Title: Emerging investigator series: 3D printed graphene-biopolymer aerogels for water contaminant removal: a proof of concept
Graphene-based 3D macroscopic aerogels with their hierarchical porous structures and mechanical strength have been widely explored for removing contaminants from water. However, their large-scale manufacturing and application in various water treatment processes are limited by their scalability. In this study, we report a proof-of-concept direct ink writing (DIW) 3D printing technique and subsequent freeze-drying to prepare graphene-biopolymer aerogels for water treatment. To provide appropriate rheology for DIW printability, two bio-inspired polymers, polydopamine (PDA) and bovine serum albumin (BSA), were added to the graphene-based ink. The biopolymers also contributed to the contaminant removal capacity of the resultant graphene-polydopamine-bovine serum albumin (G-PDA-BSA) aerogel. The physicochemical properties of the aerogel were thoroughly characterized from the nano- to macroscale. The 3D printed aerogel exhibited excellent water contaminant removal performance for heavy metals (Cr( vi ), Pb( ii )), organic dyes (cationic methylene blue and anionic Evans blue), and organic solvents ( n -hexane, n -heptane, and toluene) in batch adsorption studies. The electrostatic interaction dominated the removal of heavy metals and dyes while the hydrophobic interaction dominated the removal of organic solvents from water. Moreover, the aerogel showed superb regeneration and reuse potential. The aerogel removed 100% organic solvents over 10 cycles of regeneration and reuse; additionally, the removal efficiencies for methylene blue decreased by 2–20% after the third cycle. The fit-for-design 3D printed aerogel was also effectively used as a bottle-cap flow-through filter for dye removal. The potential and vision of the 3D printing approach for graphene-based water treatment presented here can be extended to other functional nanomaterials, can enable shape-specific applications of fit-for-purpose adsorbents/reactors and point-of-use filters, and can materialize the large-scale manufacturing of nano-enabled water treatment devices and technologies.  more » « less
Award ID(s):
1846863
NSF-PAR ID:
10212238
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
Environmental Science: Nano
ISSN:
2051-8153
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Stimuli responsive hydrogels that can change shape in response to applied external stimuli are appealing for soft robotics, biomedical devices, drug delivery, and actuators. However, existing 3D printed shape morphing materials are non‐biodegradable, which limits their use in biomedical applications. Here, 3D printed protein‐based hydrogels are developed and applied for programmable structural changes under the action of temperature, pH, or an enzyme. Key to the success of this strategy is the use of methacrylated bovine serum albumin (MA–BSA) as a biodegradable building block to Pickering emulsion gels in the presence ofN‐isopropylacrylamide or 2‐dimethylaminoethyl methacrylate. These shear‐thinning gels are ideal for direct ink write (DIW) 3D printing of multi‐layered stimuli‐responsive hydrogels. While poly(N‐isopropylacrylamide) and poly(dimethylaminoethyl methacrylate) introduce temperature and pH‐responsive properties into the printed objects, a unique feature of this strategy is an enzyme‐triggered shape transformation based on the degradation of the bovine serum albumin network. To highlight this technique, protein‐based hydrogels that reversibly change shape based on environmental temperature and pH are fabricated, and irreversibly altered by enzymatic degradation, which demonstrates the complexity that can be introduced into 4D printed systems.

     
    more » « less
  2. Abstract

    Membranes serve as important components for modern manufacturing and purification processes but are conventionally associated with excessive solvent usage. Here, for the first time, a procedure for fabricating large area polysulfone membranes is demonstrated via the combination of direct ink writing (DIW) with non-solvent induced phase inversion (NIPS). The superior control and precision of this process allows for complete utilization of the polymer dope solution during membrane fabrication, thus enabling a significant reduction in material usage. Compared to doctor blade fabrication, a 63% reduction in dope solution volume was achieved using the DIW technique for fabricating similarly sized membranes. Cross flow filtration analysis revealed that, independent of the manufacturing method (DIWvs.doctor blade), the membranes exhibited near identical separation properties. The separation properties were assessed in terms of bovine serum albumin (BSA) rejection and permeances (pressure normalized flux) of pure water and BSA solution. This new manufacturing strategy allows for the reduction of material and solvent usage while providing a large toolkit of tunable parameters which can aid in advancing membrane technology.

