In this work, the structural and electrical properties of metalorganic chemical vapor deposited Si-doped β-(Al x Ga 1−x ) 2 O 3 thin films grown on (010) β-Ga 2 O 3 substrates are investigated as a function of Al composition. The room temperature Hall mobility of 101 cm 2 /V s and low temperature peak mobility (T = 65 K) of 1157 cm 2 /V s at carrier concentrations of 6.56 × 10 17 and 2.30 × 10 17 cm −3 are measured from 6% Al composition samples, respectively. The quantitative secondary ion mass spectroscopy (SIMS) characterization reveals a strong dependence of Si and other unintentional impurities, such as C, H, and Cl concentrations in β-(Al x Ga 1−x ) 2 O 3 thin films, with different Al compositions. Higher Al compositions in β-(Al x Ga 1−x ) 2 O 3 result in lower net carrier concentrations due to the reduction of Si incorporation efficiency and the increase of C and H impurity levels that act as compensating acceptors in β-(Al x Ga 1−x ) 2 O 3 films. Lowering the growth chamber pressure reduces Si concentrations in β-(Al x Ga 1−x ) 2 O 3 films due to the increase of Al compositions as evidenced by comprehensive SIMS and Hall characterizations. Due to the increase of lattice mismatch between the epifilm and substrate, higher Al compositions lead to cracking in β-(Al x Ga 1−x ) 2 O 3 films grown on β-Ga 2 O 3 substrates. The (100) cleavage plane is identified as a major cracking plane limiting the growth of high-quality Si-doped (010) β-(Al x Ga 1−x ) 2 O 3 films beyond the critical thicknesses, which leads to highly anisotropic and inhomogeneous behaviors in terms of conductivity.
more »
« less
Probing Charge Transport and Background Doping in Metal‐Organic Chemical Vapor Deposition‐Grown (010) β‐Ga 2 O 3
A new record‐high room‐temperature electron Hall mobility (
- Award ID(s):
- 1810041
- NSF-PAR ID:
- 10159699
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- physica status solidi (RRL) – Rapid Research Letters
- Volume:
- 14
- Issue:
- 8
- ISSN:
- 1862-6254
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Metalorganic chemical vapor deposition (MOCVD) growths of β-Ga 2 O 3 on on-axis (100) Ga 2 O 3 substrates are comprehensively investigated. Key MOCVD growth parameters including growth temperature, pressure, group VI/III molar flow rate ratio, and carrier gas flow rate are mapped. The dependence of the growth conditions is correlated with surface morphology, growth rate, and electron transport properties of the MOCVD grown (100) β-Ga 2 O 3 thin films. Lower shroud gas (argon) flow is found to enhance the surface smoothness with higher room temperature (RT) electron Hall mobility. The growth rate of the films decreases but with an increase of electron mobility as the VI/III molar flow rate ratio increases. Although no significant variation on the surface morphologies is observed at different growth temperatures, the general trend of electron Hall mobilities are found to increase with increasing growth temperature. The growth rates reduce significantly with uniform surface morphologies as the chamber pressure increases. By tuning the silane flow rate, the controllable carrier concentration of (100) β-Ga 2 O 3 thin films between low-10 17 cm −3 and low-10 18 cm −3 was achieved. Under optimized growth condition, an (100) β-Ga 2 O 3 thin film with RMS roughness value of 1.64 nm and a RT mobility of 24 cm 2 /Vs at a carrier concentration of 7.0 × 10 17 cm −3 are demonstrated. The mobilities are primarily limited by the twin lamellae and stacking faults defects generated from the growth interface. Atomic resolution scanning transmission electron microscopy reveals the formation of twin boundary defects in the films, resulting in the degradation of crystalline quality. Results from this work provide fundamental understanding of the MOCVD epitaxy of (100) β-Ga 2 O 3 on on-axis Ga 2 O 3 substrates and the dependence of the material properties on growth conditions. The limitation of electron transport properties of the (100) β-Ga 2 O 3 thin films below 25 cm 2 /Vs is attributed to the formation of incoherent boundaries (twin lamellae) and stacking faults grown along the on-axis (100) crystal orientation.more » « less
-
more » « less
