  1. The newly developed FeMnAlNiTi shape memory alloy (SMA) holds significant promise due to its desirable properties including ease of processing, room temperature superelasticity, a wide superelastic window of operation, and high transformation stress levels. In this study, we report single crystals with tensile axis near h123i exhibiting transformation strains of 9% with a high trans- formation stress of 700 MPa. The functional performance revealed excellent recovery of 98% of the applied strain in an incremental strain test for each of the 40 applied cycles. Concomitantly, the total residual strain increased after each cycle. Accumulation of residual martensite is observed possibly due to pinning of austenite/martensite (A/M) interface. Subsequently, under structural fatigue loading with a constant strain amplitude of 1%, the recoverable strains saturate around 1.15% in local residual martensite domains. Intermittent enhancement of recoverable strains is observed due to transformation triggered in previously untransformed domains. Eventually, fatigue failure occur- red after 2046 cycles and the dominant mechanism for failure was microcrack initiation and coalescence along the A/M interface. Thus, it is concluded that interfacial dislo- cations, which play a crucial role in the superelastic (SE) functionality, invariably affect the structural fatigue per- formance by acting as the weakest link in the microstructure. 
    more » « less
  2. Abstract

    A face-centered-cubic (fcc) oriented FeCoCrNiAl0.5dual-phase high entropy alloy (HEA) was plastically strained in uniaxial compression at 77K and 293K and the underlying deformation mechanisms were studied. The undeformed microstructure consists of a body-centered-cubic (bcc)/B2 interdendritic network and precipitates embedded in 〈001〉-oriented fcc dendrites. In contrast to other dual-phase HEAs, at both deformation temperatures a steep rise in the stress-strain curves occurs above 23% total axial strain. As a result, the hardening rate associated saturates at the unusual high value of ~6 GPa. Analysis of the strain partitioning between fcc and bcc/B2 by digital image correlation shows that the fcc component carries the larger part of the plastic strain. Further, electron backscatter diffraction and transmission electron microscopy evidence ample fcc deformation twinning both at 77K and 293K, while slip activity only is found in the bcc/B2. These results may guide future advancements in the design of novel alloys with superior toughening characteristics.

     
    more » « less