In joining Fe-alloys and Cu-containing alloys to access the high strength of steels and corrosion resistance of Cu-alloy, cracking is widely observed due to the significant Cu microsegregation during the solidification process, resulting in an interdendritic Cu-rich liquid film at the end of solidification. By fabricating functionally graded materials (FGMs) that incorporate additional elements like Ni in the transition region between these terminal alloy classes, the hot cracking can be reduced. In the present work, the joining of stainless steel 316L (SS316L) and Monel400 by modifying the Ni concentration in the gradient region was studied. A new hot cracking criterion based on hybrid Scheil-equilibrium approach was developed and validated with monolithic multi-layer samples within the SS316L-Ni-Monel400 three-alloy system and a SS316L to 55/45 wt% SS316L/Ni to Monel400 FGM sample fabricated by direct energy deposition (DED). The new hot cracking criterion, based on the hybrid Scheil-equilibrium approach, is expected to help design FGM paths between other Fe-alloys and Cu-containing alloys as well.
more »
« less
In situ synchrotron diffraction and modeling of non-equilibrium solidification of a MnFeCoNiCu alloy
Abstract The solidification mechanism and segregation behavior of laser-melted Mn35Fe5Co20Ni20Cu20was firstly investigated via in situ synchrotron x-ray diffraction at millisecond temporal resolution. The transient composition evolution of the random solid solution during sequential solidification of dendritic and interdendritic regions complicates the analysis of synchrotron diffraction data via any single conventional tool, such as Rietveld refinement. Therefore, a novel approach combining a hard-sphere approximation model, thermodynamic simulation, thermal expansion measurement and microstructural characterization was developed to assist in a fundamental understanding of the evolution of local composition, lattice parameter, and dendrite volume fraction corresponding to the diffraction data. This methodology yields self-consistent results across different methods. Via this approach, four distinct stages were identified, including: (I) FCC dendrite solidification, (II) solidification of FCC interdendritic region, (III) solid-state interdiffusion and (IV) final cooling with marginal diffusion. It was found out that in Stage I, Cu and Mn were rejected into liquid as Mn35Fe5Co20Ni20Cu20solidified dendritically. During Stage II, the lattice parameter disparity between dendrite and interdendritic region escalated as Cu and Mn continued segregating into the interdendritic region. After complete solidification, during Stage III, the lattice parameter disparity gradually decreases, demonstrating a degree of composition homogenization. The volume fraction of dendrites slightly grew from 58.3 to 65.5%, based on the evolving composition profile across a dendrite/interdendritic interface in diffusion calculations. Postmortem metallography further confirmed that dendrites have a volume fraction of 64.7% ± 5.3% in the final microstructure.
more »
« less
- Award ID(s):
- 1847630
- PAR ID:
- 10369834
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Scientific Reports
- Volume:
- 11
- Issue:
- 1
- ISSN:
- 2045-2322
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Additions of nitrogen were made to ERNiCr-3 (FM 82) weld metal to investigate the effect on weld metal microstructure and solidification cracking susceptibility. Weld samples were prepared with different argon-nitrogen shielding gas mixtures to produce nitrogen variations in the weld metal. The cast pin tear test (CPTT) was then used to evaluate solidification cracking susceptibility as a function of weld metal nitrogen content. Phase fraction and composition of constituents in the final solidification microstructure were characterized via optical and electron microscopy. Thermodynamic (Scheil) calculations were performed to determine the phase formation during solidification, associated solidification path, and solidification temperature range. Solidification cracking susceptibility was found to increase significantly with increasing nitrogen content. The overall amount of second phase in the solidified microstructure increased when nitrogen was added to the weld metal. Small skeletal constituents in the interdendritic regions, primarily Nb-rich carbides (NbC), were more frequently observed with increasing weld metal nitrogen content. Larger cuboidal Ti-rich nitrides (TiN) and carbonitrides (Ti, Nb)(N, C) were found only when nitrogen was added to the weld metal. Their location in dendrite core regions indicates formation during an earlier stage of the solidification process. Scheil calculations confirmed the strong effect of nitrogen additions on the amount and sequence of phase formation during solidification of ERNiCr-3 weld metal. High nitrogen levels ( 100 ppm) facilitate primary nitride formation prior to the solidification of the gamma () dendrites, and increase the amount of phase constituents in the solidification microstructure. The presence of nitrogen also shifts the start of the eutectic /NbC formation at the end of solidification to lower temperatures, which results in an increase in the solidification temperature range. This occurs at much lower nitrogen levels ( 25 ppm) and correlates with the observed increase in solidification cracking susceptibility.more » « less
