Graphene nanocomposites are a promising class of advanced materials for sensing applications; yet, their commercialization is hindered due to impurity incorporation during fabrication and high costs. The aim of this work is to prepare graphene–polysulfone (G−PSU) and graphene–polyvinylidene fluoride (G−PVDF) nanocomposites that perform as multifunctional sensors and are formed using a one-step, in situ exfoliation process whereby graphite is exfoliated into graphene nanoflakes (GNFs) directly within the polymer. This low-cost method creates a nanocomposite while avoiding impurity exposure since the raw materials used in the in situ shear exfoliation process are graphite and polymers. The morphology, structure, thermal properties, and flexural properties were determined for G−PSU and G−PVDF nanocomposites, as well as the electromechanical sensor capability during cyclic flexural loading, temperature sensor testing while heating and cooling, and electrochemical sensor capability to detect dopamine while sensing data wirelessly. G−PSU and G−PVDF nanocomposites show superior mechanical characteristics (gauge factor around 27 and significantly enhanced modulus), thermal characteristics (stability up to 500 °C and 170 °C for G−PSU and G−PVDF, respectively), electrical characteristics (0.1 S/m and 1 S/m conductivity for G−PSU and G−PVDF, respectively), and distinguished resonant peaks for wireless sensing (~212 MHz and ~429 MHz). These uniquely formed G−PMC nanocomposites are promising candidates as strain sensors for structural health monitoring, as temperature sensors for use in automobiles and aerospace applications, and as electrochemical sensors for health care and disease diagnostics.
- Award ID(s):
- 1825254
- PAR ID:
- 10114061
- Date Published:
- Journal Name:
- Advances in Materials Science and Engineering
- Volume:
- 2019
- ISSN:
- 1687-8434
- Page Range / eLocation ID:
- 1 to 8
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
null (Ed.)Abstract This paper presents research results of biocidal effect of thermoplastic- polyester-elastomer (TPE-E) with incorporation of hybrid Ag/ZnO/SiO 2 NPs (silver/Zinc oxide/SiO 2 nanoparticles). These results were compared with various gamma-irradiated doses and processing techniques including extrusion, injection molding and compression molding. In all these processing techniques the TPE-E was mixed with mineral oil and Ag/ZnO/SiO 2 nanoparticles. The TPE-E nanocomposites were characterized by differential scanning calorimetry (DSC), thermogravimetry analysis (TGA), Infrared FT spectroscopy (FTIR), surface enhanced Raman technique ( SERS), FESEM (Field emission scanning electron microscopy), Energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), TEM (transmission electronic microscopy) and antimicrobial test. Antibacterial activity against E. coli and S. aureus , are reported and these results showed potential application in health care products.more » « less
-
Bismuth ferrite (BiFeO 3 ) nanocomposites were synthesized using a novel nano-agitator bead milling method followed by calcination. Bismuth oxide and iron oxide nanoparticles were mixed in a stoichiometric ratio and milled for 3 h and calcined at 650 °C in air. X-ray diffraction with Rietveld refinement, scanning electron microscopy, and transmission electron microscopy techniques were used to elucidate the structure of BiFeO 3 . The particle diameter was found to be ∼17 nm. Magnetic and electrical measurements were performed, and these results were compared with those of similar methods. Mostly, BiFeO 3 was obtained with minor secondary phase formation. The resulting powder was weakly ferromagnetic with a remnant magnetization of 0.078 emu/g. This can be attributed to residual strain and defects introduced during the milling process. Electrical testing revealed a high leakage current density that is typical of undoped bismuth ferrite.more » « less
-
Nanoporous bimetallic Fe–Ag nanoparticles (NPs) were synthesized using a facile chemical reduction method and used to decorate the surface of multi-walled carbon nanotubes (MWCNTs) for hydrogen sorption and storage. The effect of TiO 2 nanoparticles on the hydrogen storage properties of Fe–Ag/CNTs was further studied in detail. For this purpose, several nanocomposites of nanoporous bimetallic Fe–Ag/TiO 2 nanoparticles with different amounts of bimetallic Fe–Ag NPs were prepared via a hydrothermal method. The hydrogen storage capacity of the as-prepared nanocomposites was studied using electrochemical methods. The Fe–Ag/TiO 2 /CNT nanocomposite with 0.04 M bimetallic Fe–Ag NPs showed the highest capacity for hydrogen storage, which was ∼5× higher than that of pristine MWCNTs. The maximum discharge capacity was 2931 mA h g −1 , corresponding to a 10.94 wt% hydrogen storage capacity. Furthermore, a 379% increase in discharge capacity was measured after 20 cycles. These results show that Fe–Ag/TiO 2 /CNT electrodes display superior cycling stability and high reversible capacity, which is attractive for battery applications.more » « less
-
more » « less
ABSTRACT Cellulose nanocrystal (CNCs)‐reinforced poly(lactic acid) (PLA) nanocomposites were prepared using twin screw extrusion followed by injection molding. Masterbatch approach was used to achieve more efficient dispersion of CNCs in PLA matrix. Modified CNCs (b‐CNCs) were prepared using benzoic acid as a nontoxic material through a green esterification method in a solvent‐free technique. Transmission electron microscopy images did not exhibit significant differences in the structure of b‐CNCs as compared with unmodified CNCs. However, a reduction of 6.6–15.5% in the aspect ratio of b‐CNCs was observed. The fracture surface of PLA‐b‐CNCs nanocomposites exhibited rough and irregular pattern which confirmed the need of more energy for fracture. Pristine CNCs showed a decrease in the thermal stability of nanocomposites, however, b‐CNCs nanocomposites exhibited higher thermal stability than pure PLA. The average storage modulus was improved by 38 and 48% by addition of CNCs and b‐CNCs in PLA, respectively. The incorporation of b‐CNCs increased Young's modulus, ultimate tensile stress, elongation at break, and impact strength by 27.02, 10.90, 4.20, and 32.77%, respectively, however, CNCs nanocomposites exhibited a slight decrease in ultimate strength and elongation at break. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci.
2018 ,135 , 46468.