Hierarchically porous electrodes made of electrochemically active materials and conductive additives may display synergistic effects originating from the interactions between the constituent phases, and this approach has been adopted for optimizing the performances of many electrode materials. Here we report our findings in design, fabrication, and characterization of a hierarchically porous hybrid electrode composed of α-NiS nanorods decorated on reduced graphene oxide (rGO) (denoted as R-NiS/rGO), derived from water-refluxed metal–organic frameworks/rGO (Ni-MOF-74/rGO) templates. Microanalyses reveal that the as-synthesized α-NiS nanorods have abundant (101) and (110) surfaces on the edges, which exhibit a strong affinity for OH − in KOH electrolyte, as confirmed by density functional theory-based calculations. The results suggest that the MOF-derived α-NiS nanorods with highly exposed active surfaces are favorable for fast redox reactions in a basic electrolyte. Besides, the presence of rGO in the hybrid electrode greatly enhances the electronic conductivity, providing efficient current collection for fast energy storage. Indeed, when tested in a supercapacitor with a three-electrode configuration in 2 M KOH electrolyte, the R-NiS/rGO hybrid electrode exhibits a capacity of 744 C g −1 at 1 A g −1 and 600 C g −1 at 50 A g −1 , indicating remarkable rate performance, while maintaining more than 89% of the initial capacity after 20 000 cycles. Moreover, when coupled with a nitrogen-doped graphene aerogel (C/NG-A) negative electrode, the hybrid supercapacitor (R-NiS/rGO/electrolyte/C/NG-A) achieved an ultra-high energy density of 93 W h kg −1 at a power density of 962 W kg −1 , while still retaining an energy density of 54 W h kg −1 at an elevated working power of 46 034 W kg −1 .
more »
« less
Rational Design of Nickel Hydroxide‐Based Nanocrystals on Graphene for Ultrafast Energy Storage
Abstract Compact, light, and powerful energy storage devices are urgently needed for many emerging applications; however, the development of advanced power sources relies heavily on advances in materials innovation. Here, the findings in rational design, one‐pot synthesis, and characterization of a series of Ni hydroxide‐based electrode materials in alkaline media for fast energy storage are reported. Under the guidance of density functional theory calculations and experimental investigations, a composite electrode composed of Co‐/Mn‐substituted Ni hydroxides grown on reduced graphene oxide (rGO) is designed and prepared, demonstrating capacities of 665 and 427 C g−1at current densities of 2 and 20 A g−1, respectively. The superior performance is attributed mainly to the low deprotonation energy and the facile electron transport, as elaborated by theoretical calculations. When coupled with an electrode based on organic molecular‐modified rGO, the resulting hybrid device demonstrates an energy density of 74.7 W h kg−1at a power density of 1.68 kW kg−1while maintaining capacity retention of 91% after 10,000 cycles (20 A g−1). The findings not only provide a promising electrode material for high‐performance hybrid capacitors but also open a new avenue toward knowledge‐based design of efficient electrode materials for other energy storage applications.
