skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: The role of solid solutions in iron phosphate-based electrodes for selective electrochemical lithium extraction
Abstract Electrochemical intercalation can enable lithium extraction from dilute water sources. However, during extraction, co-intercalation of lithium and sodium ions occurs, and the response of host materials to this process is not fully understood. This aspect limits the rational materials designs for improving lithium extraction. Here, to address this knowledge gap, we report one-dimensional (1D) olivine iron phosphate (FePO 4 ) as a model host to investigate the co-intercalation behavior and demonstrate the control of lithium selectivity through intercalation kinetic manipulations. Via computational and experimental investigations, we show that lithium and sodium tend to phase separate in the host. Exploiting this mechanism, we increase the sodium-ion intercalation energy barrier by using partially filled 1D lithium channels via non-equilibrium solid-solution lithium seeding or remnant lithium in the solid-solution phases. The lithium selectivity enhancement after seeding shows a strong correlation with the fractions of solid-solution phases with high lithium content (i.e., Li x FePO 4 with 0.5 ≤ x < 1). Finally, we also demonstrate that the solid-solution formation pathway depends on the host material’s particle morphology, size and defect content.  more » « less
Award ID(s):
2011854
PAR ID:
10400735
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ;
Date Published:
Journal Name:
Nature Communications
Volume:
13
Issue:
1
ISSN:
2041-1723
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; ; et al (, Nature Communications)
    Abstract One-dimensional (1D) olivine iron phosphate (FePO4) is widely proposed for electrochemical lithium (Li) extraction from dilute water sources, however, significant variations in Li selectivity were observed for particles with different physical attributes. Understanding how particle features influence Li and sodium (Na) co-intercalation is crucial for system design and enhancing Li selectivity. Here, we investigate a series of FePO4particles with various features and revealed the importance of harnessing kinetic and chemo-mechanical barrier difference between lithiation and sodiation to promote selectivity. The thermodynamic preference of FePO4provides baseline of selectivity while the particle features are critical to induce different kinetic pathways and barriers, resulting in different Li to Na selectivity from 6.2 × 102to 2.3 × 104. Importantly, we categorize the FePO4particles into two groups based on their distinctly paired phase evolutions upon lithiation and sodiation, and generate quantitative correlation maps among Li preference, morphological features, and electrochemical properties. By selecting FePO4particles with specific features, we demonstrate fast (636 mA/g) Li extraction from a high Li source (1: 100 Li to Na) with (96.6 ± 0.2)% purity, and high selectivity (2.3 × 104) from a low Li source (1: 1000 Li to Na) with (95.8 ± 0.3)% purity in a single step. 
    more » « less
  2. ; ; ; ; (, Proceedings of the National Academy of Sciences)
    The lithium supply issue mainly lies in the inability of current mining methods to access lithium sources of dilute concentrations and complex chemistry. Electrochemical intercalation has emerged as a highly selective method for lithium extraction; however, limited source compositions have been studied, which is insufficient to predict its applicability to the wide range of unconventional water sources (UWS). This work addresses the feasibility and identifies the challenges of Li extraction by electrochemical intercalation from UWS, by answering three questions: 1) Is there enough Li in UWS? 2) How would the solution compositions affect the competition of Li + to major ions (Na + /Mg 2+ /K + /Ca 2+ )? 3) Does the complex solution composition affect the electrode stability? Using one-dimensional olivine FePO 4 as the model electrode, we show the complicated roles of major ions. Na + acts as the competitor ion for host storage sites. The competition from Na + grants Mg 2+ and Ca 2+ being only the spectator ions. However, Mg 2+ and Ca 2+ can significantly affect the charge transfer of Li + and Na + , therefore affecting the Li selectivity. We point to improving the selectivity of Li + to Na + as the key challenge for broadening the minable UWS using the olivine host. 
