Full Heusler compounds have long been discovered as exceptional n-type thermoelectric materials. However, no p-type compounds could match the high n-type figure of merit ( ZT ). In this work, based on first-principles transport theory, we predict the unprecedentedly high p-type ZT = 2.2 at 300 K and 5.3 at 800 K in full Heusler CsK 2 Bi and CsK 2 Sb, respectively. By incorporating the higher-order phonon scattering, we find that the high ZT value primarily stems from the ultralow lattice thermal conductivity ( κ L ) of less than 0.2 W mK −1 at room temperature, decreased by 40% compared to the calculation only considering three-phonon scattering. Such ultralow κ L is rooted in the enhanced phonon anharmonicity and scattering channels stemming from the coexistence of antibonding-induced anharmonic rattling of Cs atoms and low-lying optical branches. Moreover, the flat and heavy nature of valence band edges leads to a high Seebeck coefficient and moderate power factor at optimal hole concentration, while the dispersive and light conduction band edges yield much larger electrical conductivity and electronic thermal conductivity ( κ e ), and the predominant role of κ e suppresses the n-type ZT . This study offers a deeper insight into the thermal and electronic transport properties in full Heusler compounds with strong phonon anharmonicity and excellent thermoelectric performance.
more »
« less
Thermoelectric transport of semiconductor full-Heusler VFe 2 Al
The full-Heusler VFe 2 Al has emerged as an important thermoelectric material in its thin film and bulk phases. VFe 2 Al is attractive for use as a thermoelectric materials because of it contains only low-cost, non-toxic and earth abundant elements. While VFe 2 Al has often been described as a semimetal, here we show the electronic and thermal properties of VFe 2 Al can be explained by considering VFe 2 Al as a valence precise semiconductor like many other thermoelectric materials but with a very small band gap ( E g = 0.03 ± 0.01 eV). Using a two-band model for electrical transport and point-defect scattering model for thermal transport we analyze the thermoelectric properties of bulk full-Heusler VFe 2 Al. We demonstrate that a semiconductor transport model can explain the compilation of data from a variety of n and p-type VFe 2 Al compositions assuming a small band-gap between 0.02 eV and 0.04 eV. In this small E g semiconductor understanding, the model suggests that nominally undoped VFe 2 Al samples appear metallic because of intrinsic defects of the order of ∼10 20 defects per cm −3 . We rationalize the observed trends in weighted mobilities ( μ w ) with dopant atoms from a molecular orbital understanding of the electronic structure. We use a phonon-point-defect scattering model to understand the dopant-concentration (and, therefore, the carrier-concentration) dependence of thermal conductivity. The electrical and thermal models developed allow us to predict the zT versus carrier concentration curve for this material, which maps well to reported experimental investigations.
more »
« less
- Award ID(s):
- 1729487
- PAR ID:
- 10195244
- Date Published:
- Journal Name:
- Journal of Materials Chemistry C
- Volume:
- 8
- Issue:
- 30
- ISSN:
- 2050-7526
- Page Range / eLocation ID:
- 10174 to 10184
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Orthorhombic BaZrS 3 is a potential optoelectronic material with prospective applications in photovoltaic and thermoelectric devices. While efforts exist on understanding the effects of elemental substitution and material stability, fundamental knowledge on the electronic transport properties are sparse. We employ first principles calculations to examine the electronic band structure and optical band gap and interrogate the effect of electron transport on electrical and thermal conductivities, and Seebeck coefficient, as a function of temperature and chemical potential. Our results reveal that BaZrS 3 has a band gap of 1.79 eV in proximity of the optimal 1.35 eV recommended for single junction photovoltaics. An absorption coefficient of 3 × 10 5 cm −1 at photon energies of 3 eV is coupled with an early onset to optical absorption at 0.5 eV, significantly below the optical band gap. The carrier effective mass being lower for electrons than holes, we find the Seebeck coefficient to be higher for holes than electrons. A notable (≈1.0 at 300 K) upper limit to the thermoelectric figure of merit, obtained due to high Seebeck coefficient (3000 μV K −1 ) and ultra-low electron thermal conductivity, builds promise for BaZrS 3 as a thermoelectric.more » « less
