Following the success of 3D printing with synthetic polymers like ABS, FLA, Nylon, etc., scientists and researchers have been putting efforts into fabricating bio-compatible materials. It has not only broadened the field of bioengineering and manufacturing but also regenerative medicine. Unlike the traditional 3D printing process, additive bio-manufacturing, also known as 3D bio-printing has a lot of challenges like cell survivability and proliferation, and the mechanical properties of the biomaterials which involve printability and the ability to hold its structural integrity. Proper design of experiments with extensive rheological investigation can help identify useful mechanical property ranges which are directly related to the geometric fidelity of 3D bio-printed scaffolds. Therefore, to investigate the printability of a low viscosity Alginate-Carboxymethyl Cellulose (CMC), multiple concentrations of the mixture were tested maintaining a 8% (w/v) solid content. A set of rheological tests such as the Steady Rate Sweep Test, Three Point Thixotropic Test (3ITT), and Amplitude test were performed. The outcome of those tests showed that the rheological properties can be controlled with the percentage of CMC in the mixtures. The fabricated filaments and scaffolds in the 5 combinations of CMC percentages were analyzed for flowability and shape fidelity. The rheological results and the printability and shape fidelity results were analyzed.
Role of pendant side-chain length in determining polymer 3D printability
Three-dimensional (3D) printing allows for creation of patient-specific implants. However, development of new synthetic materials for 3D printing has been relatively slow with only a few polymers available for tissue engineering applications. Most of these polymers require harsh processing conditions like high temperatures and pressures or are mixed with a combination of leachable additives like plasticizers, initiators, crosslinkers, and solvents to enable 3D printing. Therefore, to propel the development of new polymers for ambient temperature, additive-free 3D printing it is necessary to systematically understand the relationship between the structure of a polymer with its 3D printability. Herein, three homopolyesters were synthesized, each with a common backbone but differing in the length of their saturated, aliphatic pendant chains with 2, 6, or 15 carbons. The physical properties such as the glass transition temperature ( T g ) and the rheological properties like shear thinning, temperature response, and stress relaxation were correlated to the individual polymer's 3D printability. The 3D printability of the polymers was assessed based on four criteria: ability to be extruded as continuous filaments, shape fidelity, the retention of printed shape, and the ability to form free hanging filaments. We observed that the polymers with longer side chains can be extruded at low temperature and pressure because the long side chains act as internal diluents and increase the flowability of the polymer. However, their ability to retain the 3D printed shape is adversely affected by the increase in side chain length, unless the side chains form ordered structures leading to immediate recovery of viscosity. The insight derived from the systematic investigation of the effect of polymer structure on their rheology and 3D printability can be used to rationally design other polymers for extrusion-based direct-write 3D printing.
more »
« less
- Award ID(s):
- 1659531
- NSF-PAR ID:
- 10219576
- Date Published:
- Journal Name:
- Polymer Chemistry
- Volume:
- 10
- Issue:
- 40
- ISSN:
- 1759-9954
- Page Range / eLocation ID:
- 5543 to 5554
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
null (Ed.)more » « less
Abstract -
The promising success of 3D printing technique with synthetic polymers like nylon, ABS, PLA and epoxy motivates the researchers to put efforts into fabricating constructs with biocompatible natural polymers. The efforts have been broadened into various fields such as bioengineering, manufacturing, and regenerative medicine. Additive biomanufacturing commonly known as 3D bioprinting shows a lot of potential in tissue engineering with those natural polymers. Some challenges such as achieving printability, maintaining geometry in post printing stage, comforting encapsulated cells, and ensuring high proliferation are to be resolved to turn this process into a successful trial. Appropriate design of experiments with a detail rheological investigation can identify useful mechanical properties which is directly related to shape fidelity of 3D bio-printed scaffolds. As candidate natural polymers, Alginate-low viscous Carboxymethyl Cellulose (CMC) was used restricting the solid content 8% (w/v). Various rheological tests, such as the Steady Rate Sweep Test, Thixotropic (3ITT), Amplitude, and Frequency test were performed. The result indicated that rheological properties are CMC dependent. Printability and shape fidelity were analyzed of the filaments and scaffolds fabricated with all the combinations. The rheological results were co-related with the printability and shape fidelity result.more » « less
-
