In this study, we also investigate nickel deposition on EP, CP, and as-built AM components using electroless nickel solutions. Electroless nickel plating is a method of alloy treatment designed to increase manufactured component’s hardness and surface resistance to the unrelenting environment. The electroless nickel plating process is more straightforward than its counterpart electroplating. We use low-phosphorus (2–5% P), medium-phosphorus (6–9% P), and high-phosphorus (10–13% P). These Ni deposition experiments were optimized using the L9 Taguchi design of experiments (TDOE), which compromises the prosperous content in the solution, surface finish, plane of the geometry, and bath temperature. The pre- and post-processed surface of the AM parts was characterized by KEYENCE Digital MicroscopeVHX-7000 and Phenom XL Desktop SEM. The experimental results show that electroless nickel deposition produces uniform Ni coating on the additively manufactured components up to 20 μm per hour. Mechanical properties of as-built and Ni coated AM samples were analyzed by applying a standard 10 N scratch test. Nickel coated AM samples were up to two times scratch resistant compared to the as-built samples. This study suggests electroless nickel plating is a robust viable option for surface hardening and finishing AM components for various applications and operating conditions.
more » « less- Award ID(s):
- 1914751
- NSF-PAR ID:
- 10332053
- Date Published:
- Journal Name:
- Conference: Proceedings of the ASME 2021 International Mechanical Engineering Congress and Exposition IMECE2021 November 1-5, 2021, Virtual, Online
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
"Binder jetting is an economical and rapid additive manufacturing process that offers vast opportunities to combine a variety of materials, yielding interesting and useful properties. However, binder jetted parts, which can involve at least one hard and one soft material, can be more susceptible to corrosion and wear compared to conventional single alloy components produced by laser sintering or other high-temperature processes. This paper discusses the electroless nickel coating on 420 Stainless Steel and Bronze Binder-Jetted Composites(BJC). Electroless nickel, a well-known coating to provide high corrosion resistance and hardness, was attempted on BJC. To produce high-quality smooth electroless nickel coatings, we attempted the Taguchi Design of Experiments. Our design of experiment involved important factors, such as the surface preparation methodology prior to electroless nickel coating. During electroless nickel coating, we investigated the role of phosphorus content, temperature, and time in the production of smooth deposition. Optical microscopy was performed for qualitative and quantitative analysis. We also performed SEM to investigate the microstructure of different electroless coatings on BJC. Interestingly, all the combinations of parameters used in the electroless nickel coating produced different microstructures. We found that surface preparation was a critical factor in determining the smoothness of the film. We also showed that the dependent on the Ni solution’s phosphorus level and temperature. Our research ng insights for improving the usefulness of a wide variety of BJC by various coatings."more » « less
-
Nondestructive Evaluation of Additively Manufactured Metal Components with an Eddy Current TechniqueThe ability of Additive Manufacturing (AM) processes to ensure delivery of high quality metal-based components is somewhat limited by insufficient inspection capabilities. The inspection of AM parts presents particular challenges due to the design flexibility that the fabrication method affords. The nondestructive evaluation (NDE) methods employed need to be selected based on the material properties, type of possible defects, and geometry of the parts. Electromagnetic method, in particular Eddy Current (EC), is proposed for the inspections. This evaluation of EC inspection considers surface and near-surface defects in a stainless steel (SS) 17 4 PH additively manufactured sample and a SS 17 4 PH annealed plates manufactured traditionally (reference sample). The surfaces of the samples were polished using 1 micron polishing Alumina grit to achieve a mirror like surface finish. 1.02 mm (0.04”), 0.508 mm (0.02”) and 0.203 mm (0.008”) deep Electronic Discharge Machining (EDM) notches were created on the polished surface of the samples. Lift off and defect responses for both additive and reference samples were obtained using a VMEC-1 commercial instrument and a 500 kHz absolute probe. The inspection results as well as conductivity assessments for the AM sample in terms of the impedance plane signature were compared to response of similar features in the reference sample. Direct measurement of electromagnetic properties of the AM samples is required for precise inspection of the parts. Results show that quantitative comparison of the AM and traditional materials help for the development of EC technology for inspection of additively manufactured metal parts.more » « less
-
This study investigates the mechanical behavior of additively manufactured (AM) 17-4 PH (AISI 630) stainless steels and compares their behavior to traditionally produced wrought counterparts. The goal of this study is to understand the key parameters influencing AM 17-4 PH steel fatigue life under ULCF conditions and to develop simple predictive models for fatigue-life estimation in AM 17-4 steel components. In this study, both AM and traditionally produced (wrought) material samples are fatigue tested under fully reversed (R = −1) strain controlled (2–4% strain) loading and characterized using micro-hardness, x-ray diffraction, and fractography methods. Results indicate decreased fatigue life for AM specimens as compared to wrought 17-4 PH specimens due to fabrication porosity and un-melted particle defect regions which provide a mechanism for internal fracture initiation. Heat treatment processes performed in this work, to both the AM and wrought specimens, had no observable effect on ULCF behavior. Result comparisons with an existing fatigue prediction model (the Coffin–Manson universal slopes equation) demonstrated consistent over-prediction of fatigue life at applied strain amplitudes greater than 3%, likely due to inherent AM fabrication defects. An alternative empirical ULCF capacity equation is proposed herein to aid future fatigue estimations in AM 17-4 PH stainless steel components.more » « less
-
Additively manufactured stainless steels have become increasingly popular due to their desirable properties, but their mechanical behavior in structural parts is not yet fully understood. Specifically, the impact of columnar microstructures on fatigue behavior is still unclear. A typical directed energy deposition (DED)‐fabricated 316L stainless steel microstructure consists of distinct zones with equiaxed and columnar grains. To answer the question of how these zones of a DED‐fabricated 316L stainless steel microstructure affect the local mechanical behavior individually, such as the fatigue strength, stress/strain distribution, and fatigue life, crystal plasticity simulations are conducted to investigate the influence of microstructure on local mechanical behavior such as fatigue strength, stress/strain distribution, and fatigue life. The simulations find that columnar microstructures exhibit better fatigue strength than equiaxed structures when the load is parallel to the major axis of the columnar grains, but the strength decreases when the load is perpendicular. This study also uses machine learning to predict fatigue life, which shows good agreement with crystal plasticity modeling. The study suggests that the combined crystal plasticity–machine learning approach is an effective way to predict the fatigue behavior of additively manufactured components.
-
Abstract Additively manufactured (AM) metallic materials often comprise as-printed dislocation cells inside grains. These dislocation cells can give rise to substantial microscale internal stresses in both initial undeformed and plastically deformed samples, thereby affecting the mechanical properties of AM metallic materials. Here we develop models of microscale internal stresses in AM stainless steel by focusing on their back stress components. Three sources of microscale back stresses are considered, including the printing and deformation-induced back stresses associated with as-printed dislocation cells as well as the deformation-induced back stresses associated with grain boundaries. We use a three-dimensional discrete dislocation dynamics model to demonstrate the manifestation of printing-induced back stresses. We adopt a dislocation pile-up model to evaluate the deformation-induced back stresses associated with as-printed dislocation cells. The extracted back stress relation from the pile-up model is incorporated into a crystal plasticity model that accounts for the other two sources of back stresses as well. The crystal plasticity finite element simulation results agree with the experimentally measured tension-compression asymmetry and macroscopic back stress, the latter of which represents the effective resultant of microscale back stresses of different origins. Our results provide an in-depth understanding of the origins and evolution of microscale internal stresses in AM metallic materials.more » « less