Membrane-based separations offer the potential for the lowest energy demand requirements of all separation options. Among all nanoporous membranes, the carbon molecular sieves (CMS), metal-organic frameworks (MOFs), and mixed-matrix membranes (MMMs) with angstrom level molecular discrimination properties makes them appealing for separating a wide spectrum of gas-pairs. Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the iridization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C2H6, C2H4, C3H8, C3H6 adsorption capacities reached to 42.61, 2.56, 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane were formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.
more »
« less
Zeolitic Imidazolate Framework Membranes Supported on Macroporous Carbon Hollow Fibers by Fluidic Processing Techniques
This study addresses the challenge of generalizable fabrication of metal‐organic framework (particularly zeolitic imidazolate frameworks (ZIF)) hollow fiber membranes that can allow a broader range of separations including hydrocarbon (“petrochemical”) as well as organics/water (“biorefining”) separations. We report a novel strategy that combines fluidic membrane processing with chemically inert carbon hollow fibers to produce robust ZIF membranes. Macroporous carbon hollow fibers are successfully fabricated by pyrolytic conversion of cross‐linked polymer hollow fibers. This step allows the use of a wide range of relatively aggressive fluidic processing solvents and conditions. Using these inert fiber supports, the fabrication of ZIF‐90 membranes is demonstrated and their butane isomer separations are investigated for the first time. Furthermore, ZIF membranes on carbon hollow fibers can be used in the separation of water/organic mixtures without the issue of fiber swelling or dissolution as seen in ZIF/polymer hollow fiber membranes. ZIF‐8/carbon membranes show stable operation spanning several days for dehydration of furfural and ethanol, with high water permeances and separation factors. In all cases, the ZIF membranes are prepared without any seeding, support modification, or postsynthesis procedures, thereby simplifying the fabrication process and increasing the potential for larger‐scale membrane fabrication.
more »
« less
- Award ID(s):
- 1264874
- PAR ID:
- 10035725
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials Interfaces
- Volume:
- 4
- Issue:
- 12
- ISSN:
- 2196-7350
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Recently, metal–organic framework (MOF)-based polymeric substrates show promising performance in many engineering and technology fields. However, a commonly known drawback of MOF/polymer composites is MOF crystal encapsulation and reduced surface area. This work reports a facile and gentle strategy to produce self-supported MOF predominant hollow fiber mats. A wide range of hollow MOFs including MIL-53(Al)–NH 2 , Al-PMOF, and ZIF-8 are successfully fabricated by our synthetic method. The synthetic strategy combines atomic layer deposition (ALD) of metal oxides onto polymer fibers and subsequent selective removal of polymer components followed by conversion of remaining hollow metal oxides into freestanding MOF predominant hollow fiber structures. The hollow MOFs show boosted surface area, superb porosity, and excellent pore accessibility, and exhibit a significantly improved performance in CO 2 adsorption (3.30 mmol g −1 ), CO 2 /N 2 separation selectivity (24.9 and 21.2 for 15/85 and 50/50 CO 2 /N 2 mixtures), and catalytic removal of HCHO (complete oxidation of 150 ppm within 60 min).more » « less
-
Polymer porous membranes are crucial in various applications, including water filtration, tissue engineering, and drug administration. Conventional far‐field electrospinning (FFES) is widely used for producing polymeric membranes due to its cost‐effectiveness, scalability, and flexibility in using many polymers. However, FFES has limitations in controlling pore form and size, as it produces randomly oriented fibers that lead to inconsistent and noncustomizable pore sizes. To address these limitations, this work combines near‐field electrospinning (NFES) with thermal treatment of polymer fibers and membranes. NFES offers more precise control over fiber placement and alignment, producing well‐defined fiber patterns with consistent and customizable pore sizes without compromising the thickness of membranes. By exploring the interplay between polymer behavior, thermal effects, and capillary action, the differences in pore area under various temperatures and fiber spacings are characterized. Additionally, this study investigates the influence of multilayer infusion on pore size and geometric arrangement by examining multilayer configurations stacked at various angles. The results indicate that increasing the number of layers leads to decreased pore size, while the alignment of infused fibers affects pore shape. This integrated approach enhances control over membrane characteristics, improving the performance and consistency of polymer porous membrane fabrication across various applications.more » « less
-
Graphene oxide/polymer composite water filtration membranes were developed via coalescence of graphene oxide (GO) stabilized Pickering emulsions around a porosity-generating polymer. Triptycene poly(ether ether sulfone)-CH2NH2:HCl polymer interacts with the GO at the water−oil interface, resulting in stable Pickering emulsions. When they are deposited and dried on polytetrafluoroethylene substrate, the emulsions fuse to form a continuous GO/polymer composite membrane. X-ray diffraction and scanning electron microscopy demonstrate that the intersheet spacing and thickness of the membranes increased with increasing polymer concentration, confirming the polymer as the spacer between the GO sheets. The water filtration capability of the composite membranes was tested by removing Rose Bengal from water, mimicking separations of weak black liquor waste. The composite membrane achieved 65% rejection and 2500 g m−2 h−1 bar−1. With high polymer and GO loading, composite membranes give superior rejection and permeance performance when compared with a GO membrane. This methodology for fabrication membranes via GO/polymer Pickering emulsions produces membranes with a homogeneous morphology and robust chemical separation strength.more » « less
-
Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the thermal and chemical imidization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C3H8, C3H6, CO2, and H2) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C3H8, C3H6 adsorption capacities reached 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane was formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.more » « less