-
Joining of Cu-based dispersion-strengthened alloys to Ni-based superalloys has garnered increased attention for liquid rocket engine applications due to the high thermal conductivity of Cu-based alloys and high temperature tensile strength of Ni-based superalloys. However, such joints can suffer from cracking when joined via liquid state processes, leading to part failure. In this work, compositions of 15–95 wt.% GRCop42 are alloyed with Inconel 625 and characterized to better understand the root cause of cracking. Results indicate a lack of miscibility between Cu-deprived and Cu-rich liquids in compositions corresponding to 30–95 wt.% GRCop42. Two distinct morphologies are observed and explained by use of CALPHAD; Cu-deprived dendrites with Cu-rich interdendritic zones at 30–50 wt.% GRCop42 and Cu-deprived spheres surrounded by a Cu-rich matrix at 60–95 wt.% GRCop42. Phase analysis reveals brittle intermetallic phases precipitate in the 60–95 wt.% GRCop42 Cu-deprived region. Three cracking mechanisms are proposed herein that provide guidance on the avoidance of defects Ni-based superalloy to Cu-based dispersion strengthened alloy joints.more » « less
-
Extensive research has been conducted on Ti–Fe–Sn ultrafine eutectic composites due to their high yield strength, compared to conventional microcrystalline alloys. The unique microstructure of ultrafine eutectic composites, which consists of the ultrafine-grained lamella matrix with the formation of primary dendrites, leads to high strength and desirable plasticity. A lamellar structure is known for its high strength with limited plasticity, owing to its interface-strengthening effect. Thus, extensive efforts have been conducted to induce the lamellar structure and control the volume fraction of primary dendrites to enhance plasticity by tailoring the compositions. In this study, however, it was found that not only the volume fraction of primary dendrites but also the morphology of dendrites constitute key factors in inducing excellent ductility. We selected three compositions of Ti–Fe–Sn ultrafine eutectic composites, considering the distinct volume fractions and morphologies of β-Ti dendrites based on the Ti–Fe–Sn ternary phase diagram. As these compositions approach quasi-peritectic reaction points, the α″-Ti martensitic phase forms within the primary β-Ti dendrites due to under-cooling effects. This pre-formation of the α″-Ti martensitic phase effectively governs the growth direction of β-Ti dendrites, resulting in the development of round-shaped primary dendrites during the quenching process. These microstructural evolutions of β-Ti dendrites, in turn, lead to an improvement in ductility without a significant compromise in strength. Hence, we propose that fine-tuning the composition to control the primary dendrite morphology can be a highly effective alloy design strategy, enabling the attainment of greater macroscopic plasticity without the typical ductility and strength trade-off.more » « less
-
This work proposes a methodology for designing high-strength precipitation-hardened high entropy alloys (HEAs) with an FCC matrix and L12 precipitates. High-throughput solidification calculations were conducted using the CALPHAD method, evaluating 11,235 alloys in the Cr-Co-Ni-Al-Ti system under specific boundary conditions. The acquired information was used to filter the alloys, focusing on alloys exhibiting an FCC+L12 phase field at 750 °C, a solidification interval narrower than 100 °C, and a solvus temperature under 1100 çC. The filtered alloys were analyzed to estimate their solid solution and precipitation hardening contributions to yield strength, with antiphase boundary energy (APB) assessed using two models. Three alloys were selected for testing the proposed strategy, including one with the highest yield stress and others for comparison. These alloys were produced, processed, and characterized using DSC, synchrotron XRD, SEM, and TEM. The results showed that the desired microstructure was achieved, with the alloys consisting of an FCC matrix and a high-volume fraction of L12 precipitates. Tensile tests at room temperature, 650 °C, 750 °C, and 850 °C demonstrated that the proposed model predicts well the yield strength trends, demonstrating the potential of the proposed approach for accelerating the discovery and development of novel HEAs with tailored properties.more » « less