skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • Home
  • Search Results
  • Page 1 of 1

Search for: All records

Creators/Authors contains: "W. Palosz"

Note: When clicking on a Digital Object Identifier (DOI) number, you will be taken to an external site maintained by the publisher. Some full text articles may not yet be available without a charge during the embargo (administrative interval).
What is a DOI Number?

Some links on this page may take you to non-federal websites. Their policies may differ from this site.

  1. ; ; ; ; ; ; (, Optical materials express)
    We present mid-IR spectroscopic characterization of the low-phonon chalcogenide glass, Ga2Ge5S13 (GGS) doped with Er3+ ions. Under the excitation at ∼800 nm, Er3+:GGS exhibited broad mid-IR emission bands centered at ∼2.7, ∼3.5, and ∼4.5 µm at room temperature. The emission lifetime of the 4I9/2 level of Er3+ ions in GGS glass was found to be millisecond-long at room temperature. The measured fluorescence lifetimes were nearly independent of temperature, indicating negligibly small nonradiative decay rate for the 4I9/2 state, as can be expected for a low-maximum-phonon energy host. The transition line-strengths, radiative lifetimes, fluorescence branching ratios were calculated by using the Judd-Ofelt method. The peak stimulated emission cross-section of the 4I9/2 → 4I11/2 transition of Er3+ ion was determined to be ∼0.10×10−20 cm2 at room temperature. 
    more » « less
    Accepted Manuscript Full Text Available