Polyurethane and polyurea-based adhesives are widely used in various applications, from automotive to electronics and medical applications. The adhesive performance depends strongly on its composition, and developing the formulation–structure–property relationship is crucial to making better products. Here, we investigate the dependence of the linear viscoelastic properties of polyurea nanocomposites, with an IPDI-based polyurea (PUa) matrix and exfoliated graphene nanoplatelet (xGnP) fillers, on the hard-segment weight fraction (HSWF) and the xGnP loading. We characterize the material using scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA). It is found that changing the HSWF leads to a significant variation in the stiffness of the material, from about 10 MPa for 20% HSWF to about 100 MPa for 30% HSWF and about 250 MPa for the 40% HSWF polymer (as measured by the tensile storage modulus at room temperature). The effect of the xGNP loading was significantly more limited and was generally within experimental error, except for the 20% HSWF material, where the xGNP addition led to about an 80% increase in stiffness. To correctly interpret the DMA results, we developed a new physics-based rheological model for the description of the storage and loss moduli. The model is based on the fractional calculus approach and successfully describes the material rheology in a broad range of temperatures (−70 °C–+70 °C) and frequencies (0.1–100 s−1), using only six physically meaningful fitting parameters for each material. The results provide guidance for the development of nanocomposite PUa-based materials.
more »
« less
Experimental and modeling studies of IPDI ‐based polyurea elastomers – The role of hard segment fraction
Abstract Segmented polyureas (PUa) are industrially important class of polymers widely used in coatings, sealant, and adhesive applications. Here, we report synthesis, characterization, and modeling of Isophorone Diisocyanate‐Diethyl‐Toluene‐Diamine‐Polyether amine (IPDI‐DETDA‐PO PUa) with varied hard segment contents of 20, 30, and 40 weight percent. For each of the three materials, we study its structure and phase behavior using FTIR, DSC, and TEM, and clearly show the presence of microphase separation between the hard and soft nanodomains. We then measure the linear viscoelastic response of the PUa‐s using DMA (frequency sweeps at multiple temperatures). The DMA data are shown to obey the time‐temperature superposition. Finally, we develop a new micromechanical model describing the DMA results; the model describes a phase‐separated PUa as two “Fractional‐order Maxwell gels” branches, connected in parallel, with the first FMG branch representing the “percolated hard phase and the second one modeling the “filled soft phase. In agreement with the earlier thermodynamic theories, the volume‐fraction of the percolated hard phase is related to the hard segment weight‐fraction (HSWF), defined as the combined mass of IPDI and DETDA normalized to the total mass of the polymer. The data and model are found to be in a good qualitative and quantitative agreement.
more »
« less
- Award ID(s):
- 1923201
- PAR ID:
- 10389776
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Journal of Applied Polymer Science
- Volume:
- 140
- Issue:
- 10
- ISSN:
- 0021-8995
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
ABSTRACT We present a simple regulator-type framework designed specifically for modelling formation of dwarf galaxies. Despite its simplicity, when coupled with realistic mass accretion histories of haloes from simulations and reasonable choices for model parameter values, the framework can reproduce a remarkably broad range of observed properties of dwarf galaxies over seven orders of magnitude in stellar mass. In particular, we show that the model can simultaneously match observational constraints on the stellar mass–halo mass relation, as well as observed relations between stellar mass and gas phase and stellar metallicities, gas mass, size, and star formation rate, as well as general form and diversity of star formation histories of observed dwarf galaxies. The model can thus be used to predict photometric properties of dwarf galaxies hosted by dark matter haloes in N-body simulations, such as colours, surface brightnesses, and mass-to-light ratios and to forward model observations of dwarf galaxies. We present examples of such modelling and show that colours and surface brightness distributions of model galaxies are in good agreement with observed distributions for dwarfs in recent observational surveys. We also show that in contrast with the common assumption, the absolute magnitude–halo mass relation is generally predicted to have a non-power law form in the dwarf regime, and that the fraction of haloes that host detectable ultra-faint galaxies is sensitive to reionization redshift (zrei) and is predicted to be consistent with observations for zrei ≲ 9.more » « less
-
We discuss a new approach for jet physics analysis by using subtraction between cumulants of jet substructure observables. The subtracted cumulants are insensitive to soft-particle background uncorrelated with the hard process and allow comparisons between theoretical results and experimental measurements without the complication of soft background like underlying and pile-up events. We find our method using jet mass cumulants efficiently eliminates the background in Monte Carlo simulations and ATLAS jet mass measurements and they show a good agreement with our analytic calculations performed using soft-collinear effective theory.more » « less
-
The cytoskeleton is a model active matter system that controls processes as diverse as cell motility and mechanosensing. While both active actomyosin dynamics and actin–microtubule interactions are key to the cytoskeleton's versatility and adaptability, an understanding of their interplay is lacking. Here, we couple microscale experiments with mechanistic modeling to elucidate how connectivity, rigidity, and force-generation affect emergent material properties in composite networks of actin, tubulin, and myosin. We use multi-spectral imaging, time-resolved differential dynamic microscopy and spatial image autocorrelation to show that ballistic contraction occurs in composites with sufficient flexibility and motor density, but that a critical fraction of microtubules is necessary to sustain controlled dynamics. The active double-network models we develop, which recapitulate our experimental findings, reveal that while percolated actomyosin networks are essential for contraction, only composites with comparable actin and microtubule densities can simultaneously resist mechanical stresses while supporting substantial restructuring. The comprehensive phase map we present not only provides important insight into the different routes the cytoskeleton can use to alter its dynamics and structure, but also serves as a much-needed blueprint for designing cytoskeleton-inspired materials that couple tunability with resilience and adaptability for diverse applications ranging from wound healing to soft robotics.more » « less
-
Abstract Elastomers with segmental microstructure are a fascinating class of shock‐tolerant and impact‐resistant materials. However, their technological potential remains untapped due to a vague understanding of the molecular contributions to their superior mechanical behavior. Herein, in situ light‐matter interactions, to reveal the extent of microstructural mobility by temporally exploiting molecular processes during creep response, are leveraged. The segmental microstructure comprises aromatic hard domains embedded within an aliphatic soft matrix. High‐resolution digital image correlation reveals the development of strain striations, mild anisotropy, and the mechanisms responsible for domain mobility, where the rate of hard segment mobility is found to be 60% slower than that of the soft segment. Terahertz spectral analyses pinpoint the contributions of interchain hydrogen bonding of the hard segments and their significant conformational changes by observing spectral features at ≈1.2THz and ≈1.67THz. Moreover, the domain mobility is examined using experimental and computational light scattering approaches, uncovering dynamic scattering and elucidating the difference in the complex refractive index of the soft and hard segments. The study unlocks the pathway for quantitative measurements of elusive molecular mobility and conformational changes during mechanical loading and sheds light on the origin of the shock tolerance in some elastomeric polymers with segmental microstructure.more » « less