     
    more » « less
  3. null (Ed.)
    Conventional approaches to mitigate fouling of membrane surfaces impart hydrophilicity to the membrane surface, which increases the water of hydration and fluidity near the surface. By contrast, we demonstrate here that tuning the membrane surface energy close to that of the dispersive component of water surface tension (21.8 mN m −1 ) can also improve the antifouling properties of the membrane. Specifically, ultrafiltration (UF) membranes were first modified using polydopamine (PDA) followed by grafting of amine-terminated polysiloxane (PSi-NH 2 ). For example, with 2 g L −1 PSi-NH 2 coating solution, the obtained coating layer contains 53% by mass fraction PSi-NH 2 and exhibits a total surface energy of 21 mN m −1 , decreasing the adsorption of bovine serum albumin by 44% compared to the unmodified membrane. When challenged with 1 g L −1 sodium alginate in a constant-flux crossflow system, the PSi-NH 2 -grafted membrane exhibits a 70% lower fouling rate than the pristine membrane at a water flux of 110 L (m 2 h) −1 and good stability when cleaned with NaOH solutions. 
    more » « less
  4. null (Ed.)
    Abstract The conventional manufacturing processes of aerogel insulation material is largely relying on the supercritical drying, which suffers from issues of massive energy consumption, high-cost equipment, and prolonged processing time. With the consideration of large market demand of the aerogel insulation material in the next decade, a low-cost and scalable fabrication technique is highly desired. In this paper, a direct ink writing (DIW) method is used to three-dimensionally fabricate the silica aerogel insulation material, followed by room-temperature and ambient pressure drying. Compared to the supercritical drying and freeze-drying, the reported method significantly reduces the fabrication time and costs. The cost-effective DIW technique offers the capability to print complex hollow internal structures, coupled with the porous structure, is found to be beneficial to the thermal insulation property. The addition of fiber to the ink assures the durability of the fabricated product, without sacrificing the thermal insulation performance. The foam ink preparation methods and the printability are demonstrated in this paper, along with the printing of complex three-dimensional geometries. The thermal insulation performance of the printed objects is characterized, and the mechanical properties are also examined. The proposed approach is found to have 56% reduction in the processing time. The printed silica aerogels exhibit a low thermal conductivity of 0.053 W m−1 K−1. 
    more » « less
  5. Abstract

    4D printing is the 3D printing of objects that change chemically or physically in response to an external stimulus over time. Photothermally responsive shape memory materials are attractive for their ability to undergo remote activation. While photothermal methods using gold nanorods (AuNRs) are used for shape recovery, 3D patterning of these materials into objects with complex geometries using degradable materials is not addressed. Here, the fabrication of 3D printed shape memory bioplastics with photo‐activated shape recovery is reported. Protein‐based nanocomposites based on bovine serum albumin (BSA), poly (ethylene glycol) diacrylate (PEGDA), and AuNRs are developed for vat photopolymerization. These 3D printed bioplastics are mechanically deformed under high loads, and the proteins served as mechano‐active elements that unfolded in an energy‐dissipating mechanism that prevented fracture of the thermoset. The bioplastic object maintained its metastable shape‐programmed state under ambient conditions. Subsequently, up to 99% shape recovery is achieved within 1 min of irradiation with near‐infrared (NIR) light. Mechanical characterization and small angle X‐ray scattering (SAXS) analysis suggest that the proteins mechanically unfold during the shape programming step and may refold during shape recovery. These composites are promising materials for the fabrication of biodegradable shape‐morphing devices for robotics and medicine.

     
    more » « less