Polymer matrix composites are popular in the aerospace industry due to their high strength to weight ratio. While they have become popular, understanding and predicting their specific damage evolution mechanisms remains a challenge especially in designing with damage tolerance criteria. One challenge often faced is the presence of surface damage either induced during manufacturing, machining, or service of a composite part. While many studies have investigated how quasi-static, low-velocity, and ballistic impact results in damage in the material, there remains a need to further understand the reduction in performance that results from such surface damage. In this work, micro-indentation was conducted on a unidirectional IM7/8552 laminate composite specimen to induce quasi-static impact damage that results in surface damage. The specimen was then loaded in tension to 33% of its expected failure load and imaged using synchrotron X-ray micro-computed tomography to qualitatively investigate the progression of surface damage into sub-surface damage. This work shows that at 33% of tensile failure load, surface damage propagates into delamination and fiber breakage of plies directly sub-surface. This work sheds light on the progression of surface damage at loads less than 50% of the ultimate strength of a unidirectional laminate composite.
more »
« less
Evaluation of the Effect of Thermal Oxidation and Moisture on the Interfacial Shear Strength of Unidirectional IM7/BMI Composite by Fiber Push-in Nanoindentation
Fiber push-in nanoindentation is conducted on a unidirectional carbon fiber reinforced bismaleimide resin composite (IM7/BMI) after thermal oxidation to determine the interfacial shear strength. A unidirectional IM7/BMI laminated plate is isothermally oxidized under various conditions: in air for 2 months at 195 °C and 245 °C, and immersed in water for 2 years at room temperature to reach a moisturesaturated state. The water-immersed specimens are subsequently placed in a preheated environment at 260 °C to receive sudden heating, or are gradually heated at a rate of approximately 6 °C/min. A flat punch tip of 3 μm in diameter is used to push the fiber into the matrix while the resulting loaddisplacement data is recorded. From the load-displacement data, the interfacial shear strength is determined using a shear-lag model, which is verified by finite element method simulations. It is found that thermal oxidation at 245 °C in air leads to a significant reduction in interfacial shear strength of the IM7/BMI unidirectional composite, while thermal oxidation at 195 °C and moisture concentration have a negligible effect on the interfacial shear strength. For moisture-saturated specimens under a slow heating rate, there is no detectable reduction in the interfacial shear strength. In contrast, the moisture-saturated specimens under sudden heating show a significant reduction in interfacial shear strength. Scanning electron micrographs of IM7/BMI composite reveal that both thermal oxidation at 245 °C in air and sudden heating induced microcracks and debonding along the fiber/matrix interface, thereby weakening the interface, which is the origin of failure mechanism.
more »
« less
- Award ID(s):
- 1636306
- PAR ID:
- 10048020
- Date Published:
- Journal Name:
- Experimental Mechanics
- ISSN:
- 0014-4851
- Page Range / eLocation ID:
- 1-13
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
This paper investigates the validity of the interpretation of results from testing saturated axisymmetric triaxial compression (ATC) sand specimens utilising three-dimensional (3D) synchrotron micro-computed tomography (SMT) to probe localised events that are completely missed or misinterpreted when analysing ATC measurements based on global standard measurements. Drained and undrained experiments were conducted at low and high back-pressures (BPs) coupled with multiple in situ 3D SMT to acquire high-resolution scans of the specimens at different axial strains. Specimens tested under low BP exhibited a large pore air volume change, which was not detected by the pump system that represents standard volume measurement. The increase in air volume caused a significant reduction in the degree of saturation leading to a possible transition from saturated to partially saturated constitutive behaviour. Undrained experiments exhibited a significant volume change contrary to the assumption of negligible volumetric strain for saturated undrained experiments. Air bubbles within the shear band for drained and undrained low-BP specimens showed opposite capillary pressure responses, increased for drained and decreased for undrained cases, due to the variation in the mechanism by which each of the two experiments predominantly counters the volume expansion within the shear band.more » « less
-
