Abstract Foam materials are widely used in packaging and buildings for thermal insulation, sound absorption, shock absorption, and other functions. They are dominated by petroleum‐based plastics, most of which, however, are not biodegradable nor fire‐proofing, leading to severe plastic pollution and safety concerns. Here, a fire‐proofing, thermally insulating, recyclable 3D graphite‐cellulose nanofiber (G‐CNF) foam fabricated from resource‐abundant graphite and cellulose is reported. A freeze‐drying‐free and scalable ionic crosslinking method is developed to fabricate Cu2+ionic crosslinked G‐CNF (Cu‐G‐CNF) foam with a low energy consumption and cost. Moreover, the direct foam formation strategy enables local foam manufacturing to fulfil the local demand. The ionic crosslinked G‐CNF foam demonstrates excellent water stability (the foam can maintain mechanical robustness even in wet state and recover after being dried in air without deformation), fire resistance (41.7 kW m−2vs 214.3 kW m−2in the peak value of heat release rate) and a low thermal conductivity (0.05 W/(mK)), without compromising the recyclability, degradability, and mechanical performance of the composite foam. The demonstrated 3D G‐CNF foam can potentially replace the commercial plastic‐based foam materials, representing a sustainable solution against the “white pollution”.
more »
« less
Manufacturing silica aerogel and cryogel through ambient pressure and freeze drying
Achieving a mesoporous structure in superinsulation materials is pivotal for guaranteeing a harmonious relationship between low thermal conductivity, high porosity, and low density. Herein, we report silica-based cryogel and aerogel materials by implementing freeze-drying and ambient-pressure-drying processes respectively. The obtained freeze-dried cryogels yield thermal conductivity of 23 mW m −1 K −1 , with specific surface area of 369.4 m 2 g −1 , and porosity of 96.7%, whereas ambient-pressure-dried aerogels exhibit thermal conductivity of 23.6 mW m −1 K −1 , specific surface area of 473.8 m 2 g −1 , and porosity of 97.4%. In addition, the fiber-reinforced nanocomposites obtained via freeze-drying feature a low thermal conductivity (28.0 mW m −1 K −1 ) and high mechanical properties (∼620 kPa maximum compressive stress and Young's modulus of 715 kPa), coupled with advanced flame-retardant capabilities, while the composite materials from the ambient pressure drying process have thermal conductivity of 28.8 mW m −1 K −1 , ∼200 kPa maximum compressive stress and Young's modulus of 612 kPa respectively. The aforementioned results highlight the capabilities of both drying processes for the development of thermal insulation materials for energy-efficient applications.
more »
« less
- Award ID(s):
- 1846863
- PAR ID:
- 10393016
- Date Published:
- Journal Name:
- RSC Advances
- Volume:
- 12
- Issue:
- 33
- ISSN:
- 2046-2069
- Page Range / eLocation ID:
- 21213 to 21222
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Abstract The conventional manufacturing processes of aerogel insulation material is largely relying on the supercritical drying, which suffers from issues of massive energy consumption, high-cost equipment, and prolonged processing time. With the consideration of large market demand of the aerogel insulation material in the next decade, a low-cost and scalable fabrication technique is highly desired. In this paper, a direct ink writing (DIW) method is used to three-dimensionally fabricate the silica aerogel insulation material, followed by room-temperature and ambient pressure drying. Compared to the supercritical drying and freeze-drying, the reported method significantly reduces the fabrication time and costs. The cost-effective DIW technique offers the capability to print complex hollow internal structures, coupled with the porous structure, is found to be beneficial to the thermal insulation property. The addition of fiber to the ink assures the durability of the fabricated product, without sacrificing the thermal insulation performance. The foam ink preparation methods and the printability are demonstrated in this paper, along with the printing of complex three-dimensional geometries. The thermal insulation performance of the printed objects is characterized, and the mechanical properties are also examined. The proposed approach is found to have 56% reduction in the processing time. The printed silica aerogels exhibit a low thermal conductivity of 0.053 W m−1 K−1.more » « less
-
Abstract Tailoring thermal transport by structural parameters could result in mechanically fragile and brittle networks. An indispensable goal is to design hierarchical architecture materials that combine thermal and mechanical properties in a continuous and cohesive network. A promising strategy to create such a hierarchical network targets additive manufacturing of hybrid porous voxels at nanoscale. Here we describe the convergence of agile additive manufacturing of porous hybrid voxels to tailor hierarchically and mechanically tunable objects. In one strategy, the uniformly distributed porous silica voxels, which form the basis for the control of thermal transport, are non-covalently interfaced with polymeric networks, yielding hierarchic super-elastic architectures with thermal insulation properties. Another additive strategy for achieving mechanical strength involves the versatile orthogonal surface hybridization of porous silica voxels retains its low thermal conductivity of 19.1 mW m−1 K−1, flexible compressive recovery strain (85%), and tailored mechanical strength from 71.6 kPa to 1.5 MPa. The printed lightweight high-fidelity objects promise thermal aging mitigation for lithium-ion batteries, providing a thermal management pathway using 3D printed silica objects.more » « less
-
Schanze, Kirk S. (Ed.)A high-deposition-area, robust inorganic scaffold, unique in its reproducible anisotropic macropores, is reported. This scaffold has a Young’s modulus of 455 ± 34 kPa and a yield strength of 215 ± 10 kPa in compression. It supports 3.5 ± 1.0 mL min−1 cm−2 volumetric flux of water with a modest 4.4 kPa head pressure. The scaffold is generated by freeze-casting a low-pH, concentrated silicic acid solution, followed by supercritical drying (SCD), changing the way water glass is used to generate support substrates. The scaffold enables facile immobilization of molecules or nanoparticles for liquid-phase applications, including heterogeneous catalysis, separations, biomedical devices, and energy storage.more » « less
-
Fabricating mechanically robust graphene aerogels (GAs) without compromising their notable features including superelasticity, large surface area, high porosity, and low density is challenging. This work presents a new one-pot strategy based on ambient drying to fabricate a three-dimensional (3D) graphene-polyethylene aerogel (G-PEA) with a unique hierarchical porous structure, in which the highly porous polyethylene is encapsulated by graphene frameworks. The hierarchical G-PEA exhibited substantially enhanced compressive strength while maintaining low density and superelasticity comparable to those of bare GAs. The G-PEAs with 5 wt.% PE (G-PEA5) showed a significant improvement (up to 2083%) in compressive stress compared to bare GAs, which can be attributed to the porous PE support within the GA framework. The G-PEA5 retained 94% of its compressive stress after 100 compression cycles, which is still higher than that (~80%) of bare GAs, and maintained good elastic recovery. The designed hierarchical G-PEAs show great promise in the applications that require outstanding mechanical properties.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/D2RA03325A