Scalable substitutional doping of 2D transition metal dichalcogenides is a prerequisite to developing next‐generation logic and memory devices based on 2D materials. To date, doping efforts are still nascent. Here, scalable growth and vanadium (V) doping of 2D WSe2at front‐end‐of‐line and back‐end‐of‐line compatible temperatures of 800 and 400 °C, respectively, is reported. A combination of experimental and theoretical studies confirm that vanadium atoms substitutionally replace tungsten in WSe2, which results in
Post‐synthesis doping of 2D materials is demonstrated by incorporation of vapor‐deposited transition metals into a MoTe2lattice. Using this approach, vanadium doping of 2H‐MoTe2produces a 2D ferromagnetic semiconductor with a Curie temperature above room temperature (RT). Surprisingly, ferromagnetic properties can be induced with very low vanadium concentrations, down to ≈0.2%. The vanadium species introduced at RT are metastable, and annealing to above ≈500 K results in the formation of a thermodynamically favored impurity configuration that, however, exhibits reduced ferromagnetic properties. Doping with titanium, instead of vanadium, shows a similar incorporation behavior, but no ferromagnetism is induced in MoTe2. This indicates that the type of impurities in addition to their atomic configuration is responsible for the induced magnetism. The interpretation of the experimental results is consistent with ab initio calculations, which confirm that the proposed vanadium impurity configurations exhibit magnetic moments, in contrast to the same configurations with titanium impurities. This study illustrates the possibility to induce ferromagnetic properties in layered van der Waals semiconductors by controlled magnetic impurity doping and thus to add magnetic functionalities to 2D materials.
more » « less- NSF-PAR ID:
- 10461642
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- Volume:
- 5
- Issue:
- 5
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract p ‐type doping via the introduction of discrete defect levels that lie close to the valence band maxima. Thep ‐type nature of the V dopants is further verified by constructed field‐effect transistors, where hole conduction becomes dominant with increasing vanadium concentration. Hence, this study presents a method to precisely control the density of intentionally introduced impurities, which is indispensable in the production of electronic‐grade wafer‐scale extrinsic 2D semiconductors. -
more » « less
Abstract Dilute magnetic semiconductors (DMS), achieved through substitutional doping of spin‐polarized transition metals into semiconducting systems, enable experimental modulation of spin dynamics in ways that hold great promise for novel magneto–electric or magneto–optical devices, especially for two‐dimensional (2D) systems such as transition metal dichalcogenides that accentuate interactions and activate valley degrees of freedom. Practical applications of 2D magnetism will likely require room‐temperature operation, air stability, and (for magnetic semiconductors) the ability to achieve optimal doping levels without dopant aggregation. Here, room‐temperature ferromagnetic order obtained in semiconducting vanadium‐doped tungsten disulfide monolayers produced by a reliable single‐step film sulfidation method across an exceptionally wide range of vanadium concentrations, up to 12 at% with minimal dopant aggregation, is described. These monolayers develop p‐type transport as a function of vanadium incorporation and rapidly reach ambipolarity. Ferromagnetism peaks at an intermediate vanadium concentration of ~2 at% and decreases for higher concentrations, which is consistent with quenching due to orbital hybridization at closer vanadium–vanadium spacings, as supported by transmission electron microscopy, magnetometry, and first‐principles calculations. Room‐temperature 2D‐DMS provide a new component to expand the functional scope of van der Waals heterostructures and bring semiconducting magnetic 2D heterostructures into the realm of practical application.
-
more » « less
Abstract The ability to control the density and spatial distribution of substitutional dopants in semiconductors is crucial for achieving desired physicochemical properties. Substitutional doping with adjustable doping levels has been previously demonstrated in 2D transition metal dichalcogenides (TMDs); however, the spatial control of dopant distribution remains an open field. In this work, edge termination is demonstrated as an important characteristic of 2D TMD monocrystals that affects the distribution of substitutional dopants. Particularly, in chemical vapor deposition (CVD)‐grown monolayer WS2, it is found that a higher density of transition metal dopants is always incorporated in sulfur‐terminated domains when compared to tungsten‐terminated domains. Two representative examples demonstrate this spatial distribution control, including hexagonal iron‐ and vanadium‐doped WS2monolayers. Density functional theory (DFT) calculations are further performed, indicating that the edge‐dependent dopant distribution is due to a strong binding of tungsten atoms at tungsten‐zigzag edges, resulting in the formation of open sites at sulfur‐zigzag edges that enable preferential dopant incorporation. Based on these results, it is envisioned that edge termination in crystalline TMD monolayers can be utilized as a novel and effective knob for engineering the spatial distribution of substitutional dopants, leading to in‐plane hetero‐/multi‐junctions that display fascinating electronic, optoelectronic, and magnetic properties.
-
more » « less
Abstract Monolayer ternary tellurides based on alloying different transition metal dichalcogenides (TMDs) can result in new two‐dimensional (2D) materials ranging from semiconductors to metals and superconductors with tunable optical and electrical properties. Semiconducting WTe2
x S2(1‐x )monolayer possesses two inequivalent valleys in the Brillouin zone, each valley coupling selectively with circularly polarized light (CPL). The degree of valley polarization (DVP) under the excitation of CPL represents the purity of valley polarized photoluminescence (PL), a critical parameter for opto‐valleytronic applications. Here, new strategies to efficiently tailor the valley‐polarized PL from semiconducting monolayer WTe2x S2(1‐x )at room temperature (RT) through alloying and back‐gating are presented. The DVP at RT is found to increase drastically from < 5% in WS2to 40% in WTe0.12S1.88by Te‐alloying to enhance the spin‐orbit coupling. Further enhancement and control of the DVP from 40% up to 75% is demonstrated by electrostatically doping the monolayer WTe0.12S1.88via metallic 1T′‐WTe2electrodes, where the use of 1T′‐WTe2substantially lowers the Schottky barrier height (SBH) and weakens the Fermi‐level pinning of the electrical contacts. The demonstration of drastically enhanced DVP and electrical tunability in the valley‐polarized emission from 1T′‐WTe2/WTe0.12S1.88heterostructures paves new pathways towards harnessing valley excitons in ultrathin valleytronic devices for RT applications. -
more » « less
Abstract Enhancing electron correlation in a weakly interacting topological system has great potential to promote correlated topological states of matter with extraordinary quantum properties. Here, the enhancement of electron correlation in a prototypical topological metal, namely iridium dioxide (IrO2), via doping with 3d transition metal vanadium is demonstrated. Single‐crystalline vanadium‐doped IrO2nanowires are synthesized through chemical vapor deposition where the nanowire yield and morphology are improved by creating rough surfaces on substrates. Vanadium doping leads to a dramatic decrease in Raman intensity without notable peak broadening, signifying the enhancement of electron correlation. The enhanced electron correlation is further evidenced by transport studies where the electrical resistivity is greatly increased and follows an unusual dependence on the temperature (
T ). The lattice thermal conductivity is suppressed by an order of magnitude via doping even at room temperature where phonon‐impurity scattering becomes less important. Density functional theory calculations suggest that the remarkable reduction of thermal conductivity arises from the complex phonon dispersion and reduced energy gap between phonon branches, which greatly enhances phase space for phonon–phonon Umklapp scattering. This work demonstrates a unique system combining 3d and 5d transition metals in isostructural materials to enrich the system with various types of interactions.