Two-inch diameter α -Ga 2 O 3 films with thickness ∼4 μ m were grown on basal plane sapphire by Halide Vapor Phase Epitaxy (HVPE) and doped with Sn in the top ∼1 μ m from the surface. These films were characterized with High-Resolution X-ray Diffraction (HRXRD), Scanning Electron Microscope (SEM) imaging in the Secondary Electron (SE) and Micro-cathodoluminescence (MCL) modes, contactless sheet resistivity mapping, capacitance-voltage, current-voltage, admittance spectra, and Deep Level Transient Spectroscopy (DLTS) measurements. The edge and screw dislocations densities estimated from HRXRD data were respectively 7.4 × 10 9 cm −2 and 1.5 × 10 7 cm −2 , while the films had a smooth surface with a low density (∼10 3 cm −2 ) of circular openings with diameters between 10 and 100 μ m. The sheet resistivity of the films varied over the entire 2-inch diameter from 200 to 500 Ω square −1 . The net donor concentration was ∼10 18 cm −3 near the surface and increased to ∼4 × 10 18 cm −3 deeper inside the sample. The deep traps observed in admittance and DLTS spectra had levels at E c −0.25 eV and E c −0.35 eV, with concentration ∼10 15 cm −3 and E c −1 eV with concentration ∼10 16 cm −3 . 

Thick (23 µm) films of κ-Ga 2 O 3 were grown by Halide Vapor Phase Epitaxy (HVPE) on GaN/sapphire templates at 630 °C. X-ray analysis confirmed the formation of single-phase κ-Ga 2 O 3 with half-widths of the high-resolution x-ray diffraction (004), (006), and (008) symmetric reflections of 4.5 arc min and asymmetric (027) reflection of 14 arc min. Orthorhombic κ-Ga 2 O 3 polymorph formation was confirmed from analysis of the Kikuchi diffraction pattern in electron backscattering diffraction. Secondary electron imaging indicated a reasonably flat surface morphology with a few (area density ∼10 3  cm −2 ) approximately circular (diameter ∼50–100 µm) uncoalesced regions, containing κ-Ga 2 O 3 columns with in-plane dimensions and a height of about 10 µm. Micro-cathodoluminescence (MCL) spectra showed a wide 2–3.5 eV band that could be deconvoluted into narrower bands peaked at 2.59, 2.66, 2.86, and 3.12 eV. Ni Schottky diodes prepared on the films showed good rectification but a high series resistance. The films had a thin near-surface region dominated by E c − 0.7 eV deep centers and a deeper region (∼2 µm from the surface) dominated by shallow donors with concentrations of ≤10 16  cm −3 . Photocurrent and photocapacitance spectra showed the presence of deep compensating acceptors with optical ionization energies of ∼1.35 and 2.3 eV, the latter being close to the energy of one of the MCL bands. Deep level transient spectroscopy revealed deep traps with energies near 0.3, 0.6, 0.7, 0.8, and 1 eV from the conduction band edge. The results show the potential of HVPE to grow very thick κ-Ga 2 O 3 on GaN/sapphire templates.