Search for: All records

The self-assembly and coordination of amphiphiles comprised of naphthalenediimide (NDI) and bis(indolyl)methane (BIM) chromophores were investigated as a function of pH and metal. As observed by TEM, SEM and AFM imaging, the self-assembly of NDI-BIM 1 produced irregular nanostructures at neutral pH in CH 3 CN–H 2 O (1 : 1); whereas, well-defined nanotubes were observed at pH 2. Conversely, Fmoc-protected, NDI-BIM 2 formed nanotubes at neutral pH and nonspecific aggregates at pH 2. Upon coordination of Cu 2+ ions to the bis(indoyl)methane moiety, a reorganization from nanotubes to vesicular structures was observed. 

The self-assembly and covalent crosslinking of a camptothecin (CPT) tetrapeptide nanotube is reported. Intermolecular disulfide bond formation of a self-assembled CPT-peptide reversibly stabilized the nanotubes toward dissociation at low concentrations, resulting in inhibited release of CPT. In the presence of dithiothreitol (DTT), the release of CPT was significantly accelerated. The crosslinked nanotubes also exhibited in vitro cytotoxicity against human non-small cell lung cancer cell lines A549 and H460. 

The self-assembly of bolaamphiphiles comprised of a central photochromic dithienylethene (DTE) chromophore was investigated in aqueous media. Irradiation at 254 nm induced a conversion from the open to closed states of the DTE chromophores. Whereas, in water, irradiation produced a photostationary state of 20 : 80 (open/closed), in methanol the ratio improved to 10 : 90 (open/closed). The open → closed transition was accompanied by the formation of 1D nanofibers during incubation in darkness. 

Achieving the co-assembly of more than one component represents an important challenge in the drive to create functional self-assembled nanomaterials. Multicomponent nanomaterials comprised of several discrete, spatially sorted domains of components with high degrees of internal order are particularly important for applications such as optoelectronics. In this work, single-walled carbon nanotubes (SWNTs) were threaded through the inner channel of nanotubes formed by the bolaamphiphilic self-assembly of a naphthalenediimide-lysine (NDI-Bola) monomer. The self-assembly process was driven by electrostatic interactions, as indicated by ζ -potential measurements, and cation–π interactions between the surface of the SWNT and the positively charged, NDI-Bola nanotube interior. To increase the threading efficiency, the NDI-Bola nanotubes were fragmented into shortened segments with lengths of <100 nm via sonication-induced shear, prior to co-assembly with the SWNTs. The threading process created an initial composite nanostructure in which the SWNTs were threaded by multiple, shortened segments of the NDI-Bola nanotube that progressively re-elongated along the SWNT surface into a continuous radial coating around the SWNT. The resultant composite structure displayed NDI-Bola wall thicknesses twice that of the parent nanotube, reflecting a bilayer wall structure, as compared to the monolayer structure of the parent NDI-Bola nanotube. As a final, co-axial outer layer, poly( p -phenyleneethynylene) (PPE-SO 3 Na, M W = 5.76 × 10 4 , PDI – 1.11) was wrapped around the SWNT/NDI-Bola composite resulting in a three-component (SWNT/NDI-Bola/PPE-SO 3 Na) composite nanostructure. 

This work demonstrates that sonication, followed by polymer-wrapping, is an effective strategy to modulate the length of self-assembled nanotubes. The length distributions of the nanotubes were controlled by varying the amplitude of sonication. Wrapping the nanotubes with ionic polymers suspended the propensity of the nanotube fragments to re-assemble over time into their elongated precursors.