The traditional von Neumann architecture limits the increase in computing efficiency and results in massive power consumption in modern computers due to the separation of storage and processing units. The novel neuromorphic computation system, an in-memory computing architecture with low power consumption, is aimed to break the bottleneck and meet the needs of the next generation of artificial intelligence (AI) systems. Thus, it is urgent to find a memory technology to implement the neuromorphic computing nanosystem. Nowadays, the silicon-based flash memory dominates non-volatile memory market, however, it is facing challenging issues to achieve the requirements of future data storage device development due to the drawbacks, such as scaling issue, relatively slow operation speed, and high voltage for program/erase operations. The emerging resistive random-access memory (RRAM) has prompted extensive research as its simple two-terminal structure, including top electrode (TE) layer, bottom electrode (BE) layer, and an intermediate resistive switching (RS) layer. It can utilize a temporary and reversible dielectric breakdown to cause the RS phenomenon between the high resistance state (HRS) and the low resistance state (LRS). RRAM is expected to outperform conventional memory device with the advantages, notably its low-voltage operation, short programming time, great cyclic stability, and good scalability. Among the materials for RS layer, indium gallium zinc oxide (IGZO) has shown attractive prospects in abundance and high atomic diffusion property of oxygen atoms, transparency. Additionally, its electrical properties can be easily modulated by controlling the stoichiometric ratio of indium and gallium as well as oxygen potential in the sputter gas. Moreover, since the IGZO can be applied to both the thin-film transistor (TFT) channel and RS layer, it has a great potential for fully integrated transparent electronics application. In this work, we proposed amorphous transparent IGZO-based RRAMs and investigated switching behaviors of the memory cells prepared with different top electrodes. First, ITO was choosing to serve as both TE and BE to achieve high transmittance. A multi-target magnetron sputtering system was employed to deposit all three layers (TE, RS, BE layers) on glass substrate. I-V characteristics were evaluated by a semiconductor parameter analyzer, and the bipolar RS feature of our RRAM devices was demonstrated by typical butterfly curves. The optical transmission analysis was carried out via a UV-Vis spectrometer and the average transmittance was around 80% out of entire devices in the visible-light wavelength range, implying high transparency. We adjusted the oxygen partial pressure during the sputtering of IGZO to optimize the property because the oxygen vacancy concentration governs the RS performance. Electrode selection is crucial and can impact the performance of the whole device. Thus, Cu TE was chosen for our second type of device because the diffusion of Cu ions can be beneficial for the formation of the conductive filament (CF). A ~5 nm SiO 2 barrier layer was employed between TE and RS layers to confine the diffusion of Cu into the RS layer. At the same time, this SiO 2 inserting layer can provide an additional interfacial series resistance in the device to lower the off current, consequently, improve the on/off ratio and whole performance. Finally, an oxygen affinity metal Ti was selected as the TE for our third type of device because the concentration of the oxygen atoms can be shifted towards the Ti electrode, which provides an oxygengettering activity near the Ti metal. This process may in turn lead to the formation of a sub-stoichiometric region in the neighboring oxide that is believed to be the origin of better performance. In conclusion, the transparent amorphous IGZO-based RRAMs were established. To tune the property of RS layer, the sputtering conditions of RS were varied. To investigate the influence of TE selections on switching performance of RRAMs, we integrated a set of TE materials, and a barrier layer on IGZO-based RRAM and compared the switch characteristics. Our encouraging results clearly demonstrate that IGZO is a promising material in RRAM applications and breaking the bottleneck of current memory technologies.
