skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Step‐by‐Step Guide for Synthesis and Delamination of Ti 3 C 2 T x MXene
Abstract To advance the MXene field, it is crucial to optimize each step of the synthesis process and create a detailed, systematic guide for synthesizing high‐quality MXene that can be consistently reproduced. In this study, a detailed guide is provided for an optimized synthesis of titanium carbide (Ti3C2Tx) MXene using a mixture of hydrofluoric and hydrochloric acids for the selective etching of the stoichimetric‐Ti3AlC2MAX phase and delamination of the etched multilayered Ti3C2TxMXene using lithium chloride at 65 °C for 1 h with argon bubbling. The effect of different synthesis variables is investigated, including the stoichiometry of the mixed powders to synthesize Ti3AlC2, pre‐etch impurity removal conditions, selective etching, storage, and drying of MXene multilayer powder, and the subsequent delamination conditions. The synthesis yield and the MXene film electrical conductivity are used as the two parameters to evaluate the MXene quality. Also the MXenes are characterized with scanning electron microscopy, x‐ray diffraction, atomic force microscopy, and ellipsometry. The Ti3C2Txfilm made via the optimized method shows electrical conductivity as high as ≈21,000 S/cm with a synthesis yield of up to 38 %. A detailed protocol is also provided for the Ti3C2TxMXene synthesis as the supporting information for this study.  more » « less
Award ID(s):
1950672
PAR ID:
10419157
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Small Methods
Volume:
7
Issue:
8
ISSN:
2366-9608
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; ; et al (, RSC Advances)
    null (Ed.)
    Quaternary MAX phases, (Ta 1−x Ti x ) 3 AlC 2 ( x = 0.4, 0.62, 0.75, 0.91 or 0.95), have been synthesised via pressureless sintering of TaC, TiC, Ti and Al powders. Via chemical etching of the Al layers, (Ta 0.38 Ti 0.62 ) 3 C 2 T z – a new MXene, has also been synthesised. All materials contain an M-layer solid solution of Ta and Ti, with a variable Ta concentration, paving the way for the synthesis of a range of alloyed (Ta,Ti) 3 C 2 T z MXenes with tuneable compositions for a wide range of potential applications. 
    more » « less
  2. ; ; ; ; ; ; (, Materials Advances)
    Thein situHF acid etching of Ti3AlC2yielded multilayered Ti3C2. Sonication delaminated nanosheets, suspended in DI water, post rheological optimization 3D printed using DIW platform to produce conductive patterns of MXene. 
    more » « less
  3. ; (, Advanced Composites and Hybrid Materials)
    Abstract Ti3C2Tx(MXenes) are novel 2D nanomaterials with exceptional electrical conductivity. Their surfaces are covered with functional groups that may significantly affect material properties such as hydrophobicity, electrical conductivity, and oxidation resistance. The role of these terminations in high-temperature ceramic systems with regard to phase and microstructural evolution has not been investigated. In this study, Ti3C2Tx-SiOC 2D nanocomposites were fabricated with -F and -OH terminated MXene to evaluate the role of surface terminations in silane coupling and phase formation during the polymer-to-ceramic transformation. X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and X-ray photoelectron spectroscopy (XPS) identified self-etching mechanisms caused by F-terminated Ti3C2Txand revealed that the F surface terminations were retained in the MXene structure until evolution at ~ 550 °C. Evolved F reacted with Si–H bonds in the transforming ceramic matrix, causing additional mass loss and volumetric deformation. LiOH alkalization was shown to suppress the self-etching phenomenon through the substitution of F groups with OH on the nanosheet surface. Furthermore, F terminations were determined to only engage in hydrogen bonding with silane molecules as opposed to covalent linkages with OH terminations, which accelerated silane removal and Ti3C2Txdegradation. The study provides a fundamental understanding of the nature and behavior of MXene surface terminations in the context of high-temperature ceramic nanocomposite fabrication. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; (, 2D Materials)
    Abstract Porous MXene-polymer composites have gained attention due to their low density, large surface area, and high electrical conductivity, which can be used in applications such as electromagnetic interference shielding, sensing, energy storage, and catalysis. High internal phase emulsions (HIPEs) can be used to template the synthesis of porous polymer structures, and when solid particles are used as the interfacial agent, composites with pores lined with the particles can be realized. Here, we report a simple and scalable method to prepare conductive porous MXene/polyacrylamide structures via polymerization of the continuous phase in oil/water HIPEs. The HIPEs are stabilized by salt flocculated Ti 3 C 2 T x nanosheets, without the use of a co-surfactant. After polymerization, the polyHIPE structure consists of porous polymer struts and pores lined with Ti 3 C 2 T x nanosheets, as confirmed by scanning electron microscopy, energy dispersive x-ray spectroscopy, and x-ray photoelectron spectroscopy. The pore size can be tuned by varying the Ti 3 C 2 T x concentration, and the interconnected Ti 3 C 2 T x network allows for electrical percolation at low Ti 3 C 2 T x loading; further, the electrical conductivity is stable for months indicating that in these composites, the nanosheets are stable to oxidation at ambient conditions. The polyHIPEs also exhibit rapid radio frequency heating at low power (10 °C s −1 at 1 W). This work demonstrates a simple approach to accessing electrically conductive porous MXene/polymer composites with tunable pore morphology and good oxidation stability of the nanosheets. 
    more » « less
  5. ; ; ; ; ; ; ; (, Journal of Materials Chemistry C)
    Transition metal carbides (MXenes) are an emerging family of highly conductive two-dimensional materials with additional functional properties introduced by surface terminations. Further modification of the surface terminations makes MXenes even more appealing for practical applications. Herein, we report a facile and environmentally benign synthesis of reduced Ti 3 C 2 T x MXene (r-Ti 3 C 2 T x ) via a simple treatment with l -ascorbic acid at room temperature. r-Ti 3 C 2 T x shows a six-fold increase in electrical conductivity, from 471 ± 49 for regular Ti 3 C 2 T x to 2819 ± 306 S m −1 for the reduced version. Additionally, we show an enhanced oxidation stability of r-Ti 3 C 2 T x as compared to regular Ti 3 C 2 T x . An examination of the surface-enhanced Raman scattering (SERS) activity reveals that the SERS enhancement factor of r-Ti 3 C 2 T x is an order of magnitude higher than that of regular Ti 3 C 2 T x . The improved SERS activity of r-Ti 3 C 2 T x is attributed to the charge transfer interaction between the MXene surface and probe molecules, re-enforced by an increased electronic density of states (DOS) at the Fermi level of r-Ti 3 C 2 T x . The findings of this study suggest that reduced MXene could be a superior choice over regular MXene, especially for the applications that employ high electronic conductivity, such as electrode materials for batteries and supercapacitors, photodetectors, and SERS-based sensors. 
    more » « less