomposite multilayer (DD-ML) films. The film consists of two 10 nm thin Ca 0.3 Y 0.7 Ba 2 Cu 3 O 7-x (CaY-123) spacers stacking alternatively with three BZO + Y 2 O 3 /YBCO layers of 50 nm each in thickness that contain 3 vol% of Y 2 O 3 and BZO doping in the range of 2–6 vol%. Enhanced magnetic vortex pinning and improved pinning isotropy with respect to the orientation of magnetic field (B) have been achieved in the DD-ML samples at lower BZO doping as compared to that in the single-layer counterparts (DD-SL) without the CaY-123 spacers. For example, the pinning force density ( F p ) of ∼58 GNm −3 in 2 vol.% of DD-ML film is ∼110% higher than in 2 vol% of DD-SL at 65 K and B // c -axis, which is attributed to the improved pinning efficiency by c -axis aligned BZO nanorods through diffusion of Calcium (Ca) along the tensile-strained channels at BZO nanorods/YBCO interface for improvement of the interface microstructure and hence pinning efficiency of BZO nanorods. An additional benefit is in the considerably improved J c ( θ ) and reduced J c anisotropy in the former over the entire range of the B orientations. However, at higher BZO doping, the BZO nanorods become segmented and misoriented, which may change the Ca diffusion pathways and reduce the benefit of Ca in improving the pinning efficiency of BZO nanorods. 

Abstract Microstructural analysis of the BaZrO 3 (BZO)/YBa 2 Cu 3 O 7 (YBCO) interface has revealed a highly defective and oxygen deficient 2-3 nm thick YBCO column surrounding the BZO one-dimensional artificial pinning centers (1D-APCs). The resulting semi-coherent interface is the consequence of the ∼7.7% BZO/YBCO lattice mismatch and is responsible for the low pinning efficiency of BZO 1D-APCs. Herein, we report an interface engineering approach of dynamic Ca/Cu replacement on YBCO lattice to reduce/eliminate the BZO/YBCO lattice mismatch for improved pinning at a wide angular range of the magnetic field orientation. The Ca/Cu replacement induces a local elongation of the YBCO c-lattice near the BZO/YBCO interface, thereby ensuring a reduction in the BZO/YBCO lattice mismatch to ∼1.4% and a coherent BZO/YBCO interface. This has resulted in enhanced pinning at B//c-axis and a broad angular range of B-field orientation. For example, the 6 vol.% BZO/YBCO film with interface engineering exhibits F p ∼158 GN/m 3 at 65 K and B//c-axis, which is 440% higher than the ∼36.1 GN/m 3 for the reference 6% BZO/YBCO sample, and enhanced J c and F p in a wide angular range up to ∼ 80°. This result illustrates a facile scheme for engineering 1D-APC/YBCO interface to resume the pristine pinning efficiency of the 1D-APCs. 

Abstract One-dimensional c -axis-aligned BaZrO 3 (BZO) nanorods are regarded as strong one-dimensional artificial pinning centers (1D-APCs) in BZO-doped YaBa 2 Cu 3 O 7− x (BZO/YBCO) nanocomposite films. However, a microstructure analysis has revealed a defective, oxygen-deficient YBCO column around the BZO 1D-APCs due to the large lattice mismatch of ∼7.7% between the BZO (3a = 1.26 nm) and YBCO (c = 1.17 nm), which has been blamed for the reduced pinning efficiency of BZO 1D-APCs. Herein, we report a dynamic lattice enlargement approach on the tensile strained YBCO lattice during the BZO 1D-APCs growth to induce c -axis elongation of the YBCO lattice up to 1.26 nm near the BZO 1D-APC/YBCO interface via Ca/Cu substitution on single Cu-O planes of YBCO, which prevents the interfacial defect formation by reducing the BZO/YBCO lattice mismatch to ∼1.4%. Specifically, this is achieved by inserting thin Ca 0.3 Y 0.7 Ba 2 Cu 3 O 7− x (CaY-123) spacers as the Ca reservoir in 2–6 vol.% BZO/YBCO nanocomposite multilayer (ML) films. A defect-free, coherent BZO 1D-APC/YBCO interface is confirmed in transmission electron microscopy and elemental distribution analyses. Excitingly, up to five-fold enhancement of J c ( B ) at magnetic field B = 9.0 T// c -axis and 65 K–77 K was obtained in the ML samples as compared to their BZO/YBCO single-layer (SL) counterpart’s. This has led to a record high pinning force density F p together with significantly enhanced B max at which F p reaches its maximum value F p,max for BZO 1D-APCs at B // c -axis. At 65 K, the F p,max ∼158 GN m −3 and B max ∼ 8.0 T for the 6% BZO/YBCO ML samples represent a significant enhancement over F p,max ∼ 36.1 GN m −3 and B max ∼ 5.0 T for the 6% BZO/YBCO SL counterparts. This result not only illustrates the critical importance of a coherent BZO 1D-APC/YBCO interface in the pinning efficiency, but also provides a facile scheme to achieve such an interface to restore the pristine pinning efficiency of the BZO 1D-APCs.