more »
« less
- Award ID(s):
- 1742828
- PAR ID:
- 10048310
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Energy Materials
- Volume:
- 8
- Issue:
- 9
- ISSN:
- 1614-6832
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Supercapacitors and batteries are essential for sustainable energy development. However, the bottleneck is the associated high cost, which limits bulk use of batteries and supercapacitors. In this context, realizing that the cost of energy‐storage device mainly depends on materials, synthesis processes/procedures, and device fabrication, an effort is made to rationally design and develop novel low‐cost electrode materials with enhanced electrochemical performance in asymmetric supercapacitors. Herein, surface functionalization approach is adopted to design low‐cost 3D mesoporous and nanostructured nickel–nickel oxide electrode materials using facile synthesis for application in supercapacitors. It is demonstrated that the 3D mesoporous Ni provides the high surface area and enhanced ionic conductivity, while germanium functionalization improves the electrical conductivity and reduces the charge‐transfer resistance of NiO. Surface functionalization with Ge demonstrates the significant improvement in specific capacitance of NiO. The asymmetric supercapacitor using these Ge‐functionalized NiO–Ni electrodes provides a specific capacitance of 304 Fg−1(94 mF cm−2), energy density of 23.8 Wh kg−1(7.35 μWh cm−2), and power density of 6.8 kW kg−1(2.1 mW cm−2) with excellent cyclic stability of 92% after 10 000 cycles. To validate their practical applications, powering the digital watch using the asymmetric supercapacitors in laboratory conditions is demonstrated.more » « less
-
Abstract Organic materials with redox‐active oxygen functional groups are of great interest as electrode materials for alkali‐ion storage due to their earth‐abundant constituents, structural tunability, and enhanced energy storage properties. Herein, a hybrid carbon framework consisting of reduced graphene oxide and oxygen functionalized carbon quantum dots (CQDs) is developed via the one‐pot solvothermal reduction method, and a systematic study is undertaken to investigate its redox mechanism and electrochemical properties with Li‐, Na‐, and K‐ions. Due to the incorporation of CQDs, the hybrid cathode delivers consistent improvements in charge storage performance for the alkali‐ions and impressive reversible capacity (257 mAh g−1at 50 mA g−1), rate capability (111 mAh g−1at 1 A g−1), and cycling stability (79% retention after 10 000 cycles) with Li‐ion. Furthermore, density functional theory calculations uncover the CQD structure‐electrochemical reactivity trends for different alkali‐ion. The results provide important insights into adopting CQD species for optimal alkali‐ion storage.more » « less
-
The realization of biomass‐derived supercapacitors of high performance is of practical importance for the manufacturing of supercapacitors from green and renewable sources. Herein, the feasibility of constructing high‐performance supercapacitors from potato‐derived activated carbon (AC) is demonstrated. The potato‐derived AC is produced from potato mash through hydrothermal treatment and high‐temperature activation with KOH as agent. The supercapacitors with aqueous electrolyte of 6 mKOH and a mass loading of 5 mg per electrode achieve a specific gravimetric capacitance of 333.7 F g−1per electrode and a specific energy of 11.75 W h g−1at a specific power of 197.6 W kg−1at a current density of 0.4 A g−1under a nominal compressive stress of 7.96 MPa. The supercapacitors with a mass loading of 10 mg per electrode achieve the maximum specific gravimetric capacitance of 340.6 F g−1and a specific energy of 11.75 W h g−1at a specific power of 194.2 W kg−1at a current density of 0.4 A g−1under a nominal compressive stress of 7.96 MPa. Increasing the compaction of electrode materials under compressive stress has the potential to increase the electrochemical performance of supercapacitors.more » « less
-
Abstract The growing demand for bioelectronics has generated widespread interest in implantable energy storage. These implantable bioelectronic devices, powered by a complementary battery/capacitor system, have faced difficulty in miniaturization without compromising their functionality. This paper reports on the development of a promising high‐rate cathode material for implantable power sources based on Li‐exchanged Na1.5VOPO4F0.5anchored on reduced graphene oxide (LNVOPF‐rGO). LNVOPF is unique in that it offers dual charge storage mechanisms, which enable it to exhibit mixed battery/capacitor electrochemical behavior. In this work, electrochemical Li‐ion exchange of the LNVOPF structure is characterized by operando X‐ray diffraction. Through designed nanostructuring, the charge storage kinetics of LNVOPF are improved, as reflected in the stored capacity of 107 mAh g−1at 20C. A practical full cell device composed of LNVOPF and T‐Nb2O5, which serves as a pseudocapacitive anode, is fabricated to demonstrate not only high energy/power density storage (100 Wh kg−1at 4000 W kg−1) but also reliable pulse capability and biocompatibility, a desirable combination for applications in biostimulating devices. This work underscores the potential of miniaturizing biomedical devices by replacing a conventional battery/capacitor couple with a single power source.more » « less