Stimuli responsive hydrogels that can change shape in response to applied external stimuli are appealing for soft robotics, biomedical devices, drug delivery, and actuators. However, existing 3D printed shape morphing materials are non‐biodegradable, which limits their use in biomedical applications. Here, 3D printed protein‐based hydrogels are developed and applied for programmable structural changes under the action of temperature, pH, or an enzyme. Key to the success of this strategy is the use of methacrylated bovine serum albumin (MA–BSA) as a biodegradable building block to Pickering emulsion gels in the presence of
We describe the synthesis, characterization and direct‐write 3D printing of triblock copolymer hydrogels that have a tunable response to temperature and shear stress. In aqueous solutions, these polymers utilize the temperature‐dependent self‐association of poly(alkyl glycidyl ether) ‘A’ blocks and a central poly(ethylene oxide) segment to create a physically crosslinked three‐dimensional network. The temperature response of these hydrogels was dependent upon composition, chain length and concentration of the ‘A’ block in the copolymer. Rheological experiments confirmed the existence of sol–gel transitions and the shear‐thinning behavior of the hydrogels. The temperature‐ and shear‐responsive properties enabled direct‐write 3D printing of complex objects with high fidelity. Hydrogel cytocompatibility was also confirmed by incorporating HeLa cells into select hydrogels resulting in high viabilities over 24 h. The tunable temperature response and innate shear‐thinning properties of these hydrogels, coupled with encouraging cell viability results, present an attractive opportunity for additive manufacturing and tissue engineering applications. © 2018 Society of Chemical Industry
more » « less- NSF-PAR ID:
- 10078511
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Polymer International
- Volume:
- 68
- Issue:
- 7
- ISSN:
- 0959-8103
- Page Range / eLocation ID:
- p. 1238-1246
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
4D Printing of Multi‐Stimuli Responsive Protein‐Based Hydrogels for Autonomous Shape Transformationsmore » « less
Abstract N ‐isopropylacrylamide or 2‐dimethylaminoethyl methacrylate. These shear‐thinning gels are ideal for direct ink write (DIW) 3D printing of multi‐layered stimuli‐responsive hydrogels. While poly(N ‐isopropylacrylamide) and poly(dimethylaminoethyl methacrylate) introduce temperature and pH‐responsive properties into the printed objects, a unique feature of this strategy is an enzyme‐triggered shape transformation based on the degradation of the bovine serum albumin network. To highlight this technique, protein‐based hydrogels that reversibly change shape based on environmental temperature and pH are fabricated, and irreversibly altered by enzymatic degradation, which demonstrates the complexity that can be introduced into 4D printed systems. -
Herein, we describe a method to produce yeast-laden hydrogel inks for the direct-write 3D printing of cuboidal lattices for immobilized whole-cell catalysis. A poly(alkyl glycidyl ether)-based triblock copolymer was designed to have three important features for this application: (1) a temperature response, which allowed for facile processing of the material; (2) a shear response, which facilitated the extrusion of the material through a nozzle; and (3) UV light induced polymerization, which enabled the post-extrusion chemical crosslinking of network chains, and the fabrication of robust printed objects. These three key stimuli responses were confirmed via rheometrical characterization. A genetically-engineered yeast strain with an upregulated α-factor production pathway was incorporated into the hydrogel ink and 3D printed. The immobilized yeast cells exhibited adequate viability of 87.5% within the hydrogel. The production of the upregulated α-factor was detected using a detecting yeast strain and quantified at 268 nM ( s = 34.6 nM) over 72 h. The reusability of these bioreactors was demonstrated via immersion of the yeast-laden hydrogel lattice in fresh SC media and confirmed by the detection of similar amounts of upregulated α-factor at 259 nM ( s = 45.1 nM). These yeast-laden materials represent an attractive opportunity for whole-cell catalysis of other high-value products in a sustainable and continuous manner.more » « less
-
