Title: Environmentally friendly thermoelectric sulphide Cu 2 ZnSnS 4 single crystals achieving a 1.6 dimensionless figure of merit ZT
Thermoelectrics (TEs) are an important class of technology that harvest electric power directly from heat sources. When designing both high performance and environmentally friendly TE materials, the pseudo-cubic structure has great theoretical potential to maximize the dimensionless figure of merit ZT . The TE multinary single crystal with a pseudo-cubic structure paves a new path toward manipulating valley degeneracy and anisotropy with low thermal conductivity caused by short-range lattice distortion. Here, we report a record high ZT = 1.6 around 800 K realized in a totally environmentally benign p-type Na-doped Cu 2 ZnSnS 4 (CZTS) single crystal. The exceptional performance comes from a high power factor while maintaining intrinsically low thermal conductivity. The combination of the pseudo-cubic structure and intrinsic properties of the CZTS single crystal takes advantage of simple material tuning without complex techniques.  more » « less
Award ID(s):
1651668
NSF-PAR ID:
10340375
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Journal of Materials Chemistry A
Volume:
9
Issue:
28
ISSN:
2050-7488
Page Range / eLocation ID:
15595 to 15604
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Germanium telluride is a high performing thermoelectric material that additionally serves as a base for alloys such as GeTe–AgSbTe 2 and GeTe–PbTe. Such performance motivates exploration of other GeTe alloys in order understand the impact of site substitution on electron and phonon transport. In this work, we consider the root causes of the high thermoelectric performance material Ge 1− x Mn x Te. Along this alloy line, the crystal structure, electronic band structure, and electron and phonon scattering all depend heavily on the Mn content. Structural analysis of special quasirandom alloy structures indicate the thermodynamic stability of the rock salt phase over the rhombohedral phase with increased Mn incorporation. Effective band structure calculations indicate band convergence, the emergence of new valence band maxima, and strong smearing at the band edge with increased Mn content in both phases. High temperature measurements on bulk polycrystalline samples show a reduction in hole mobility and a dramatic increase in effective mass with respect to increasing Mn content. In contrast, synthesis as a function of tellurium chemical potential does not significantly impact electronic properties. Thermal conductivity shows a minimum near the rhombohedral to cubic phase transition, while the Mn Ge point defect scattering is weak as indicated by the low K L dependence on the Ge–Mn fraction (Fig. 10). From this work, alloys near this phase transition show optimal performance due to low thermal conductivity, moderate effective mass, and low scattering rates compared to Mn-rich compositions. 
    more » « less
  2. Thermoelectric materials can convert heat into electricity. They are used to generate electricity when other power sources are not available or to increase energy efficiency by recycling waste heat. The Yb 21 Mn 4 Sb 18 phase was previously shown to have good thermoelectric performance due to its large Seebeck coefficient (∼290 μV K −1 ) and low thermal conductivity (0.4 W m −1 K −1 ). These characteristics stem respectively from the unique [Mn 4 Sb 10 ] 22− subunit and the large unit cell/site disorder inherent in this phase. The solid solutions, Yb 21 Mn 4− x Cd x Sb 18 ( x = 0, 0.5, 1.0, 1.5) and Yb 21− y Ca y Mn 4 Sb 18 ( y = 3, 6, 9, 10.5) have been prepared, their structures characterized and thermoelectric properties from room temperature to 800 K measured. A detailed look into the structural disorder for the Cd and Ca solid solutions was performed using synchrotron powder X-ray diffraction and pair distribution function methods and shows that these are highly disordered structures. The substitution of Cd gives rise to more metallic behavior whereas Ca substitution results in high resistivity. As both Cd and Ca are isoelectronic substitutions, the changes in properties are attributed to changes in the electronic structure. Both solid solutions show that the thermal conductivities remain extremely low (∼0.4 W m −1 K −1 ) and that the Seebeck coefficients remain high (>200 μV K −1 ). The temperature dependence of the carrier mobility with increased Ca substitution, changing from approximately T −1 to T −0.5 , suggests that another scattering mechanism is being introduced. As the bonding changes from polar covalent with Yb to ionic for Ca, polar optical phonon scattering becomes the dominant mechanism. Experimental studies of the Cd solid solutions result in a max zT of ∼1 at 800 K and, more importantly for application purposes, a ZT avg ∼ 0.6 from 300 K to 800 K. 
    more » « less
  3. Abstract