    more » « less
  3. ; ; ; (, RSC Advances)
    Capacitive deionization (CDI) is an energy saving and environmentally friendly technology for water desalination. However, classical CDI is challenged by a low salt removal capacity. To improve the desalination capacity, electrode materials utilizing the battery mechanism for salt ion removal have emerged as a new direction more recently. In this work, we report a study of amorphous iron phosphate (FePO 4 ) as a promising electrode material for pseudocapacitive sodium ion removal. Sodium ions can be effectively, reversibly intercalated and de-intercalated upon its electrochemical reduction and oxidation, with an excellent sodium ion capacity under half-cell testing conditions. By assembling a hybrid CDI (HCDI) system utilizing the FePO 4 electrode for pseudocapacitive sodium ion removal and active carbon electrode for capacitive chloride ion removal, the cell exhibited a high salt removal capacity and good reversibility and durability, which was attributed to the advantageous features of amorphous FePO 4 . The HCDI system achieved a high deionization capacity (82 mg g −1 ) in 10 mM NaCl, a fast deionization rate (0.046 mg g −1 s −1 ), and good stability and cyclability. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, Chemistry of Materials)
    Recent research has demonstrated the potential for topological superconductivity, anisotropic Majorana bound states, optical nonlinearity, and enhanced electrochemical activity for transition metal dichalcogenides (TMDs) with a 2M structure. These unique TMD compounds exhibit metastability and, upon heating, undergo a transition to the thermodynamically stable 2H phase. The 2M phase is commonly made at high temperatures using traditional solid-state methods, and this metastability further complicates the growth of large 2M WS2 crystals. Herein, a novel synthetic method was developed, focusing on a molten salt reaction to synthesize large 2H crystals and then inducing transformation to the 2M phase through intercalation and thermal treatment. The 2H crystals were intercalated via a room-temperature sodium naphthalenide solution, producing a previously unreported Na-intercalated 2H WS2 phase. Thermal heating was required to facilitate the phase transition to the intercalated 2M crystal structure. This phase transition was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), electron dispersive X-ray spectroscopy (EDS), and Raman spectroscopy, which confirmed the synthesis of the intercalated 2M phase. Upon deintercalation, crystal and powder samples showed superconductivity with a Tc of 8.6–8.7 K, similar to previously reported values. The generality of this process was further demonstrated using alkali metal triethyl borohydride to intercalate 2H WS2 and produced the desired 2M phase. This novel synthetic method has broad implications for discovering metastable phases in other TMD families and layered materials. Separation of the intercalation and phase transition also has the potential to allow for large-scale synthesis of this technologically important phase with greater control over each step of the reaction. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Energy Materials)
    Abstract Structural and ion‐ordering phase transitions limit the viability of sodium‐ion intercalation materials in grid scale battery storage by reducing their lifetime. However, the combination of phenomena in nanoparticulate electrodes creates complex behavior that is difficult to investigate, especially on the single‐nanoparticle scale under operating conditions. In this work, operando single‐particle X‐ray diffraction (oSP‐XRD) is used to observe single‐particle rotation, interlayer spacing, and layer misorientation in a functional sodium‐ion battery. oSP‐XRD is applied to Na2/3[Ni1/3Mn2/3]O2, an archetypal P2‐type sodium‐ion‐positive electrode material with the notorious P2‐O2 phase transition induced by sodium (de)intercalation. It is found that during sodium extraction, the misorientation of crystalline layers inside individual particles increases before the layers suddenly align just prior to the P2‐O2 transition. The increase in the long‐range order coincides with an additional voltage plateau signifying a phase transition prior to the P2‐O2 transition. To explain the layer alignment, a model for the phase evolution is proposed that includes a transition from localized to correlated Jahn–Teller distortions. The model is anticipated to guide further characterization and engineering of sodium‐ion intercalation materials with P2‐O2 type transitions. oSP‐XRD, therefore, opens a powerful avenue for revealing complex phase behavior in heterogeneous nanoparticulate systems. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email