Search for: All records

Abstract Localized states in two-dimensional (2D) transition metal dichalcogenides (TMDCs) have been the subject of intense study, driven by potential applications in quantum information science. Despite the rapidly growing knowledge surrounding these emitters, their microscopic nature is still not fully understood, limiting their production and application. Motivated by this challenge, and by recent theoretical and experimental evidence showing that nanowrinkles generate strain-localized room-temperature emitters, we demonstrate a method to intentionally induce wrinkles with collections of stressors, showing that long-range wrinkle direction and position are controllable with patterned array design. Nano-photoluminescence (nano-PL) imaging combined with detailed strain modeling based on measured wrinkle topography establishes a correlation between wrinkle properties, particularly shear strain, and localized exciton emission. Beyond the array-induced wrinkles, nano-PL spatial maps further reveal that the strain environment around individual stressors is heterogeneous due to the presence of fine wrinkles that are less deterministic. At cryogenic temperatures, antibunched emission is observed, confirming that the nanocone-induced strain is sufficiently large for the formation of quantum emitters. At 300 K, detailed nanoscale hyperspectral images uncover a wide range of low-energy emission peaks originating from the fine wrinkles, and show that the states can be tightly confined to regions <10 nm, even in ambient conditions. These results establish a promising potential route towards realizing room temperature quantum emission in 2D TMDC systems. 

When combined with nanostructured substrates, two-dimensional semiconductors can be engineered with strain to tailor light–matter interactions on the nanoscale. Recently, room-temperature nanoscale exciton localization with controllable wrinkling in 1L-WSe2 was achieved using arrays of gold nanocones. Here, the characterization of quantum dot-like states and single-photon emitters in the 1L-WSe2/nanocone system is reported. The nanocones induce a wide range of strains, and as a result, a diverse ensemble of narrowband, potential single-photon emitters is observed. The distribution of emitter energies reveals that most reside in two spectrally isolated bands, leaving a less populated intermediate band that is spectrally isolated from the ensembles. The spectral isolation is advantageous for high-purity quantum light emitters, and anti-bunched emission from one of these states is confirmed up to 25 K. Although the spatial distribution of strain is expected to influence the orientation of the transition dipoles of the emitters, multimodal emission polarization anisotropy and atomic force microscopy reveal that the macroscopic orientation of the wrinkles is not a good predictor of dipole orientation. Finally, the emission is found to change with thermal cycling from 4 to 290 K and back to 4 K, highlighting the need to control factors such as temperature-induced strain to enhance the robustness of this quantum emitter platform. The initial characterization here shows that controlled nanowrinkles of 1L-WSe2 generate quantum light in addition to uncovering potential challenges that need to be addressed for their adoption into quantum photonic technologies.