Search for: All records

Nanotubes assembled from macrocyclic precursors offer a unique combination of low dimensionality, structural rigidity, and distinct interior and exterior microenvironments. Usually the weak stacking energies of macrocycles limit the length and mechanical strength of the resultant nanotubes. Imine‐linked macrocycles were recently found to assemble into high‐aspect ratio (>10³), lyotropic nanotubes in the presence of excess acid. Yet these harsh conditions are incompatible with many functional groups and processing methods, and lower acid loadings instead catalyze macrocycle degradation. Here we report pyridine‐2,6‐diimine‐linked macrocycles that assemble into high‐aspect ratio nanotubes in the presence of less than 1 equiv of CF₃CO₂H per macrocycle. Analysis by gel permeation chromatography and fluorescence spectroscopy revealed a cooperative self‐assembly mechanism. The low acid concentrations needed to induce assembly enabled nanofibers to be obtained by touch‐spinning, which exhibit higher Young's moduli (1.33 GPa) than many synthetic polymers and biological filaments. These findings represent a breakthrough in the design of inverse chromonic liquid crystals, as assembly under such mild conditions will enable the design of structurally diverse and mechanically robust nanotubes from synthetically accessible macrocycles.

Nanotubes assembled from macrocyclic precursors offer a unique combination of low dimensionality, structural rigidity, and distinct interior and exterior microenvironments. Usually the weak stacking energies of macrocycles limit the length and mechanical strength of the resultant nanotubes. Imine‐linked macrocycles were recently found to assemble into high‐aspect ratio (>10³), lyotropic nanotubes in the presence of excess acid. Yet these harsh conditions are incompatible with many functional groups and processing methods, and lower acid loadings instead catalyze macrocycle degradation. Here we report pyridine‐2,6‐diimine‐linked macrocycles that assemble into high‐aspect ratio nanotubes in the presence of less than 1 equiv of CF₃CO₂H per macrocycle. Analysis by gel permeation chromatography and fluorescence spectroscopy revealed a cooperative self‐assembly mechanism. The low acid concentrations needed to induce assembly enabled nanofibers to be obtained by touch‐spinning, which exhibit higher Young's moduli (1.33 GPa) than many synthetic polymers and biological filaments. These findings represent a breakthrough in the design of inverse chromonic liquid crystals, as assembly under such mild conditions will enable the design of structurally diverse and mechanically robust nanotubes from synthetically accessible macrocycles.

2D covalent organic frameworks (2D COFs) are a unique materials platform that combines covalent connectivity, structural regularity, and molecularly precise porosity. However, 2D COFs typically form insoluble aggregates, thus limiting their processing via additive manufacturing techniques. In this work, colloidal suspensions of boronate‐ester‐linked 2D COFs are used as a spray‐coating ink to produce large‐area 2D COF thin films. This method is synthetically general, with five different 2D COFs prepared as colloidal inks and subsequently spray‐coated onto a diverse range of substrates. Moreover, this approach enables the deposition of multiple 2D COF materials simultaneously, which is not possible by polymerizing COFs on substrates directly. When combined with stencil masks, spray‐coated 2D COFs are rapidly deposited as thin films larger than 200 cm²with line resolutions below 50 µm. To demonstrate that this deposition scheme preserves the desirable attributes of 2D COFs, spray‐coated 2D COF thin films are incorporated as the active material in acoustic sensors. These 2D‐COF‐based sensors have a 10 ppb limit‐of‐quantification for trimethylamine, which places them among the most sensitive sensors for meat and seafood spoilage. Overall, this work establishes a scalable additive manufacturing technique that enables the integration of 2D COFs into thin‐film device architectures.

2D polymers (2DPs) are promising as structurally well‐defined, permanently porous, organic semiconductors. However, 2DPs are nearly always isolated as closed shell organic species with limited charge carriers, which leads to low bulk conductivities. Here, the bulk conductivity of two naphthalene diimide (NDI)‐containing 2DP semiconductors is enhanced by controllably n‐doping the NDI units using cobaltocene (CoCp₂). Optical and transient microwave spectroscopy reveal that both as‐prepared NDI‐containing 2DPs are semiconducting with sub‐2 eV optical bandgaps and photoexcited charge‐carrier lifetimes of tens of nanoseconds. Following reduction with CoCp₂, both 2DPs largely retain their periodic structures and exhibit optical and electron‐spin resonance spectroscopic features consistent with the presence of NDI‐radical anions. While the native NDI‐based 2DPs are electronically insulating, maximum bulk conductivities of >10⁻⁴ S cm⁻¹are achieved by substoichiometric levels of n‐doping. Density functional theory calculations show that the strongest electronic couplings in these 2DPs exist in the out‐of‐plane (π‐stacking) crystallographic directions, which indicates that cross‐plane electronic transport through NDI stacks is primarily responsible for the observed electronic conductivity. Taken together, the controlled molecular doping is a useful approach to access structurally well‐defined, paramagnetic, 2DP n‐type semiconductors with measurable bulk electronic conductivities of interest for electronic or spintronic devices.