skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Local lattice distortions and dynamics in extremely overdoped superconducting YSr 2 Cu 2.75 Mo 0.25 O 7.54
A common characteristic of many “overdoped” cuprates prepared with high-pressure oxygen isTcvalues ≥ 50 K that often exceed that of optimally doped parent compounds, despite O stoichiometries that place the materials at the edge or outside of the conventional boundary between superconducting and normal Fermi liquid states. X-ray absorption fine-structure (XAFS) measurements at 52 K on samples of high-pressure oxygen (HPO) YSr2Cu2.75Mo0.25O7.54,Tc= 84 K show that the Mo is in the (VI) valence in an unusually undistorted octahedral geometry with predominantly Mo neighbors that is consistent with its assigned substitution for Cu in the chain sites of the structure. Perturbations of the Cu environments are minimal, although the Cu X-ray absorption near-edge structure (XANES) differs from that in other cuprates. The primary deviation from the crystal structure is therefore nanophase separation into Mo- and Cu-enriched domains. There are, however, indications that the dynamical attributes of the structure are altered relative to YBa2Cu3O7, including a shift of the Cu-apical O two-site distribution from the chain to the plane Cu sites. Another effect that would influenceTcis the possibility of multiple bands at the Fermi surface caused by the presence of the second phase and the lowering of the Fermi level.  more » « less
Award ID(s):
1928874
PAR ID:
10135230
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ; ; ;
Publisher / Repository:
Proceedings of the National Academy of Sciences
Date Published:
Journal Name:
Proceedings of the National Academy of Sciences
Volume:
117
Issue:
9
ISSN:
0027-8424
Page Range / eLocation ID:
p. 4559-4564
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; ; et al (, Proceedings of the National Academy of Sciences)
    null (Ed.)
    A crucial issue in cuprates is the extent and mechanism of the coupling of the lattice to the electrons and the superconductivity. Here we report Cu K edge extended X-ray absorption fine structure measurements elucidating the internal quantum tunneling polaron (iqtp) component of the dynamical structure in two heavily overdoped superconducting cuprate compounds, tetragonal YSr 2 Cu 2.75 Mo 0.25 O 7.54 with superconducting critical temperature, T c = 84 K and hole density p = 0.3 to 0.5 per planar Cu, and the tetragonal phase of Sr 2 CuO 3.3 with T c = 95 K and p = 0.6. In YSr 2 Cu 2.75 Mo 0.25 O 7.54 changes in the Cu-apical O two-site distribution reflect a sequential renormalization of the double-well potential of this site beginning at T c , with the energy difference between the two minima increasing by ∼6 meV between T c and 52 K. Sr 2 CuO 3.3 undergoes a radically larger transformation at T c , >1-Å displacements of the apical O atoms. The principal feature of the dynamical structure underlying these transformations is the strongly anharmonic oscillation of the apical O atoms in a double-well potential that results in the observation of two distinct O sites whose Cu–O distances indicate different bonding modes and valence-charge distributions. The coupling of the superconductivity to the iqtp that originates in this nonadiabatic coupling between the electrons and lattice demonstrates an important role for the dynamical structure whereby pairing occurs even in a system where displacements of the atoms that are part of the transition are sufficiently large to alter the Fermi surface. The synchronization and dynamic coherence of the iqtps resulting from the strong interactions within a crystal would be expected to influence this process. 
    more » « less
  2. ; ; ; ; ; ; ; (, Proceedings of the National Academy of Sciences)
    The local structure of the highly “overdoped” 95 K superconductor Sr2CuO3.3determined by Cu K X-ray absorption fine structure (XAFS) at 62 K in magnetically oriented samples shows that 1) the magnetization is perpendicular to thecaxis; 2) at these levels of precision the Cu sublattice is tetragonal in agreement with the crystal structure; the O sublattice has 3) continuous -Cu-O- chains that orient perpendicular to an applied magnetic field; 4) approximately half-filled -Cu-O- chains that orient parallel to this field; 5) a substantial number of apical O vacancies; 6) O ions at some apical positions with expanded Cu-O distances; and 7) interstitial positions that imply highly displaced Sr ions. These results contradict the universally accepted features of cuprates that require intact CuO2planes, magnetization along thecaxis, and a termination of the superconductivity when the excess charge on the CuO2Cu ions exceeds 0.27. These radical differences in charge and structure demonstrate that this compound constitutes a separate class of Cu-O–based superconductors in which the superconductivity originates in a different, more complicated structural unit than CuO2planes while retaining exceptionally high transition temperatures. 
