Title: Radial bimetallic structures via wire arc directed energy deposition-based additive manufacturing
Abstract

Bimetallic wire arc additive manufacturing (AM) has traditionally been limited to depositions characterized by single planar interfaces. This study demonstrates a more complex radial interface concept, with in situ mechanical interlocking and as-built properties suggesting a prestressed compressive effect. A 308 L stainless core is surrounded by a mild steel casing, incrementally maintaining the interface throughout the Z-direction. A small difference in the thermal expansion coefficient between these steels creates residual stresses at their interface. X-ray diffraction analysis confirms phase purity and microstructural characterization reveals columnar grain growth independent of layer transitions. Hardness values are consistent with thermal dissipation characteristics, and the compressive strength of the bimetallic structures shows a 33% to 42% improvement over monolithic controls. Our results demonstrate that biomimetic radial bimetallic variation is feasible with improved mechanical response over monolithic compositions, providing a basis for advanced structural design and implementation using arc-based metal AM.

 
more » « less
Award ID(s):
1934230
NSF-PAR ID:
10424896
Author(s) / Creator(s):
; ;
Publisher / Repository:
Nature Publishing Group
Date Published:
Journal Name:
Nature Communications
Volume:
14
Issue:
1
ISSN:
2041-1723
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Balancing strength and ductility is crucial for structural materials, yet often presents a paradoxical challenge. This research focuses on crafting a unique bimetallic structure, combining non-magnetic, stainless steel 316L (SS316L) with limited strength but enhanced ductility and magnetic, martensitic 17-4 PH with higher strength but lower ductility. Utilizing a powder-based laser-directed energy deposition (L-DED) system, two vertical bimetallic configurations (SS316L/17-4 PH) and a radial bimetallic structure (SS316L core encased in 17-4 PH) were fabricated. Monolithic SS316L, 17-4 PH, and a 50% SS316L/50% 17-4 PH mixture were printed. The printed samples' phase, microstructure, room temperature mechanical properties, and fracture morphology were examined in as-printed conditions. Bimetallic samples exhibited both phases, with a smooth grain transition at the interface. Radial bimetallic samples demonstrated higher mechanical strength than other compositions, except 17-4 PH. These findings showcase the potential of the L-DED approach for creating functional components with tailored mechanical properties. 
    more » « less
  2. null (Ed.)
    316L stainless steel (SS) to Al12Si aluminum alloy structures were processed, tailoring the compositionally graded interface on a SS 316 substrate using a directed energy deposition (DED)-based additive manufacturing (AM) process. Applying such a compositionally graded transition on bimetallic materials, especially joining two dissimilar metals, could avoid the mechanical property mismatch. This study's objective was to understand the processing parameters that influence the properties of AM processed SS 316L to Al12Si bimetallic structures. Two different approaches fabricated these bimetallic structures. The results showed no visible defects on the as-fabricated samples using 4 layers of Al-rich mixed composition as the transition section. The microstructural characterization showed a unique morphology in each section. Both cooling rate and compositional variations caused microstructural variation. FeAl, Fe2Al5, and FeAl3 intermetallic phases were formed at the compositionally graded transition section. After stress relief heat-treatment of SS 316L/Al12Si bimetallic samples, diffused intermetallic phases were seen at the compositionally graded transition. At the interface, as processed, bimetallic structures had a microhardness value of 834.2 ± 107.1 HV0.1, which is a result of the FeAl3 phase at the compositionally graded transition area. After heat-treatment, the microhardness value reduced to 578.7 ± 154.1 HV0.1 due to more Fe dominated FexAly phase formation. The compression test results showed that the non-HT and HT SS 316L/Al12Si bimetallic structures had a similar maximum compressive strength of 299.4 ± 22.1 MPa and 270.1 ± 27.1 MPa, respectively. 
    more » « less
  3. The demand for advanced materials has driven innovation in titanium alloy design, particularly in the aerospace, automotive, and biomedical sectors. Additive manufacturing (AM) enables the construction of multi-material structures, offering potential improvements in mechanical properties such as wear resistance and high-temperature capabilities, thus extending the service life of components such as Ti6Al4V. Directed energy deposition (DED)-based metal AM was used to manufacture radial multi-material structures with a Ti6Al4V (Ti64) core and a Ti6Al4V-5 wt.% B4C composite outer layer. X-ray diffraction analysis and microstructural observation suggest that distinct B4C particles are strongly attached to the Ti6Al4V matrix. The addition of B4C increased the average hardness from 313 HV for Ti6Al4V to 538 HV for the composites. The addition of 5 wt.% B4C in Ti6Al4V increased the average compressive yield strength (YS) to 1440 MPa from 972 MPa for the control Ti6Al4V, i.e., >48% increase without any significant change in the elastic modulus. The radial multi-material structures did not exhibit any changes in the compressive modulus compared to Ti6Al4V but displayed an increase in the average compressive YS to 1422 MPa, i.e., >45% higher compared to Ti6Al4V. Microstructural characterization revealed a smooth transition from the pure Ti6Al4V at the core to the Ti64-B4C composite outer layer. No interfacial failure was observed during compressive deformation, indicating a strong metallurgical bonding during multi-material radial composite processing. Our results demonstrated that a significant improvement in mechanical properties can be achieved in one AM build operation through designing innovative multi-material structures using DED-based AM.