more »
« less
Cryogenic Storage Memory with High‐Speed, Low‐Power, and Long‐Retention Performance
Abstract Cryogenic‐computing draws attention due to its variety of applications such as cloud‐computing, aerospace electronics, and quantum computing. Low temperature (e.g., 77 K) enables higher switching speed, improved reliability, and suppressed noise. Although cryogenic dynamic random‐access memory is studied, the cryogenic NAND flash is not explored intensively. Herein, a cryogenic storage memory based on the charge‐trap mechanism is reported. By removing the tunneling oxide from the conventional silicon/oxide/nitride/oxide/silicon (SONOS)‐type flash memory (therefore becoming silicon/oxide/nitride/silicon (SONS)), high‐speed and low‐power operation is aimed to be achieved while relieved from poor retention issue thanks to the cryogenic environment. The FinFET‐structured SONS memory device is demonstrated experimentally with gate length of 20–30 nm, which can achieve the retention issue (>10 years) with low voltage (≈6.5 V) and high speed (≈5 µs) operation at 77 K. To have a holistic system‐level evaluation, benchmark simulation of an interface between a host microprocessor and solid‐state‐drive is conducted, considering the refrigerator cooling cost and the heat loss via cables across two temperatures (300 and 77 K). The results show that the SONS‐type cryogenic storage system shows over 81% improvement in both latency and power, compared to the SONOS counterpart located at cryogenics.
more »
« less
- Award ID(s):
- 2218604
- PAR ID:
- 10406911
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- Volume:
- 9
- Issue:
- 6
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Computational storage adds computing to storage devices, providing potential benefits in offload, data-reduction, and lower energy. Successful computational SSD architectures should match growing flash bandwidth, which in turn requires high SSD DRAM memory bandwidth. This creates a memory wall scaling problem, resulting from SSDs’ stringent power and cost constraints. A survey of recent computational SSD research shows that many computational storage offloads are suited to stream computing. To exploit this opportunity, we propose a novel general-purpose computational SSD and core architecture, called ASSASIN (Architecture Support for Stream computing to Accelerate computatIoNal Storage). ASSASIN provides a unified set of compute engines between SSD DRAM and the flash array. This eliminates the SSD DRAM bottleneck by enabling direct computing on flash data streams. ASSASIN further employs a crossbar to achieve performance even when flash data layout is uneven and preserve independence for page layout decisions in the flash translation layer. With stream buffers and scratchpad memories, ASSASIN core’s memory hierarchy and instruction set extensions provide superior low-latency access at low-power and effectively keep streaming flash data out of the in-SSD cache-DRAM memory hierarchy, thereby solving the memory wall. Evaluation shows that ASSASIN delivers 1.5x - 2.4x speedup for offloaded functions compared to state-of-the-art computational SSD architectures. Further, ASSASIN’s streaming approach yields 2.0x power efficiency and 3.2x area efficiency improvement. And these performance benefits at the level of computational SSDs translate to 1.1x - 1.5x end-to-end speedups on data analytics workloads.more » « less
-
Abstract Memristors have emerged as transformative devices to enable neuromorphic and in‐memory computing, where success requires the identification and development of materials that can overcome challenges in retention and device variability. Here, high‐entropy oxide composed of Zr, Hf, Nb, Ta, Mo, and W oxides is first demonstrated as a switching material for valence change memory. This multielement oxide material provides uniform distribution and higher concentration of oxygen vacancies, limiting the stochastic behavior in resistive switching. (Zr, Hf, Nb, Ta, Mo, W) high‐entropy‐oxide‐based memristors manifest the “cocktail effect,” exhibiting comparable retention with HfO2‐ or Ta2O5‐based memristors while also demonstrating the gradual conductance modulation observed in WO3‐based memristors. The electrical characterization of these high‐entropy‐oxide‐based memristors demonstrates forming‐free operation, low device and cycle variability, gradual conductance modulation, 6‐bit operation, and long retention which are promising for neuromorphic applications.more » « less
-
