skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Attention:

The NSF Public Access Repository (PAR) system and access will be unavailable from 11:00 PM ET on Thursday, June 12 until 2:00 AM ET on Friday, June 13 due to maintenance. We apologize for the inconvenience.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: High-efficiency blue photoluminescence in the Cs 2 NaInCl 6 :Sb 3+ double perovskite phosphor
In this paper, the photoluminescent properties of a lead-free double perovskite Cs 2 NaInCl 6 doped with Sb 3+ are explored. The host crystal structure is a cubic double perovskite with Fm 3̄ m symmetry, a = 10.53344(4) Å, and rock salt ordering of Na + and In 3+ . It is a wide bandgap compound ( E g ≈ 5.1 eV), and substitution with Sb 3+ leads to strong absorption in the UV due to localized 5s 2 → 5s 1 5p 1 transitions on Sb 3+ centers. Radiative relaxation back to the 5s 2 ground state, via a 3 P 1 → 1 S 0 transition, leads to intense blue luminescence, centered at 445 nm, with a photoluminescent quantum yield of 79%. The Stokes shift of 0.94 eV is roughly 33% smaller than it is in the related vacancy ordered double perovskite Cs 2 SnCl 6 . The reduction in Stokes shift is likely due to a change in coordination number of Sb 3+ from 6-coordinate in Cs 2 NaInCl 6 to 5-coordinate in Cs 2 SnCl 6 . In addition to the high quantum yield, Cs 2 NaInCl 6 :Sb 3+ exhibits excellent air/moisture stability and can be prepared from solution; these characteristics make it a promising blue phosphor for applications involving near-UV excitation.  more » « less
Award ID(s):
1847701 1911311
PAR ID:
10206138
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Journal of Materials Chemistry C
Volume:
8
Issue:
20
ISSN:
2050-7526
Page Range / eLocation ID:
6797 to 6803
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; (, Nanoscale)
    Blue emitting Sn-based lead-free halide perovskite nanocrystals (NCs) are considered to be a promising material in lighting and displays. However, industrialised fabrication of blue-emitting NCs still remains a significant challenge due to the use of toxic solvents and optical instability, not mentioning in large-scale synthesis. In this work, a green-route synthesis of blue-emitting lead-free halide perovskite Cs 2 SnCl 6 powders is developed, in which deionized water with a small amount of inorganic acid is used as the solvent and the synthesis of the Cs 2 SnCl 6 powders is achieved on a microfluidic platform. Using the Cs 2 SnCl 6 powders, we prepare Cs 2 SnCl 6 NCs via an ultrasonication process. Changing the volume ratio of the ligands (oleic acid to oleylamine) can alter the photoluminescence (PL) characteristics of the prepared NCs, including the PL-peak wavelength, PL-peak intensity and quantum yield. The highest photoluminescence quantum yield (PLQY) of 13.4% is achieved by the Cs 2 SnCl 6 NCs prepared with the volume ratio of oleic acid to oleylamine of 40 μL to 10 μL. A long-term PL stability test demonstrates that the as-synthesized Cs 2 SnCl 6 NCs can retain a stable PLQY over a period of 60 days. This work opens up a new path for a large-scale green-route synthesis of blue-emitting Sn-based lead-free NCs, such as Cs 2 SnX 6 (Cl, Br and I), towards their applications in optoelectronics. 
    more » « less
  2. ; ; ; ; ; ; ; (, Journal of Materials Chemistry C)
    Mn2+/Cr3+codoped Cs2AgInCl6double perovskite were synthesizedviaa facile hydrothermal method, which exhibits two photoluminescence bands with a wide emission switch ranging from orange to NIR and the photoluminescence quantum yield of 49.3%. 
    more » « less
  3. ; ; ; ; ; ; (, Inorganic Chemistry Frontiers)
    Broadband near infrared (NIR) emission materials are of interest for various applications including non-destructive biomedical imaging. In this work, ytterbium ions (Yb 3+ ) were successfully doped into Cs 2 AgInCl 6 :Cr 3+ (CAIC:Cr 3+ ) double perovskite single crystals (DPSCs) by a facile hydrothermal method. Under 365 nm excitation, the co-doped CAIC:Cr 3+ ,Yb 3+ DPSCs showed broad NIR emission ranging from 800 to 1400 nm, which spanned the NIR-I (700–900 nm) and NIR-II (1000–1700 nm) bio-windows, with an emission band at 1000 nm and a full-width at half maximum (FWHM) of 188 nm. It is found that Yb 3+ ion doping could effectively improve the photoluminescence (PL) performance of CAIC:Cr 3+ DPSCs. Compared to the photoluminescence quantum yield (PLQY) of 22.5% for the single doped CAIC:Cr 3+ , the co-doped CAIC:Cr 3+ ,Yb 3+ DPSCs show a higher PLQY of ∼45%, which is attributed to the synergistic effect of reduced non-radiative recombination due to defect passivation and increase in crystallinity, and energy transfer (ET) of self-trapped excitons (STEs) to Cr 3+ . As a demonstration of applications, NIR pc-LEDs were fabricated by combining the as-synthesized NIR-emitting phosphor CAIC:Cr 3+ ,Yb 3+ with InGaN UV chips ( λ em = 365 nm) and used to image veins in a palm and for night vision using a NIR camera. The results suggest that the synthesized CAIC:Cr 3+ ,Yb 3+ DPSCs have great potential in biological applications. 