null (Ed.)Three-dimensional (3D) printing allows for creation of patient-specific implants. However, development of new synthetic materials for 3D printing has been relatively slow with only a few polymers available for tissue engineering applications. Most of these polymers require harsh processing conditions like high temperatures and pressures or are mixed with a combination of leachable additives like plasticizers, initiators, crosslinkers, and solvents to enable 3D printing. Therefore, to propel the development of new polymers for ambient temperature, additive-free 3D printing it is necessary to systematically understand the relationship between the structure of a polymer with its 3D printability. Herein, three homopolyesters were synthesized, each with a common backbone but differing in the length of their saturated, aliphatic pendant chains with 2, 6, or 15 carbons. The physical properties such as the glass transition temperature ( T g ) and the rheological properties like shear thinning, temperature response, and stress relaxation were correlated to the individual polymer's 3D printability. The 3D printability of the polymers was assessed based on four criteria: ability to be extruded as continuous filaments, shape fidelity, the retention of printed shape, and the ability to form free hanging filaments. We observed that the polymers with longer side chains can be extruded at low temperature and pressure because the long side chains act as internal diluents and increase the flowability of the polymer. However, their ability to retain the 3D printed shape is adversely affected by the increase in side chain length, unless the side chains form ordered structures leading to immediate recovery of viscosity. The insight derived from the systematic investigation of the effect of polymer structure on their rheology and 3D printability can be used to rationally design other polymers for extrusion-based direct-write 3D printing.more » « less
-
more » « less
Abstract The fabrication of three‐dimensional (3D) scaffolds is indispensable to tissue engineering and 3D printing is emerging as an important approach towards this. Hydrogels are often used as inks in extrusion‐based 3D printing, including with encapsulated cells; however, numerous challenging requirements exist, including appropriate viscosity, the ability to stabilize after extrusion, and cytocompatibility. Here, we present a shear‐thinning and self‐healing hydrogel crosslinked through dynamic covalent chemistry for 3D bioprinting. Specifically, hyaluronic acid was modified with either hydrazide or aldehyde groups and mixed to form hydrogels containing a dynamic hydrazone bond. Due to their shear‐thinning and self‐healing properties, the hydrogels could be extruded for 3D printing of structures with high shape fidelity, stability to relaxation, and cytocompatibility with encapsulated fibroblasts (>80% viability). Forces for extrusion and filament sizes were dependent on parameters such as material concentration and needle gauge. To increase scaffold functionality, a second photocrosslinkable interpenetrating network was included that was used for orthogonal photostiffening and photopatterning through a thiol‐ene reaction. Photostiffening increased the scaffold's modulus (∼300%) while significantly decreasing erosion (∼70%), whereas photopatterning allowed for spatial modification of scaffolds with dyes. Overall, this work introduces a simple approach to both fabricate and modify 3D printed scaffolds. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 865–875, 2018.
-
more » « less
Abstract Shear‐recoverable hydrogels based on block copolypeptides with rapid self‐recovery hold potential in extrudable and injectable 3D‐printing applications. In this work, a series of 3‐arm star‐shaped block copolypeptides composed of an inner hydrophilic poly(
l ‐glutamate) domain and an outer β‐sheet forming domain is synthesized with varying side chains and block lengths. By changing the β‐sheet forming domains, hydrogels with diverse microstructures and mechanical properties are prepared and structure–function relationships are determined using scattering and rheological techniques. Differences in the properties of these materials are amplified during direct‐ink writing with a strong correlation observed between printability and material chemistry. Significantly, it is observed that non‐canonical β‐sheet blocks based on phenyl glycine form more stable networks with superior mechanical properties and writability compared to widely used natural amino acid counterparts. The versatile design available through block copolypeptide materials provides a robust platform to access tunable material properties based solely on molecular design. These systems can be exploited in extrusion‐based applications such as 3D‐printing without the need for additives.