-
Compositional diversity and intriguing structural features have made Zintl phases excellent candidates as thermoelectric materials. Zintl phase with 21-4-18 composition has shown high thermoelectric performance in the mid- to high-temperature ranges. The complex crystal structure and favorable transport properties of these compounds indicate the potential for high thermoelectric efficiency. Arsenic-based Eu21Zn4As18, belonging to the Ca21Mn4Sb18 structure type, exhibits a semiconductor-like p-type transport behavior and has a calculated band gap of 0.49 eV. The compound is paramagnetic at high temperatures, with an antiferromagnetic transition occurring at T-N = similar to 10 K. The moment obtained from the Curie-Weiss data fit aligns with Eu2+ ions. At the same time, the field-dependent measurement at 2 K indicates complex magnetic ordering with a saturation moment consistent with Eu2+ ions. Pristine Eu21Zn4As18 exhibits an ultralow lattice thermal conductivity of 0.40 W m(-1) K-1 at 873 K. Electronic transport properties measurement shows evidence of bipolar conduction across much of the measured temperature range (450-780 K). However, the Seebeck coefficient remains extremely high (>440 mu V K-1) across this range, indicating the potential for high zT if an appropriate dopant is found. This work represents the first report on the temperature-dependent thermal conductivity, Seebeck coefficient, and thermoelectric efficiency of the arsenic-containing Zintl phase with 21-4-18 composition, showcasing its promise for further optimization of the thermoelectric performance.more » « less
-
The design of high-entropy alloys is effective in lowering thermal conductivity but often reduces carrier mobility, thereby limiting electrical transport properties. Understanding the relationship among configurational entropy, thermal conductivity, and carrier mobility in high-entropy alloys is critical for enhancing thermoelectric performance. We demonstrate that a systematic and substantial increase in configurational entropy in half-Heusler alloys leads to an asymptotic reduction of lattice thermal conductivity. The reduced phonon group velocity and enhanced phonon scattering induced by atomic-scale chemical disorder result in a low lattice thermal conductivity of 2 watts per meter per kelvin at room temperature, with an achievable minimum of about 1.48 watts per meter per kelvin as disorder further increases, approaching the amorphous limit. Single-phase stabilization, along with optimized carrier mobility, is essential to preserve high electrical conductivity. Our results provide fundamental insights into integrating specific strategies with high-entropy design to simultaneously achieve low thermal conductivity and high thermoelectric performance, advantageous for high-temperature thermoelectric power generation applications.more » « less
-
Germanium telluride is a high performing thermoelectric material that additionally serves as a base for alloys such as GeTe–AgSbTe 2 and GeTe–PbTe. Such performance motivates exploration of other GeTe alloys in order understand the impact of site substitution on electron and phonon transport. In this work, we consider the root causes of the high thermoelectric performance material Ge 1− x Mn x Te. Along this alloy line, the crystal structure, electronic band structure, and electron and phonon scattering all depend heavily on the Mn content. Structural analysis of special quasirandom alloy structures indicate the thermodynamic stability of the rock salt phase over the rhombohedral phase with increased Mn incorporation. Effective band structure calculations indicate band convergence, the emergence of new valence band maxima, and strong smearing at the band edge with increased Mn content in both phases. High temperature measurements on bulk polycrystalline samples show a reduction in hole mobility and a dramatic increase in effective mass with respect to increasing Mn content. In contrast, synthesis as a function of tellurium chemical potential does not significantly impact electronic properties. Thermal conductivity shows a minimum near the rhombohedral to cubic phase transition, while the Mn Ge point defect scattering is weak as indicated by the low K L dependence on the Ge–Mn fraction (Fig. 10). From this work, alloys near this phase transition show optimal performance due to low thermal conductivity, moderate effective mass, and low scattering rates compared to Mn-rich compositions.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1039/D0TC02659J