    Sb‐doped and GeTe‐alloyed n‐type thermoelectric materials that show an excellent figure of meritZTin the intermediate temperature range (400–800 K) are reported. The synergistic effect of favorable changes to the band structure resulting in high Seebeck coefficient and enhanced phonon scattering by point defects and nanoscale precipitates resulting in reduction of thermal conductivity are demonstrated. The samples can be tuned as single‐phase solid solution (SS) or two‐phase system with nanoscale precipitates (Nano) based on the annealing processes. The GeTe alloying results in band structure modification by widening the bandgap and increasing the density‐of‐states effective mass of PbTe, resulting in significantly enhanced Seebeck coefficients. The nanoscale precipitates can improve the power factor in the low temperature range and further reduce the lattice thermal conductivity (κlat). Specifically, the Seebeck coefficient of Pb0.988Sb0.012Te–13%GeTe–Nano approaches −280 µV K−1at 673 K with a low κlatof 0.56 W m−1K−1at 573 K. Consequently, a peakZTvalue of 1.38 is achieved at 623 K. Moreover, a high averageZTavgvalue of ≈1.04 is obtained in the temperature range from 300 to 773 K for n‐type Pb0.988Sb0.012Te–13%GeTe–Nano.

     
    more » « less
  4. Abstract

    The Ag and In co‐doped PbTe, AgnPb100InnTe100+2n(LIST), exhibitsn‐type behavior and features unique inherent electronic levels that induce self‐tuning carrier density. Results show that In is amphoteric in the LIST, forming both In3+and In1+centers. Through unique interplay of valence fluctuations in the In centers and conduction band filling, the electron carrier density can be increased from ≈3.1 × 1018cm−3at 323 K to ≈2.4 × 1019cm−3at 820 K, leading to large power factors peaking at ≈16.0 µWcm−1K−2at 873 K. The lone pair of electrons from In+can be thermally continuously promoted into the conduction band forming In3+, consistent with the amphoteric character of In. Moreover, with rising temperature, the Fermi level shifts into the conduction band, which enlarges the optical band gap based on the Moss–Burstein effect, and reduces bipolar diffusion and thermal conductivity. Adding extra Ag in LIST improves the electrical transport properties and meanwhile lowers the lattice thermal conductivity to ≈0.40 Wm−1K−1. The addition of Ag creates spindle‐shaped Ag2Te nanoprecipitates and atomic‐scale interstitials that scatter a broader set of phonons. As a result, a maximumZTvalue ≈1.5 at 873 K is achieved in Ag6Pb100InTe102(LIST).

     
    more » « less
  5. Abstract: Thermoelectricity allows direct conversion between heat and electricity, providing alternatives for green energy technologies. Despite these advantages, for most materials the energy conversion efficiency is limited by the tendency for the electrical and thermal conductivity to be proportional to each other and the Seebeck coefficient to be small. Here we report counter examples, where the heavy fermion compounds Yb TM 2 Zn 20 ( TM = Co, Rh, Ir) exhibit enhanced thermoelectric performance including a large power factor ( PF = 74 μW/cm-K 2 ; TM = Ir) and a high figure of merit ( ZT = 0.07; TM = Ir) at 35 K. The combination of the strongly hybridized electronic state originating from the Yb f -electrons and the novel structural features (large unit cell and possible soft phonon modes) leads to high power factors and small thermal conductivity values. This demonstrates that with further optimization these systems could provide a platform for the next generation of low temperature thermoelectric materials. 
    more » « less