Tri‐cation (Cs+/CH3NH3+/CH(NH2)2+) and dual‐anion (Br–/I–) perovskites are promising light absorbers for inexpensive infrared (IR) photodetectors but degrade under prolonged IR exposure. Here, stable IR photodetectors based on electrospun tri‐cation perovskite fibers infiltrated with hole‐transporting π‐conjugated small molecule 2,2′,7,7′‐tetrakis[
It is a great challenge to obtain broadband response perovskite photodetectors (PPDs) due to the relatively large bandgaps of the most used methylammonium lead halide perovskites. The response range of the reported PPDs is limited in the ultraviolet–visible range. Here, highly sensitive PPDs are successfully fabricated with low bandgap (≈1.25 eV) (FASnI3)0.6(MAPbI3)0.4perovskite as active layers, exhibiting a broadband response from 300 to 1000 nm. The performance of the PPDs can be optimized by adjusting the thicknesses of the perovskite and C60layers. The optimized PPDs with 1000 nm thick perovskite layer and 70 nm thick C60layer exhibit an almost flat external quantum efficiency (EQE) spectrum from 350 to 900 nm with EQE larger than 65% under −0.2 V bias. Meanwhile, the optimized PPDs also exhibit suppressed dark current of 3.9 nA, high responsivity (
- NSF-PAR ID:
- 10041356
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 27
- Issue:
- 42
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract N ,N ‐di(4‐methoxyphenyl)amino]‐9,9‐spirobifluorene (Spiro‐OMeTAD) are demonstrated. These hybrid perovskite photodetectors operate at a low bias of 5 V and exhibit ultra‐high gains with external quantum efficiencies (EQEs) as high as 3009%, decreasing slightly to ≈2770% after 3 months in air. These EQE values are almost ten times larger than those measured for photodetectors comprising bilayer perovskite/Spiro‐OMeTAD films. A high density of charge traps on electrospun fiber surfaces gives rise to a photomultiplication effect in which photogenerated holes can travel through the active layer multiple times before recombining with trapped electrons. Time‐resolved photoluminescence and conductive atomic force microscopy mapping reveal the improved performance of electrospun fibers to originate from the significantly enhanced interfacial surface area between the perovskite and Spiro‐OMeTAD compared to bilayers. As a solution‐based, scalable and continuous method of depositing perovskite layers, electrospinning thus presents a promising strategy for the inexpensive fabrication of high‐performance IR photodetectors for applications ranging from information technology to imaging. -
more » « less
Abstract Perovskite light‐emitting diodes (LEDs) have recently attracted great research interest for their narrow emissions and solution processability. Remarkable progress has been achieved in green perovskite LEDs in recent years, but not blue or red ones. Here, highly efficient and spectrally stable red perovskite LEDs with quasi‐2D perovskite/poly(ethylene oxide) (PEO) composite thin films as the light‐emitting layer are reported. By controlling the molar ratios of organic salt (benzylammonium iodide) to inorganic salts (cesium iodide and lead iodide), luminescent quasi‐2D perovskite thin films are obtained with tunable emission colors from red to deep red. The perovskite/polymer composite approach enables quasi‐2D perovskite/PEO composite thin films to possess much higher photoluminescence quantum efficiencies and smoothness than their neat quasi‐2D perovskite counterparts. Electrically driven LEDs with emissions peaked at 638, 664, 680, and 690 nm have been fabricated to exhibit high brightness and external quantum efficiencies (EQEs). For instance, the perovskite LED with an emission peaked at 680 nm exhibits a brightness of 1392 cd m−2and an EQE of 6.23%. Moreover, exceptional electroluminescence spectral stability under continuous device operation has been achieved for these red perovskite LEDs.
-
more » « less
Atomically thin 2D transition metal dichalcogenides (TMDs), such as MoS2, are promising candidates for nanoscale photonics because of strong light–matter interactions. However, Fermi‐level pinning due to metal‐induced gap states (MIGS) at the metal–monolayer (1L)‐MoS2interface limits the application of optoelectronic devices based on conventional metals due to high contact resistance. On the other hand, a semimetal–TMD–semimetal device can overcome this limitation, where the MIGS are sufficiently suppressed allowing ohmic contacts. Herein, the optoelectronic performance of a bismuth–1L‐MoS2–bismuth device with ohmic electrical contacts and extraordinary optoelectronic properties is demonstrated. To address the wafer‐scale production, full coverage 1L‐MoS2grown by chemical vapor deposition. High photoresponsivity of 300 A W−1at wavelength 400 nm measured at 77 K, which translates into an external quantum efficiency (EQE) ≈1000 or 105%, is measured. The 90% rise time of the devices at 77 K is 0.1 ms, suggesting they can operate at the speed of ≈10 kHz. High‐performance broadband photodetector with spectral coverage ranging from 380 to 1000 nm is demonstrated. The combination of large‐array device fabrication, high sensitivity, and high‐speed response offers great potential for applications in photonics, including integrated optoelectronic circuits.
-
more » « less
Abstract Room‐temperature solution‐processed flexible photodetectors with spectral response from 300 to 2600 nm are reported. Solution‐processed polymeric thin film with transparency ranging from 300 to 7000 nm and superior electrical conductivity as the transparent electrode is reported. Solution‐processed flexible broadband photodetectors with a “vertical” device structure incorporating a perovskite/PbSe quantum dot bilayer thin film based on the above solution‐processed transparent polymeric electrode are demonstrated. The utilization of perovskite/PbSe quantum dot bilayer thin film as the photoactive layer extends spectral response to infrared region and boosts photocurrent densities in both visible and infrared regions through the trap‐assisted photomultiplication effect. Operated at room temperature and under an external bias of ‐1 V, the solution‐processed flexible photodetectors exhibit over 230 mA W‐1responsivity, over 1011 cm Hz1/2/W photodetectivity from 300 to 2600 nm and ≈70 dB linear dynamic ranges. It is also found that the solution‐processed flexible broadband photodetectors exhibit fast response time and excellent flexibility. All these results demonstrate that this work develop a facile approach to realize room‐temperature operated ultrasensitive solution‐processed flexible broadband photodetectors with “vertical” device structure through solution‐processed transparent polymeric electrode.
-
more » « less
Abstract The ability to produce atomically precise, artificial oxide heterostructures allows for the possibility of producing exotic phases and enhanced susceptibilities not found in parent materials. Typical ferroelectric materials either exhibit large saturation polarization away from a phase boundary or large dielectric susceptibility near a phase boundary. Both large ferroelectric polarization and dielectric permittivity are attained wherein fully epitaxial (PbZr0.8Ti0.2O3)
n /(PbZr0.4Ti0.6O3)2n (n = 2, 4, 6, 8, 16 unit cells) superlattices are produced such that the overall film chemistry is at the morphotropic phase boundary, but constitutive layers are not. Long‐ (n ≥ 6) and short‐period (n = 2) superlattices reveal large ferroelectric saturation polarization (P s= 64 µC cm−2) and small dielectric permittivity (εr≈ 400 at 10 kHz). Intermediate‐period (n = 4) superlattices, however, exhibit both large ferroelectric saturation polarization (P s= 64 µC cm−2) and dielectric permittivity (εr= 776 at 10 kHz). First‐order reversal curve analysis reveals the presence of switching distributions for each parent layer and a third, interfacial layer wherein superlattice periodicity modulates the volume fraction of each switching distribution and thus the overall material response. This reveals that deterministic creation of artificial superlattices is an effective pathway for designing materials with enhanced responses to applied bias.