SUMMARY Low-temperature plastic rheology of calcite plays a significant role in the dynamics of Earth's crust. However, it is technically challenging to study plastic rheology at low temperatures because of the high confining pressures required to inhibit fracturing. Micromechanical tests, such as nanoindentation and micropillar compression, can provide insight into plastic rheology under these conditions because, due to the small scale, plastic deformation can be achieved at low temperatures without the need for secondary confinement. In this study, nanoindentation and micropillar compression experiments were performed on oriented grains within a polycrystalline sample of Carrara marble at temperatures ranging from 23 to 175 °C, using a nanoindenter. Indentation hardness is acquired directly from nanoindentation experiments. These data are then used to calculate yield stress as a function of temperature using numerical approaches that model the stress state under the indenter. Indentation data are complemented by uniaxial micropillar compression experiments. Cylindrical micropillars ∼1 and ∼3 μm in diameter were fabricated using a focused ion beam-based micromachining technique. Yield stress in micropillar experiments is determined directly from the applied load and micropillar dimensions. Mechanical data are fit to constitutive flow laws for low-temperature plasticity and compared to extrapolations of similar flow laws from high-temperature experiments. This study also considered the effects of crystallographic orientation on yield stress in calcite. Although there is a clear orientation dependence to plastic yielding, this effect is relatively small in comparison to the influence of temperature.
more »
« less
Atomic-scale homogeneous plastic flow beyond near-theoretical yield stress in a metallic glass
Abstract The onset of yielding and the related atomic-scale plastic flow behavior of bulk metallic glasses at room temperature have not been fully understood due to the difficulty in performing the atomic-scale plastic deformation experiments needed to gain direct insight into the underlying fundamental deformation mechanisms. Here we overcome these limitations by combining a unique sample preparation method with atomic force microscopy-based indentation, which allows study of the yield stress, onset of yielding, and atomic-scale plastic flow of a platinum-based bulk metallic glass in volumes containing as little as approximately 1000 atoms. Yield stresses markedly higher than in conventional nanoindentation testing were observed, surpassing predictions from current models that relate yield stress to tested volumes; subsequent flow was then established to be homogeneous without exhibiting collective shear localization or loading rate dependence. Overall, variations in glass properties due to fluctuations of free volume are found to be much smaller than previously suggested.
more »
« less
- Award ID(s):
- 1901959
- PAR ID:
- 10221259
- Date Published:
- Journal Name:
- Communications Materials
- Volume:
- 2
- Issue:
- 1
- ISSN:
- 2662-4443
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Molecular processes of creep in metallic glass thin films are simulated at experimental timescales using a metadynamics-based atomistic method. Space–time evolutions of the atomic strains and nonaffine atom displacements are analyzed to reveal details of the atomic-level deformation and flow processes of amorphous creep in response to stress and thermal activations. From the simulation results, resolved spatially on the nanoscale and temporally over time increments of fractions of a second, we derive a mechanistic explanation of the well-known variation of creep rate with stress. We also construct a deformation map delineating the predominant regimes of diffusional creep at low stress and high temperature and deformational creep at high stress. Our findings validate the relevance of two original models of the mechanisms of amorphous plasticity: one focusing on atomic diffusion via free volume and the other focusing on stress-induced shear deformation. These processes are found to be nonlinearly coupled through dynamically heterogeneous fluctuations that characterize the slow dynamics of systems out of equilibrium.more » « less
-
The influence of the pore topology and polymer properties on mechanical characteristics of asymmetric polyethersulfone (PES) and symmetric polyvinylidene fluoride (PVDF) microfiltration membranes was investigated by conducting elongation, creep, stress relaxation, small-amplitude oscillatory and bubble point pressure tests. The main aspects of the membrane stress-strain curves were found to be similar despite significant differences in the pore topology and polymer properties. While the Kelvin-Voigt model for solid polymers described the membrane viscoelastic response below the transition to ductile yielding, the stress-strain curves of membranes and solid polymers above the yield point appeared to be drastically different. All tested membranes demonstrated weak strain hardening, low sensitivity to strain rate, significant elastic recovery, stress relaxation and reduction of the bubble point pressure with accumulation of plastic deformation. Therefore, tensile stresses exerted on a membrane under assembling and process conditions should be smaller than the yield stress to assure that they will not impair filter performance. The novelty of our approach is the use of models for perforated plates to evaluate membrane mechanical properties as ductile yielding for both proceeds via localized plastic deformation around pores. Presented results provide a reliable framework for development of membranes with properties tailored to applications.more » « less
-
null (Ed.)Materials that exhibit yielding behavior are used in many applications, from spreadable foods and cosmetics to direct write three-dimensional printing inks and filled rubbers. Their key design feature is the ability to transition behaviorally from solid to fluid under sufficient load or deformation. Despite its widespread applications, little is known about the dynamics of yielding in real processes, as the nonequilibrium nature of the transition impedes understanding. We demonstrate an iteratively punctuated rheological protocol that combines strain-controlled oscillatory shear with stress-controlled recovery tests. This technique provides an experimental decomposition of recoverable and unrecoverable strains, allowing for solid-like and fluid-like contributions to a yield stress material’s behavior to be separated in a time-resolved manner. Using this protocol, we investigate the overshoot in loss modulus seen in materials that yield. We show that this phenomenon is caused by the transition from primarily solid-like, viscoelastic dissipation in the linear regime to primarily fluid-like, plastic flow at larger amplitudes. We compare and contrast this with a viscoelastic liquid with no yielding behavior, where the contribution to energy dissipation from viscous flow dominates over the entire range of amplitudes tested.more » « less
-
Abstract Ultrahigh surface-to-volume ratio in nanoscale materials, could dramatically facilitate mass transport, leading to surface-mediated diffusion similar to Coble-type creep in polycrystalline materials. Unfortunately, the Coble creep is just a conceptual model, and the associated physical mechanisms of mass transport have never been revealed at atomic scale. Akin to the ambiguities in Coble creep, atomic surface diffusion in nanoscale crystals remains largely unclear, especially when mediating yielding and plastic flow. Here, by using in situ nanomechanical testing under high-resolution transmission electron microscope, we find that the diffusion-assisted dislocation nucleation induces the transition from a normal to an inverse Hall-Petch-like relation of the strength-size dependence and the surface-creep leads to the abnormal softening in flow stress with the reduction in size of nanoscale silver, contrary to the classical “alternating dislocation starvation” behavior in nanoscale platinum. This work provides insights into the atomic-scale mechanisms of diffusion-mediated deformation in nanoscale materials, and impact on the design for ultrasmall-sized nanomechanical devices.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1038/s43246-021-00124-3