Traditional Carbon Fiber Reinforced Plastics (CFRPs), carry high in-plane strength and electrical conductivity but exhibit intrinsic weaknesses in strength, toughness and conductivity in the through-thickness direction (i.e. z-direction). This paper presents a novel approach to align and thread Carbon Nanofibers (CNFs) through the porous medium (Carbon fiber fabric) using an interesting radial-flow alignment method and manufacture a novel CNFs z-threaded CFRP prepreg. This new radial-flow alignment approach is unique and has been found highly effective to z-thread the array of carbon fibers (diameter ~ 7 microns) with numerous long CNFs (length ~ 50-200 microns) under a Scanning Electronic Microscope (SEM) analysis. Experimental tests performed on a cured laminate sample prepared by this novel technique with 1 wt% aligned CNF concentration showed a significant improvement on the z-directional electrical conductivity for direct current (DC). The 1 wt% CNFs z-threaded CFRP was found about 100 times as conductive as the control CFRP; whereas the unaligned 1 wt% CNFs modified CFRP was only about 16 times as conductive as the control sample.more » « less
-
Carbon fiber reinforced polymer (CFRP) composites have been increasingly used in many vehicles such as airplanes, automobiles, and ships due to the advantages of high-strength, high-modulus, lightweight, and corrosion resistance. CFRP structures enhance the vehicle's performance, energy-efficiency, comfort, and safety. However, a common safety concern is how the CFRP materials perform when the vehicle is in fire and if there are enough time to safely evacuate the passengers. The elevated temperature can soften and decompose the polymer matrix, delaminate the CFRP laminate, and burn the CFRP through the contact with oxygen. As a result, the thermal and flammability response of CFRP is important for considering CFRP for vehicle applications; and some specialty high-temperature or flame/smoke/toxicity-proven resins have been investigated for CFRP parts manufacturing due to the needs. In this paper, a novel flame resistant hypothesis of utilizing the unique nano/micro- interlocked fiber reinforcing structure of the long-range carbon nanofiber z-threaded CFRP (ZT-CFRP) composite laminates for improving the flammability performance will be investigated. The carbon nanofibers (CNT) and carbon nanotubes (CNT), which have excellent thermal and mechanical properties, will be dispersed in an epoxy resin and will zig-zag thread through a carbon fiber fabric using an electrical/flow assisted impregnation process to create the unidirectional ZT-CFRP prepregs, respectively, which will be further processed into ZT-CFRP composite laminates. The UL-94 flammability test will be employed to characterize the ZT-CFRP laminates' flammability performance against the control baseline data of the regular CFRP, all without using any flame retardant chemicals. An impressive self-extinguishing flammability characteristic of the CNF based ZT-CFRP samples has been distinctly identified from all the samples. The UL-94 testing results and the effectiveness of using the long-range nanofiber z-threading strategy for enabling the novel nano/microstructure-induced flame resistant and self-extinguishing characteristics will be discussed.more » « less
-
Manoj Gupta (Ed.)
Three-dimensional (3D) printing with continuous carbon-fiber-reinforced polymer (C-CFRP) composites is under increasing development, as it offers more versatility than traditional molding processes, such as the out-of-autoclave-vacuum bag only (OOA-VBO) process. However, due to the layer-by-layer deposition of materials, voids can form between the layers and weaken some of the parts’ properties, such as the interlaminar shear strength (ILSS). In this paper, a novel mold-less magnetic compaction force-assisted additive manufacturing (MCFA-AM) method was used to print carbon nanofiber (CNF) z-threaded CFRP (ZT-CFRP) laminates with significantly improved ILSS and reduced void content compared to traditional C-CFRP laminates, which are printed using a no-pressure 3D-printing process (similar to the fused-deposition-modeling process). The radial flow alignment (RFA) and resin-blending techniques were utilized to manufacture a printing-compatible fast-curing ZT-CFRP prepreg tape to act as the feedstock for a MCFA-AM printhead, which was mounted on a robotic arm. In terms of the ILSS, the MCFA-AM method coupled with ZT-CFRP nanomaterial technology significantly outperformed the C-CFRP made with both the traditional no-pressure 3D-printing process and the OOA-VBO molding process. Furthermore, the mold-less MCFA-AM process more than doubled the production speed of the OOA-VBO molding process. This demonstrates that through the integration of new nanomaterials and 3D-printing techniques, a paradigm shift in C-CFRP manufacturing with significantly better performance, versatility, agility, efficiency, and lower cost is achievable.
-
Moisture is a known issue for carbon fiber reinforced polymer (CFRP) manufacturing. During the process, in which a CFRP prepreg is carefully thawed, cut, stacked, and cured into a laminate, any bad moisture control can cause voids, affect the curing, and degrade the laminate. Recent studies of carbon nanofiber z-threaded CFRP (i.e., ZT-CFRP) prepreg and its laminates showed significant multifunctional improvements in the mechanical strengths, toughness, thermal conductivity, and electrical conductivity. The carbon nanofibers zig-zag thread among the carbon fibers in the through-thickness direction (i.e., z-direction) and mechanically interlock the fiber system together to form an effective 3D-fiber-network reinforced laminate. This paper presents a preliminary experimental study on the ZT-CFRP prepreg when facing the moisture exposure during the prepreg handling and lamination process. Both the ZT-CFRP and traditional CFRP prepregs, subjected to different humidity conditions, will be cut, and cured into laminate samples. The samples will be tested for their interlaminar shear strengths (ILSS) and hardness. Microscope pictures of the samples' fracture patterns will be compared for explaining the combined impact of the moistures and the carbon nanofiber z-threading strategy on the laminates' interlaminar shear strength and curing state.more » « less
-
In this study, unidirectional carbon fiber prepregs that contain long carbon nanofiber (CNF) z threads as a through-thickness (z-directional) reinforcement were manufactured. The CNF z threads are long enough to thread through multiple carbon fiber (CF) arrays, which creates a multi-scale CNF/CF/resin-composite. The CNF z-threaded prepregs were manufactured using an electric-field aligned flow-transferring process. It was hypothesized that the CNF z-threads with the zig-zag threading pattern reinforces the interlaminar and intralaminar regions of the CFRP laminate thus improve the compressive strength by reducing the chance of carbon fiber buckling. Compressive testing was performed per modified version of ASTM D695 (i.e., SACMA SRM 1R 94) to evaluate the compressive strength of the CNF z-threaded CFRP (ZT-CFRP) laminates. The samples were manufactured using AS4 carbon fibers, EPON 862/Epikure-W resin and a 1wt% CNF content. ZT-CFRP testing results were compared with unaligned CNF-modified CFRP (UA-CFRP) and unmodified CFRP samples to investigate the impact of the CNF z-threads on the compressive strength. Results showed an increase of ~15% for the compressive strength of ZT CFRPs, whereas the UA-CFRPs experienced a decrease of ~8% when compared to unmodified CFRPs. It was concluded that CNF/carbon fiber interlocking stops and delays crack growth, and helps to stabilize carbon fibers from further buckling.more » « less