The major focus of artificial intelligence (AI) research is made on biomimetic synaptic processes that are mimicked by functional memory devices in the computer industry [1]. It is urgent to find a memory technology for suiting with Brain-Inspired Computing to break the von Neumann bottleneck which limits the efficiency of conventional computer architectures [2]. Silicon-based flash memory, which currently dominates the market for data storage devices, is facing challenging issues to meet the needs of future data storage device development due to the limitations, such as high-power consumption, high operation voltage, and low retention capacity [1]. The emerging resistive random-access memory (RRAM) has elicited intense research as its simple sandwiched structure, including top electrode (TE) layer, bottom electrode (BE) layer, and an intermediate resistive switching (RS) layer, can store data using RS phenomenon between the high resistance state (HRS) and the low resistance state (LRS). This class of emerging devices is expected to outperform conventional memory devices [3]. Specifically, the advantages of RRAM include low-voltage operation, short programming time, great cyclic stability, and good scalability [4]. Among the materials for RS layer, indium gallium zinc oxide (IGZO) has attracted attention because of its abundance and high atomic diffusion property of oxygen atoms, transparency, and its easily modulated electrical properties by controlling the stoichiometric ratio of indium and gallium as well as oxygen potential in the sputter gas [5, 6]. Moreover, since the IGZO can be applied to both the thin-film transistor (TFT) channel and RS layer, the IGZO-based fully integrated transparent electronics are very promising [5]. In this work, we proposed transparent IGZO-based RRAMs. First, we chose ITO to serve as both TE and BE to achieve high transmittance in the visible regime of light. All three layers (TE, RS, BE layers) were deposited using a multi-target magnetron sputtering system on glass substrates to demonstrate fully transparent oxide-based devices. I-V characteristics were evaluated by a semiconductor parameter analyzer, and our devices showed typical butterfly curves indicating the bipolar RS property. And the IGZO-based RRAM can survive more than 50 continuous sweeping cycles. The optical transmission analysis was carried out via an UV-Vis spectrometer and the average transmittance around 80% out of entire devices in the visible-light wavelength range, implying high transparency. To investigate the thickness dependence on the properties of RS layer, 50nm, 100nm and 150nm RS layer of IGZO RRAM were fabricated. Also, the oxygen partial pressure during the sputtering of IGZO was varied to optimize the property because the oxygen vacancy concentration governs the RS and RRAM performance. Electrode selection is crucial and can impact the performance of the whole device [7]. Thus, Cu TE was chosen for our second type of device because the diffusion of Cu ions can be beneficial for the formation the conductive filament (CF). Finally, a ~5 nm SiO2 barrier layer was employed between TE and RS layers to confine the diffusion of Cu into the RS layer. At the same time, this SiO2 inserting layer can provide an additional interfacial series resistance in the device to lower the off current, consequently, improve the on/off ratio and whole performance. In conclusion, the transparent IGZO-based RRAMs were established. To tune the property of RS layer, the thickness layer and sputtering conditions of RS were adjusted. In order to engineer the diffusion capability of the TE material to the RS layer and the BE, a set of TE materials and a barrier layer were integrated in IGZO-based RRAM and the performance was compared. Our encouraging results clearly demonstrate that IGZO is a promising material in RRAM applications and overcoming the bottleneck of current memory technologies.more » « less
-
Abstract Recent advances in photonic integrated circuits have enabled a new generation of programmable Mach–Zehnder meshes (MZMs) realized by using cascaded Mach–Zehnder interferometers capable of universal linear-optical transformations onNinput/output optical modes. MZMs serve critical functions in photonic quantum information processing, quantum-enhanced sensor networks, machine learning and other applications. However, MZM implementations reported to date rely on thermo-optic phase shifters, which limit applications due to slow response times and high power consumption. Here we introduce a large-scale MZM platform made in a 200 mm complementary metal–oxide–semiconductor foundry, which uses aluminium nitride piezo-optomechanical actuators coupled to silicon nitride waveguides, enabling low-loss propagation with phase modulation at greater than 100 MHz in the visible–near-infrared wavelengths. Moreover, the vanishingly low hold-power consumption of the piezo-actuators enables these photonic integrated circuits to operate at cryogenic temperatures, paving the way for a fully integrated device architecture for a range of quantum applications.more » « less