    more » « less
  3. ; ; ; (, Advanced Electronic Materials)
    Abstract The highest ambient‐pressure Tc among binary compounds is 40 K (MgB2). Higher Tc is achieved in high‐pressure hydrides or multielement cuprates. Alternatively, are explored superconducting properties of binary, metastable sub‐oxides, that may emerge under extremely low oxygen partial pressure. The emphasis is on the rock‐salt structure, which is known to promote superconductivity, and exploring AlO, ScO, TiO, and NbO. Dynamic lattice stability is achieved by introducing metal and oxygen vacancies in the fashion of Nb1−xO1−x‐type structure (x = ¼). The electron‐phonon (e‐ph) coupling is remarkably large in Al1−xO1−xand Ti1−xO1−x(λ ≈ 2 at x = ¼), with Tc ≈ 35 K according to the Allen–Dynes equation. Significantly, the coupling strength is comparable to that in high‐pressure hydrides, yet, in contrast to hydrides and MgB2, the coupling is largely driven by low frequency phonons. Sc1−xO1−xand Nb1−xO1−xshow significantly smaller λ and Tc. Further, hydrogen intercalation to boost λ and Tc is investigated. Only Ti1−x(O1−xHx) and Nb1−x(O1−xHx) are dynamically stable upon intercalation, where H, respectively, decreases and increases Tc. The effect of H doping on electronic structure and Tc is discussed. Altogether, the study suggests that metal sub‐oxides are promising compounds to achieve strong e‐ph coupling at ambient pressure. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, Inorganic Chemistry)
    Polycrystalline LiMo8O10 was prepared in a sealed Mo crucible at 1380 °C for 48 h using the conventional high-temperature solid-state method. The polar tetragonal crystal structure (space group I41md) is confirmed based on the Rietveld refinement of powder neutron diffraction and 7Li/6Li solid-state NMR. The crystal structure features infinite chains of Mo4O5 (i.e., Mo2Mo4/2O6/2O6/3) as a repeat unit containing edge-sharing Mo6 octahedra with strong Mo–Mo metal bonding along the chain. X-ray absorption near-edge spectroscopy of the Mo-L3 edge is consistent with the formal Mo valence/configuration. Magnetic measurements reveal that LiMo8O10 is paramagnetic down to 1.8 K. Temperature-dependent resistivity [ρ(T)] measurement indicates a semiconducting behavior that can be fitted with Mott’s variable range hopping conduction mechanism in the temperature range of 215 and 45 K. The ρ(T) curve exhibits an exponential increase below 5 K with a large ratio of ρ1.8/ρ300 = 435. LiMo8O10 shows a negative field-dependent magnetoresistance between 2 and 25 K. Heat capacity measurement fitted with the modified Debye model yields the Debye temperature of 365 K. 
    more » « less
  5. ; ; ; ; ; ; ; ; (, Advanced Materials Interfaces)
    Abstract Control of surface functionalization of MXenes holds great potential, and in particular, may lead to tuning of magnetic and electronic order in the recently reported magnetic Cr2TiC2Tx. Here, vacuum annealing experiments of Cr2TiC2Txare reported with in situ electron energy loss spectroscopy and novel in situ Cr K‐edge extended energy loss fine structure analysis, which directly tracks the evolution of the MXene surface coordination environment. These in situ probes are accompanied by benchmarking synchrotron X‐ray absorption fine structure measurements and density functional theory calculations. With the etching method used here, the MXene has an initial termination chemistry of Cr2TiC2O1.3F0.8. Annealing to 600 °C results in the complete loss of F, but O termination is thermally stable up to (at least) 700 °C. These findings demonstrate thermal control of F termination in Cr2TiC2Txand offer a first step toward termination engineering this MXene for magnetic applications. Moreover, this work demonstrates high energy electron spectroscopy as a powerful approach for surface characterization in 2D materials. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email