Three-dimensional (3D) printing is becoming increasingly prevalent in tissue engineering, driving the demand for low-modulus, high-performance, biodegradable, and biocompatible polymers. Extrusion-based direct-write (EDW) 3D printing enables printing and customization of low-modulus materials, ranging from cell-free printing to cell-laden bioinks that closely resemble natural tissue. While EDW holds promise, the requirement for soft materials with excellent printability and shape fidelity postprinting remains unmet. The development of new synthetic materials for 3D printing applications has been relatively slow, and only a small polymer library is available for tissue engineering applications. Furthermore, most of these polymers require high temperature (FDM) or additives and solvents (DLP/SLA) to enable printability. In this study, we present low-modulus 3D printable polyester inks that enable low-temperature printing without the need for solvents or additives. To maintain shape fidelity, we incorporate physical and chemical cross-linkers. These 3D printable polyester inks contain pendant amide groups as the physical cross-linker and coumarin pendant groups as the photochemical cross-linker. Molecular dynamics simulations further confirm the presence of physical interactions between different pendants, including hydrogen bonding and hydrophobic interactions. The combination of the two types of cross-linkers enhances the zero-shear viscosity and hence provides good printability and shape fidelity.more » « less
-
Heavy metal contamination is one of the leading causes of water pollution, with known adverse effects on human health and the environment. This work demonstrates a novel custom-made 3D printable eco-friendly hydrogel and fabrication process that produces stable biocompatible adsorbents with the ability to capture and remove heavy metals from aqueous environments quickly and economically. The 3D printable ink contains alginate, gelatin, and polyethyleneimine (PEI), which binds heavy metals through primary and secondary amine side chains favoring heavy metal adsorption. The ink's rheological properties are optimized to create mechanically stable constructs, in the form of 3D-printed tablets, fabricated entirely by printing. The optimized tablets have high porosity and accessible surface area with multiple binding sites for heavy metal ion adsorption while the printing process enables rapid and affordable production with the potential for scale-up. The results demonstrate the contribution of hydrogel composition and rheology in determining the printability, stability, and heavy metal binding characteristics of the hydrogel, and indicate the critical role of the PEI in increasing stability of the printed construct, in addition to its metal binding properties. The highest removal capacity was obtained for copper, followed by cadmium, cobalt, and nickel ions. In the optimized formulation, each hydrogel tablet removed 60% from 100 ppm copper in 5 h and up to 98% in 18 h. For more concentrated solutions (1000 ppm), ∼25% of copper was removed in 18 h. The printed tablets are stable, robust, and can be produced in a single simple step from inexpensive biomaterials. The ink's tunability, excellent printability, and stability offer a universally applicable procedure for creating hydrogel-based structures for environmental remediation. These unique capabilities open new avenues for manufacturing tailor-made constructs with integrated functionality for water treatment and environmental applications.more » « less
-
more » « less
Abstract The fabrication of three‐dimensional (3D) scaffolds is indispensable to tissue engineering and 3D printing is emerging as an important approach towards this. Hydrogels are often used as inks in extrusion‐based 3D printing, including with encapsulated cells; however, numerous challenging requirements exist, including appropriate viscosity, the ability to stabilize after extrusion, and cytocompatibility. Here, we present a shear‐thinning and self‐healing hydrogel crosslinked through dynamic covalent chemistry for 3D bioprinting. Specifically, hyaluronic acid was modified with either hydrazide or aldehyde groups and mixed to form hydrogels containing a dynamic hydrazone bond. Due to their shear‐thinning and self‐healing properties, the hydrogels could be extruded for 3D printing of structures with high shape fidelity, stability to relaxation, and cytocompatibility with encapsulated fibroblasts (>80% viability). Forces for extrusion and filament sizes were dependent on parameters such as material concentration and needle gauge. To increase scaffold functionality, a second photocrosslinkable interpenetrating network was included that was used for orthogonal photostiffening and photopatterning through a thiol‐ene reaction. Photostiffening increased the scaffold's modulus (∼300%) while significantly decreasing erosion (∼70%), whereas photopatterning allowed for spatial modification of scaffolds with dyes. Overall, this work introduces a simple approach to both fabricate and modify 3D printed scaffolds. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 865–875, 2018.
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/c9py00879a