Abstract Cultivated natural fibers have a huge possibility for green and sustainable reinforcement for polymers, but their limited load-bearing ability and flammability prevent them from wide applications in composites. According to the beam theory, normal stress is the maximum at the outermost layers but zero at the mid-plane under bending (with (non)linear strain distribution). Shear stress is the maximum at the mid-plane but manageable for most polymers. Accordingly, a laminated composite made of hybrid fiber-reinforced shape memory photopolymer was developed, incorporating strong synthetic glass fibers over a weak core of natural hemp fibers. Even with a significant proportion of natural hemp fibers, the mechanical properties of the hybrid composites were close to those reinforced solely with glass fibers. The composites exhibited good shape memory properties, with at least 52% shape fixity ratio and 71% shape recovery ratio, and 24 MPa recovery stress. After 40 s burning, a hybrid composite still maintained 83.53% of its load carrying capacity. Therefore, in addition to largely maintaining the load carrying capacity through the hybrid reinforcement design, the use of shape memory photopolymer endowed a couple of new functionalities to the composites: the plastically deformed laminated composite beam can largely return to its original shape due to the shape memory effect of the polymer matrix, and the flame retardancy of the polymer matrix makes the flammable hemp fiber survive the fire hazard. The findings of this study present exciting prospects for utilizing low-strength and flammable natural fibers in multifunctional load-bearing composites that possess both flame retardancy and shape memory properties.
more »
« less
Influence of uniaxial compression on the shape memory behavior of vitrimer composite embedded with tension‐programmed unidirectional shape memory polymer fibers
Abstract Tension programmed shape memory polymer (SMP) fibers have been used as sutures for closing wide‐opened cracks per the close‐then‐heal strategy. However, the composite may be subjected to compression loading during service. These compression loads can reduce the amount of recoverable strain in these pre‐tensioned fibers, limiting their ability to close cracks. The purpose of this study is to investigate the effect of in‐service compression loading on the shape memory effect (SME) of composites consisting of SMP fiber and SMP matrix. To this end, pre‐stretched shape memory Polyethylene Terephthalate (PET) fibers were embedded into a shape memory vitrimer to obtain composite samples with different fiber volume fractions. The SME of both the PET fiber and the vitrimer was investigated. The effect of compression load on the SME of the composite was studied. It is found that, uniaxial compression on the composite along the fiber direction significantly reduced the shrinking ability of the embedded pre‐tensioned SMP fibers. Hence, this is a factor that needs to be considered when designing such types of self‐healing composites.
more »
« less
- Award ID(s):
- 1946231
- PAR ID:
- 10375626
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Journal of Applied Polymer Science
- Volume:
- 138
- Issue:
- 20
- ISSN:
- 0021-8995
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract In this paper, an open-cell metallic foam was filled in by a tough shape memory polymer (SMP), to form a hybrid metal/polymer composite with multifunctionalities and enhanced mechanical properties. This work aims to study the positive composite actions between the metallic skeleton and the SMP filler. Mechanical, thermal, and conductive properties of the resulting hybrid composite were evaluated and compared to the individual components. Uniaxial compression tests and shape memory effect tests were conducted. Results demonstrated an improvement in the compressive strength and toughness. The hybrid composite also exhibited excellent shape recovery and high recovery stress of 1.76 MPa. Infrared thermography has been used to verify the free shape recovery by Joule heating. Sandwich structures with the hybrid composite as the core were studied through low velocity impact test and three-point bending test. The sandwich structures with the composite foam core showed significant performance improvement in both tests. Electrical resistivity study during the three-point bending test validates the possible application of this multifunctional polymer-aluminum open cell foam composite as strain sensor. This type of hybrid composites can be beneficial in many industrial sectors that search for an ideal combination of high strength, high toughness, low weight, damage sensing, and excellent energy absorption capabilities.more » « less
-
Fibrous shape memory polymers (SMPs) have received growing interest in various applications, especially in biomedical applications, which offer new structures at the microscopic level and the potential of enhanced shape deformation of SMPs. In this paper, we report on the development and investigation of the properties of acrylate-based shape memory polymer fibers, fabricated by electrospinning technology with the addition of polystyrene (PS). Fibers with different diameters are manufactured using four different PS solution concentrations (25, 30, 35, and 40 wt%) and three flow rates (1.0, 2.5, and 5.0 μL min −1 ) with a 25 kV applied voltage and 17 cm electrospinning distance. Scanning electron microscope (SEM) images reveal that the average fiber diameter varies with polymer concentration and flow rates, ranging from 0.655 ± 0.376 to 4.975 ± 1.634 μm. Dynamic mechanical analysis (DMA) and stress–strain testing present that the glass transition temperature and tensile values are affected by fiber diameter distribution. The cyclic bending test directly proves that the electrospun SMP fiber webs are able to fully recover; additionally, the recovery speed is also affected by fiber diameter. With the combination of the SMP material and electrospinning technology, this work paves the way in designing and optimizing future SMP fibers properties by adjusting the fiber diameter.more » « less
-
Abstract High-performance lightweight architectures, such as metallic microlattices with excellent mechanical properties have been 3D printed, but they do not possess shape memory effect (SME), limiting their usages for advanced engineering structures, such as serving as a core in multifunctional lightweight sandwich structures. 3D printable self-healing shape memory polymer (SMP) microlattices could be a solution. However, existing 3D printable thermoset SMPs are limited to either low strength, poor stress memory, or non-recyclability. To address this issue, a new thermoset polymer, integrated with high strength, high recovery stress, perfect shape recovery, good recyclability, and 3D printability using direct light printing, has been developed in this study. Lightweight microlattices with various unit cells and length scales were printed and tested. The results show that the cubic microlattice has mechanical strength comparable to or even greater than that of metallic microlattices, good SME, decent recovery stress, and recyclability, making it the first multifunctional lightweight architecture (MLA) for potential multifunctional lightweight load carrying structural applications.more » « less
-
This study investigates a neoteric approach in manufacturing lunar regolith-filled shape memory vitrimer (SMV) composites for extraterrestrial applications. A SMV with robust mechanical properties was combined with locally available lunar regolith to form a composite material. Fourier Transfer Infrared Spectroscopy (FTIR), Scanning Electron Microscope (SEM), Thermogravimetric Analysis (TGA), and X-ray fluorescence (XRF) were used to characterize the resin, the regolith simulant, and the prepared SMV-regolith composites. We explored conventional synthesis as well as 3D printing methods for manufacturing the composite. Glass fabric-reinforced laminated composites were also prepared to evaluate the impact tolerance and damage healing efficiency. Compressive strength, flexural strength, and impact resistance of the composite were tested at both room and elevated temperatures. A compressive strength of 96.0 MPa and 5.4 MPa were recorded for composite with 40 wt% regolith ratio at room and elevated temperatures, respectively. The glass fabric reinforced SMV-regolith laminate exhibited a bending strength of 232.7 MPa, good impact tolerance under low-velocity impact test, and good healing efficiency up to two damage healing cycles. The 3D printed SMV-regolith composite using a liquid crystal display (LCD)-based printer exhibited a good thermomechanical property with a compressive and tensile strength of 139.16 MPa and 13.99 MPa, respectively, and a good shape memory effect. However, the LCD-based printing using vat-photopolymerization limits the size of the printed samples. Nonetheless, this study shows that utilization of regolith to form advanced composite is possible. SMV regolith composite is a promising material for lunar base applications due to its simple manufacturing process, excellent mechanical properties, and low energy consumption.more » « less