     
    more » « less
  4. Directed energy deposition (DED)-based additive manufacturing (AM) was employed to fabricate three distinct bimetallic compositions to understand the role interface for the deformation behavior of bimetallic structures under compressive loading. Commercially pure titanium (CP Ti) with a hexagonal closed packed (HCP) structure, nickel (Ni) with a face-centered cubic (FCC), and tantalum (Ta) with a body-centered cubic (BCC) structure were selected to understand the deformation behavior within the pure metals and damage accumulation at the bimetallic interface. By incorporating the combination of these materials, such as Ni-Ti, Ni-Ta, and Ta-Ti, we aimed to manufacture layered-base polycrystalline composite structures with FCC-HCP, FCC-BCC, and BCC-HCP crystal unit cells, respectively. In Ni-Ti and Ni-Ta bimetallic structures, it was determined that deformation is controlled by the Ni region, where the highest deflection occurs when Ni bulges out and makes lateral stress at the interface, resulting in crack initiation, propagation, and failure of the structure. Structural edges were found to experience the highest deformation, prompting grain inclination towards the <111> crystal orientation, resulting in a favorable orientation for dislocation slip and a higher Taylor factor. However, strong interfacial bonding and similar Young's modulus between Ta and Ti altered the deformation mechanisms to twinning formation in the Ti region and observed buckling of the entire structure without significant failure at the interface. 
    more » « less
  5. The mechanical properties of bimetallic composites are significantly influenced by their interfacial morphologies. This study delves into the impact of various heat treatment conditions on the microstructure and mechanical attributes of steel/nickel bimetallic (17-4PH/IN625) components produced through extrusion-based sintering-assisted additive manufacturing (ES-AM). The bimetallic composites were annealed at 1150°C for 1, 4, and 8 h, followed by an aging treatment at 482°C for samples annealed for 8 h. After annealing, microstructural heterogeneities, including variations in grain size and elemental distribution within the transition zone close to the interface, were observed. It was found that in the diffusion transition zone between the two alloy layers, the diffusion of iron (Fe) and nickel (Ni) elements increased with longer holding times, as corroborated by microhardness tests and quantified through theoretical parabolic diffusion law. The transition zone exhibited two distinct areas: an Fe-predominant zone and a Ni-predominant zone, with the latter containing oxides and molybdenum (Mo)- and niobium (Nb)-rich precipitates. No new phases emerged post-heat treatment; however, shifts in peak due to stress relaxation and the emergence of precipitates were identified through X-ray diffraction (XRD) observations. Microhardness within the transition zone increased following heat treatment, peaking at 186 HV1.0 after a 4-h annealing. The optimal heat treatment condition was identified as 1150°C for 4 h, which facilitated the development of uniform microstructures and improved bonding strength. This study demonstrates an enhanced interfacial bonding strength in 17-4PH and IN625 bimetallic parts manufactured through ES-AM, suggesting their wide-ranging potential applications in industry.

     
    more » « less