We have carried out a combined theoretical and experimental investigation of both stoichiometric and nonstoichiometric CoFeVGe alloys. In particular, we have investigated CoFeVGe, Co 1.25 Fe 0.75 VGe, Co 0.75 Fe 1.25 VGe, and CoFe 0.75 VGe bulk alloys. Our first principles calculations suggest that all four alloys show ferromagnetic order, where CoFeVGe, Co 1.25 Fe 0.75 VGe, and Co 0.75 Fe 1.25 VGe are highly spin polarized with spin polarization values of over 80%. However, the spin polarization value of CoFe 0.75 VGe is only about 60%. We have synthesized all four samples using arc melting and high-vacuum annealing at 600 °C for 48 hours. The room temperature x-ray diffraction of these samples exhibits a cubic crystal structure with disorder. All the samples show single magnetic transitions at their Curie temperatures, where the Curie temperature and high field (3T) magnetization are 288 K and 42 emu/g; 305 K and 1.5 emu/g; 238 K and 39 emu/g; and 306 K and 35 emu/g for CoFeVGe, Co 1.25 Fe 0.75 VGe, Co 0.75 Fe 1.25 VGe, and CoFe 0.75 VGe, respectively.
more »
« less
Synthesis, crystal structure, and magnetic properties of CoMoFeAl and related compounds
We have carried out joint theoretical and experimental investigations of three Heusler compounds CoMoFeAl, CoMo 0.5 Fe 1.5 Al, and Co 1.5 Mo 0.5 FeAl. Our first-principle calculations show that all three compounds show either ferro- or ferrimagnetic order with CoMoFeAl and CoMo 0.5 Fe 1.5 Al exhibiting high spin polarization of almost 80%. The investigated samples were prepared using arc melting and high vacuum annealing. All the samples show cubic crystal structure with disorder. The parent compound CoMoFeAl shows a small saturation magnetization of 12 emu/g, and a Curie temperature of 440 K. The other two compounds, namely, Co 1.5 Mo 0.5 FeAl and CoMo 0.5 Fe 1.5 Al, show much higher saturation magnetizations of 62 emu/g and 59 emu/g, and substantially higher Curie temperatures of 950 K and 780 K, respectively.
more »
« less
- Award ID(s):
- 2003828
- NSF-PAR ID:
- 10421909
- Date Published:
- Journal Name:
- AIP Advances
- Volume:
- 13
- Issue:
- 2
- ISSN:
- 2158-3226
- Page Range / eLocation ID:
- 025213
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract We have carried out a combined theoretical and experimental investigation of FeCrVAl, and the effect of Mn and Co doping on its structural, magnetic, and electronic band properties. Our first principles calculations indicate that FeCrVAl, FeCr 0.5 Mn 0.5 VAl, and FeCr 0.5 Co 0.5 VAl exhibit nearly perfect spin polarization, which may be further enhanced by mechanical strain. At the same time, FeCrV 0.5 Mn 0.5 Al and FeCrV 0.5 Co 0.5 Al exhibit a relatively small value of spin polarization, making them less attractive for practical applications. Using arc melting and high vacuum annealing, we synthesized three compounds FeCrVAl, FeCr 0.5 Mn 0.5 VAl, and FeCr 0.5 Co 0.5 VAl, which are predicted to exhibit high spin polarization. The room temperature x-ray diffraction patterns of all samples are fitted with full B2 type disorder with a small amount of FeO 2 secondary phase. All samples show very small saturation magnetizations at room temperature. The thermomagnetic curves M(T) of FeCrVAl and FeCr 0.5 Co 0.5 VAl are similar to that of a paramagnetic material, whereas that of FeCr 0.5 Mn 0.5 VAl indicates ferrimagnetic behavior with the Curie temperature of 135 K. Our findings may be of interest for researchers working on Heusler compounds for spin-based electronic applications.more » « less
-
more » « less
First-principles calculations were performed to calculate the electronic structures of low temperature phase (LTP) MnBi (Mn50Bi50) and substitutionally and interstitially Sn-doped MnBi [Mn50Bi25Sn25, (Mn0.5Bi0.5)66.7Sn33.3]. Brillouin function predicts the temperature dependence of saturation magnetization M(T). Sn substitution for Bi in MnBi (Mn50Bi25Sn25) changes the magnetocrystalline anisotropy constant (Ku) from −0.202 MJ/m3 (the in-plane magnetization) for LTP MnBi to 1.711 MJ/m3 (the out-of-plane magnetization). In comparison, the Ku remains negative but slightly decreases to −0.043 MJ/m3 when Sn is interstitially doped in MnBi [(Mn0.5Bi0.5)66.7Sn33.3]. The Curie temperature (TC) decreases from 716 K for LTP Mn50Bi50 to 445 K for Mn50Bi25Sn25 and 285 K for (Mn0.5Bi0.5)66.7Sn33.3. Mn50Bi25Sn25 has a lower magnetic moment of 5.034 μB/f.u. but a higher saturation magnetization of 64.2 emu/g than (Mn0.5Bi0.5)66.7Sn33.3 with a magnetic moment of 6.609 μB/f.u. and a saturation magnetization of 48.2 emu/g because the weight and volume of the substitutionally Sn-doped MnBi are smaller than the interstitially Sn-doped MnBi. The low Curie temperature and magnetization for Sn-doped MnBi are attributed to the high concentration of Sn. Thus, future study needs to focus on low Sn-concentrated MnBi.
-
Half-metallic Heusler alloys have attracted significant attention due to their potential application in spin-transport-based devices. We have synthesized one such alloy, CoFeV 0.5 Mn 0.5 Si, using arc melting and high-vacuum annealing at 600 °C for 24 hours. First principles calculation indicates that CoFeV 0.5 Mn 0.5 Si shows a nearly half-metallic band structure with a degree of spin polarization of about 93%. In addition, this value can be enhanced by the application of tensile strain. The room temperature x-ray diffraction patterns are indexed with the cubic crystal structure without secondary phases. The annealed sample shows ferromagnetic order with the Curie temperature well above room temperature ( T c = 657 K) and a saturation magnetization of about 92 emu/g. Our results indicate that CoFeV 0.5 Mn 0.5 Si has a potential for room temperature spin-transport-based devices.more » « less
-
New magnetic materials for energy and information-processing applications are of paramount importance in view of significant global challenges in environmental and information security. The discovery and design of materials requires efficient computational and experimental approaches for high throughput and efficiency. When increasingly powerful computational techniques are combined with special non-equilibrium fabrication methods, the search can uncover metastable compounds with desired magnetic properties. Here we review recent results on novel Fe-, Co- and Mn-rich magnetic compounds with high magnetocrystalline anisotropy, saturation magnetization, and Curie temperature created by combining experiments, adaptive genetic algorithm searches, and advanced electronic-structure computational methods. We discuss structural and magnetic properties of such materials including Co– and/or Fe–X compounds (X = N, Si, Sn, Zr, Hf, Y, C, S, Ti, or Mn), and their prospects for practical applications.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1063/9.0000396