Polymer matrix composites have high strengths in tension. However, their compressive strengths are much lower than their tensile strengths due to their weak fiber/matrix interfacial shear strengths. We recently developed a new approach to fabricate composites by overwrapping individual carbon fibers or fiber tows with a carbon nanotube sheet and subsequently impregnate them into a matrix to enhance the interfacial shear strengths without degrading the tensile strengths of the carbon fibers. In this study, a theoretical analysis is conducted to identify the appropriate thickness of the nanocomposite interphase region formed by carbon nanotubes embedded in a matrix. Fibers are modeled as an anisotropic elastic material, and the nanocomposite interphase region and the matrix are considered as isotropic. A microbuckling problem is solved for the unidirectional composite under compression. The analytical solution is compared with finite element simulations for verification. It is determined that the critical load at the onset of buckling is lower in an anisotropic carbon fiber composite than in an isotropic fibfer composite due to lower transverse properties in the fibers. An optimal thickness for nanocomposite interphase region is determined, and this finding provides a guidance for the manufacture of composites using aligned carbon nanotubes as fillers in the nanocomposite interphase region.more » « less
-
ABSTRACT This study investigates linkages between volume change, pore fluid drainage, shear wave velocity, and temperature of soft clays using a thermal triaxial cell equipped with bender elements, a measurement approach that has not been explored widely in past thermo-mechanical studies. Two kaolinite specimens were consolidated mechanically to a normally consolidated state and then subjected to drained and undrained heating-cooling cycles, respectively. After cooling, the specimens were subjected to further mechanical consolidation to evaluate changes in apparent preconsolidation stress. Both specimens showed net contractive thermal strains after a heating-cooling cycle and overconsolidated behavior during mechanical compression immediately after cooling. The shear wave velocity increased during drained heating, but negligible changes were observed during drained cooling, indicating permanent hardening because of thermal consolidation during the heating-cooling cycle. The shear wave velocity decreased during undrained heating because of a reduction in effective stress associated with thermal pressurization of the pore fluid but subsequently increased when drainage was permitted at elevated temperature. The shear wave velocity increased slightly during undrained cooling but decreased when drainage was permitted at room temperature. Net increases in small-strain shear modulus of 17 and 11 % after heating-cooling cycles under drained and undrained (with drainage after reaching stable temperatures) conditions, respectively, provide further evidence to the potential of thermal soil improvement of normally consolidated clays. Transient changes in shear modulus also highlight the importance of considering drainage conditions and corresponding changes in effective stress state during heating-cooling cycles.more » « less
-
High performance carbon fibers are widely used as fiber reinforcements in composite material systems for aerospace, automotive, and defense applications. Longitudinal tensile failure of such composite systems is a result of clustering of single fiber tensile failures occurring at the microscale, on the order of a few microns to a few hundred microns. Since fiber tensile strength at the microscale has a first order effect on composite strength, it is important to characterize the strength of single fibers at microscale gage lengths which is extremely challenging. An experimental technique based on a combination of transverse loading of single fibers under SEM with DIC is a potential approach to access microscale gage lengths. The SEM-DIC technique requires creation of uniform, random, and contrastive sub-microscale speckle pattern on the curved fiber surface for accurate strain measurements. In this paper, we investigate the formation of such sub-microscale speckle patterns on individual sized IM7 carbon fibers of nominal diameter 5.2 µm via sputter coating. Various process conditions such as working pressure, sputtering current, and coating duration are investigated for pattern creation on fiber surface using a gold-palladium (Au-Pd) target. A nanocluster type sub-microscale pattern is obtained on the fiber surface for different coating conditions. Numerical translation experiments are performed using the obtained patterns to study image correlation and identify a suitable pattern for SEM-DIC experiments. The pattern obtained at a working pressure of 120–140 mTorr with 50 mA current for a duration of 10 min is found to have an average speckle size of 53 nm and good contrast for image correlation. Rigid body translation SEM experiments for drift/distortion correction using a sized IM7 carbon fiber coated with the best patterning conditions showed that Stereo-SEM-DIC is needed for accurately characterizing fiber strain fields due to its curved surface. The effect of sputter coating on fiber tensile strength and strain is investigated via single fiber tensile tests. Results showed that there is no significant difference in the mean tensile strength and failure strain between uncoated and coated fibers (average increment in fiber diameter of ∼221 nm due to coating) at 5% significance level. SEM images of failure surfaces for uncoated and coated fibers also confirmed a tensile failure of fibers as observed for polyacrylonitrile PAN-based fibers in literature.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1007/s11340-017-0335-6