skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Spatially Distributed Ramp Reversal Memory in VO 2
Abstract Ramp‐reversal memory has recently been discovered in several insulator‐to‐metal transition materials where a non‐volatile resistance change can be set by repeatedly driving the material partway through the transition. This study uses optical microscopy to track the location and internal structure of accumulated memory as a thin film of VO2is temperature cycled through multiple training subloops. These measurements reveal that the gain of insulator phase fraction between consecutive subloops occurs primarily through front propagation at the insulator‐metal boundaries. By analyzing transition temperature maps, it is found, surprisingly, that the memory is also stored deep inside both insulating and metallic clusters throughout the entire sample, making the metal‐insulator coexistence landscape more rugged. This non‐volatile memory is reset after heating the sample to higher temperatures, as expected. Diffusion of point defects is proposed to account for the observed memory writing and subsequent erasing over the entire sample surface. By spatially mapping the location and character of non‐volatile memory encoding in VO2, this study results enable the targeting of specific local regions in the film where the full insulator‐to‐metal resistivity change can be harnessed in order to maximize the working range of memory elements for conventional and neuromorphic computing applications.  more » « less
Award ID(s):
2006192
PAR ID:
10430944
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Electronic Materials
Volume:
9
Issue:
10
ISSN:
2199-160X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Physics Research)
    Abstract Mott insulator VO2exhibits an ultrafast and reversible semiconductor‐to‐metal transition (SMT) near 340 K (67 °C). In order to fulfill the multifunctional device applications, effective transition temperature (Tc) tuning as well as integrated functionality in VO2is desired. In this study, multifunctionalities including tailorable SMT characteristics, ferromagnetic (FM) integration, and magneto‐optical (MO) coupling, have been demonstrated via metal/VO2nanocomposite designs with controlled morphology, i.e., a two‐phase Ni/VO2pillar‐in‐matrix geometry and a three‐phase Au/Ni/VO2particle‐in‐matrix geometry. EvidentTcreduction of 20.4 to 54.9 K has been achieved by morphology engineering. Interestingly, the Au/Ni/VO2film achieves a record‐lowTcof 295.2 K (22.2 °C), slightly below room temperature (25 °C). The change in film morphology is also correlated with unique property tuning. Highly anisotropic magnetic and optical properties have been demonstrated in Ni/VO2film, whereas Au/Ni/VO2film exhibits isotropic properties because of the uniform distribution of Au/Ni nanoparticles. Furthermore, a strong MO coupling with enhanced magnetic coercivity and anisotropy is demonstrated for both films, indicating great potential for optically active property tuning. This demonstration opens exciting opportunities for the VO2‐based device implementation towards smart windows, next‐generation optical‐coupled switches, and spintronic devices. 
    more » « less
  2. ; ; ; ; ; (, Advanced Materials Interfaces)
    Abstract Straining the vanadium dimers along the rutilec‐axis can be used to tune the metal‐to‐insulator transition (MIT) of VO2but has thus far been limited to TiO2substrates. In this work VO2/MgF2epitaxial films are grown via molecular beam epitaxy (MBE) to strain engineer the transition temperature (TMIT). First, growth parameters are optimized by varying the synthesis temperature of the MgF2(001) substrate (TS) using a combination of X‐ray diffraction techniques, temperature dependent transport, and soft X‐ray photoelectron spectroscopy. It is determined thatTSvalues greater than 350 °C induce Mg and F interdiffusion and ultimately the relaxation of the VO2layer. Using the optimized growth temperature, VO2/MgF2(101) and (110) films are then synthesized. The three film orientations display MITs with transition temperatures in the range of 15–60 °C through precise strain engineering. 
    more » « less
  3. ; ; ; ; ; ; ; (, Optical Materials Express)
    We study the ultrafast time resolved response of 30 nm films of VO2on a TiO2substrate when 3.1 eV (400 nm wavelength) pump pulses were used to excite the insulator to metal transition (IMT). We found that the IMT threshold for these samples (≤30µJ/cm2) is more than 3 orders of magnitude lower than that generally reported for a more traditional 1.55 eV (800 nm wavelength) excitation. The samples also exhibited unusual reflectivity dynamics at near-threshold values of pump fluence where their fractional relative reflectivity ΔR/R initially increased before becoming negative after several hundreds of picoseconds, in stark contrast with uniformly negative ΔR/R observed for both higher 400 nm pump fluences and for 800 nm pump pulses. We explain the observed behavior by the interference of the reflected probe beam from the inhomogeneous layers formed inside the film by different phases of VO2and use a simple diffusion model of the VO2phase transition to support qualitatively this hypothesis. We also compare the characteristics of the VO2films grown on undoped TiO2and on doped TiO2:Nb substrates and observe more pronounced reflectivity variation during IMT and faster relaxation to the insulating state for the VO2/TiO2:Nb sample. 
    more » « less
  4. ; ; ; ; ; ; (, Advanced Electronic Materials)
    Abstract The characteristic metal–insulator phase transition (MIT) in vanadium dioxide results in nonlinear electrical transport behavior, allowing VO2devices to imitate the complex functions of neurological behavior. Chemical doping is an established method for varying the properties of the MIT, and interstitial dopant boron has been shown to generate a unique dynamic relaxation effect in individual B‐VO2particles. This paper describes the first demonstration of an electrically stimulated B‐VO2proto‐device which manifests a time‐dependent critical transformation temperature and switching voltage derived from the coupling of dopant diffusion dynamics and the metal–insulator transition of VO2. During quasi‐steady current‐driven transitions, the electrical responses of B‐VO2proto‐devices show a step‐by‐step progression through the phase transformation, evidencing domain transformations within individual particles. The dynamic relaxation effect is shown to increase the critical switching voltage by up to 41% (ΔVcrit =0.13 V) and also to increase the resistivity of the M1 phase of B‐VO2by 14%, imbuing a memristive response derived from intrinsic material properties. These observations demonstrate the dynamic relaxation effect in B‐VO2proto‐devices whose electrical transport responses can be adjusted by electronic phase transitions triggered by temperature but also by time as a result of intrinsic dynamics of interstitial dopants. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Functional Materials)
    Abstract Vanadium dioxide (VO2) is a well‐studied Mott‐insulator because of the very abrupt physical property switching during its semiconductor‐to‐metal transition (SMT) around 341 K (68 °C). In this work, through novel oxide‐metal nanocomposite designs (i.e., Au:VO2and Pt:VO2), a very broad range of SMT temperature tuning from≈323.5 to≈366.7 K has been achieved by varying the metallic secondary phase in the nanocomposites (i.e., Au:VO2and Pt:VO2thin films, respectively). More surprisingly, the SMTTccan be further lowered to≈301.8 K (near room temperature) by reducing the Au particle size from 11.7 to 1.7 nm. All the VO2nanocomposite thin films maintain superior phase transition performance, i.e., large transition amplitude, very sharp transition, and narrow width of thermal hysteresis. Correspondingly, a twofold variation of the complex dielectric function has been demonstrated in these metal‐VO2nanocomposites. The wide range physical property tuning is attributed to the band structure reconstruction at the metal‐VO2phase boundaries. This demonstration paved a novel approach for tuning the phase transition property of Mott‐insulating materials to near room temperature transition, which is important for sensors, electrical switches, smart windows, and actuators. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email