    more » « less
  4. ; ; ; ; ; ; ; ; (, Advanced Functional Materials)
    Abstract All‐inorganic lead halide perovskite nanocrystals (NCs) have great optoelectronic properties with promising applications in light‐emitting diodes (LEDs), lasers, photodetectors, solar cells, and photocatalysis. However, the intrinsic toxicity of Pb and instability of the NCs impede their broad applications. Shell‐coating is an effective method for enhanced environmental stability while reducing toxicity by choosing non‐toxic shell materials such as metal oxides, polymers, silica, etc. However, multiple perovskite NCs can be encapsulated within the shell material and a uniform epitaxial‐type shell growth of well‐isolated NCs is still challenging. In this work, lead‐free vacancy‐ordered double perovskite Cs2SnX6(X = Cl, Br, and I) shells are epitaxially grown on the surface of CsPbX3NCs by a hot‐injection method. The effectiveness of the non‐toxic double perovskite shell protection is demonstrated by the enhanced environmental and phase stability against UV illumination and water. In addition, the photoluminescence quantum yields (PL QYs) increase for the CsPbCl3and CsPbBr3NCs after shelling because of the type I band alignment of the core/shell materials, while enhanced charge transport properties obtained from CsPbI3/Cs2SnI6core/shell NCs are due to the efficient charge separation in the type II core/shell band alignment. 
    more » « less
  5. ; ; ; ; ; (, Chemical Science)
    null (Ed.)
    Non-luminescent, isostructural crystals of [(C 6 H 11 NC) 2 Au](EF 6 )·C 6 H 6 (E = As, Sb) lose benzene upon standing in air to produce green luminescent (E = As) or blue luminescent (E = Sb) powders. Previous studies have shown that the two-coordinate cation, [(C 6 H 11 NC) 2 Au] + , self-associates to form luminescent crystals that contain linear or nearly linear chains of cations and display unusual polymorphic, vapochromic, and/or thermochromic properties. Here, we report the formation of non-luminescent crystalline salts in which individual [(C 6 H 11 NC) 2 Au] + ions are isolated from one another. In [(C 6 H 11 NC) 2 Au](BArF 24 ) ((BArF 24 ) − is tetrakis[3,5-bis(trifluoromethyl)phenyl]borate) each cation is surrounded by two anions that prohibit any close approach of the gold ions. Crystallization of [(C 6 H 11 NC) 2 Au](EF 6 ) (E = As or Sb, but not P) from benzene solution produces colorless, non-emissive crystals of the solvates [(C 6 H 11 NC) 2 Au](EF 6 )·C 6 H 6 . These two solvates are isostructural and contain columns in which cations and benzene molecules alternate. With the benzene molecules separating the cations, the shortest distances between gold ions are 6.936(2) Å for E = As and 6.9717(19) Å for E = Sb. Upon removal from the mother liquor, these crystals crack due to the loss of benzene from the crystal and form luminescent powders. Crystals of [(C 6 H 11 NC) 2 Au](SbF 6 )·C 6 H 6 that powder out form a pale yellow powder with a blue luminescence with emission spectra and powder X-ray diffraction data that show that the previously characterized [(C 6 H 11 NC) 2 Au](SbF 6 ) is formed. In the process, the distances between the gold( i ) ions decrease to ∼3 Å and half of the cyclohexyl groups move from an axial orientation to an equatorial one. Remarkably, when crystals of [(C 6 H 11 NC) 2 Au](AsF 6 )·C 6 H 6 stand in air, they lose benzene and are converted into the yellow, green-luminescent polymorph of [(C 6 H 11 NC) 2 Au](AsF 6 ) rather than the colorless, blue-luminescent polymorph. Paradoxically, the yellow, green-luminescent powder that forms as well as authentic crystals of the yellow, green-luminescent polymorph of [(C 6 H 11 NC) 2 Au](AsF 6 ) are sensitive to benzene vapor and are converted by exposure to benzene vapor into the colorless, blue-luminescent polymorph. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email