Gallium oxide (Ga2O3) is a highly promising ultrawide‐bandgap semiconductor for power electronics that emerged about a decade ago. Epitaxial growth Ga2O3at the small scale is demonstrated. In order to develop scalable manufacturing of high‐performance epitaxial structures, in‐depth understanding of the fundamental growth processes, control parameters, and mechanism is imperative. This review discusses the recent progress in epitaxial growth of β‐Ga2O3films and highlights challenges in obtaining high growth rate, low defects, and high carrier mobilities. Compared with the other epitaxy methods, metal–organic chemical vapor deposition (MOCVD) offers a wider growth window and precursor selection option, to minimize the tradeoff between crystal quality and growth rate. Growth rate is inversely proportional to temperature, within a certain temperature window, because of the unavoidable premature gas‐phase reactions and desorption of the highly volatile gallium suboxide (Ga2O) at elevated temperatures. Growth defects, background impurity incorporation, and carrier mobilities can be affected by the choice of MOCVD precursors, nucleation, and adsorption/desorption/diffusion of adatoms on substrate surfaces of different orientations, including the effect of growing on cleavage and noncleavage planes. This review summarizes the current status of the epitaxial growth of β‐Ga2O3and analyzes the major factors that enhance mobility and reduce background doping concentration. The insights gained help advance the manufacturability of device‐grade epitaxial thin films.
-
more » « less
A high figure‐of‐merit UV‐C solar‐blind photodetector (PD) fabricated from thin‐film beta‐gallium oxide (β‐Ga2O3) grown on
n ‐Si substrates by plasma‐assisted molecular beam epitaxy is demonstrated. Film growth sequences for nucleation of Ga2O3on (100)‐ and (111)‐oriented Si substrates are developed, and the influence of crucial growth parameters is systematically investigated, namely, substrate temperature, oxygen flow rate, and plasma power on the functional properties of the PDs. The PDs show an ultra‐high responsivity of 837 A W−1and a fast ON/OFF time below 4 ms at −5 V. In addition, they display strong rectifying properties and a sharp cutoff below 280 nm with the average responsivities between 10 and 80 A W−1, a detectivity on the order of 1010 Jones, and rise/fall times between 4 and 500 ms. High photoconductive gain is likely to be due to the mid‐bandgap donor/acceptor defect levels, including oxygen vacancies in the form of self‐trapped holes. It is demonstrated that these defect levels can be modified by controlling the growth conditions, thereby allowing for tailoring of the PD characteristics for specific applications. The methodology represents a cost‐effective solution over homoepitaxial approaches, with characteristics that meet or exceed those reported previously, offering new possibilities for on‐wafer integration with Si opto‐electronics. -
We report the use of suboxide molecular-beam epitaxy ( S-MBE) to grow β-Ga 2 O 3 at a growth rate of ∼1 µm/h with control of the silicon doping concentration from 5 × 10 16 to 10 19 cm −3 . In S-MBE, pre-oxidized gallium in the form of a molecular beam that is 99.98% Ga 2 O, i.e., gallium suboxide, is supplied. Directly supplying Ga 2 O to the growth surface bypasses the rate-limiting first step of the two-step reaction mechanism involved in the growth of β-Ga 2 O 3 by conventional MBE. As a result, a growth rate of ∼1 µm/h is readily achieved at a relatively low growth temperature ( T sub ≈ 525 °C), resulting in films with high structural perfection and smooth surfaces (rms roughness of <2 nm on ∼1 µm thick films). Silicon-containing oxide sources (SiO and SiO 2 ) producing an SiO suboxide molecular beam are used to dope the β-Ga 2 O 3 layers. Temperature-dependent Hall effect measurements on a 1 µm thick film with a mobile carrier concentration of 2.7 × 10 17 cm −3 reveal a room-temperature mobility of 124 cm 2 V −1 s −1 that increases to 627 cm 2 V −1 s −1 at 76 K; the silicon dopants are found to exhibit an activation energy of 27 meV. We also demonstrate working metal–semiconductor field-effect transistors made from these silicon-doped β-Ga 2 O 3 films grown by S-MBE at growth rates of ∼1 µm/h.more » « less