High energy density lithium-O2 batteries have potential to increase electric vehicle driving range, but commercialization is prevented by technical challenges. Researchers have proposed electrolytes, catalysts, and binders to improve the battery capacity and reduce capacity fade. Novel battery design, however, is not always consistent with reduction in greenhouse gas (GHG) emissions. Optimizing battery design using solely electrochemical metrics ignores variations in the environmental impacts of different materials. The lack of uniform reporting practices further complicates such efforts. This paper presents commonly used lithium-O2 battery materials along with their GHG emissions. We use LCA methodology to estimate GHG emissions for five proposed lithium-O2 battery designs: (i) without catalyst, (ii) with catalyst, (iii) carbon-less and binder-less, (iv) anode protection, and (v) carbon-less, binder-less with gold catalyst. This work highlights knowledge gaps in lithium-O2 battery LCA, provides a benchmark to quantify battery composition impacts, and demonstrates the GHG emissions associated with certain materials and designs for laboratory-scale batteries. Predicted GHG emissions range from 10–70 kg of CO2 equivalent (kg CO2𝑒) kg−1 of battery, 60–1200 kg CO2𝑒 kWh−1, and 0.15–21 kg CO2𝑒 per km of vehicle travel, if battery replacement is considered.
more »
« less
Applying life cycle analysis for materials selection in Li-O2 batteries
AbstractGreenhouse gas emission reduction is often cited as a reason for high energy density, next-generation battery development. As lithium-O2battery research has progressed, researchers have examined the potential of many novel materials in the drive to reduce parasitic reactions and increase capacity. While the field has made great strides towards producing more reliable batteries, there has been little verification that lithium-O2batteries will reduce net environmental impacts. This paper examines how material selection ultimately impacts lithium-O2battery environmental impacts. Given that researchers should not wait until lithium-O2batteries reach commercialization to assess their environmental impact, this paper describes how to incorporate LCA as an integral part of the battery design process. Furthermore, it provides impact factors of many relevant materials to increase the ease of LCA for the field. <bold>Graphic abstract</bold>
more »
« less
- Award ID(s):
- 1903440
- PAR ID:
- 10435612
- Publisher / Repository:
- Cambridge University Press (CUP)
- Date Published:
- Journal Name:
- MRS Advances
- Volume:
- 8
- Issue:
- 15
- ISSN:
- 2059-8521
- Format(s):
- Medium: X Size: p. 803-810
- Size(s):
- p. 803-810
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract All‐solid‐state batteries have the potential for enhanced safety and capacity over conventional lithium ion batteries, and are anticipated to dominate the energy storage industry. As such, strategies to enable recycling of the individual components are crucial to minimize waste and prevent health and environmental harm. Here, we use cold sintering to reprocess solid‐state composite electrolytes, specifically Mg and Sr doped Li7La3Zr2O12with polypropylene carbonate (PPC) and lithium perchlorate (LLZO−PPC−LiClO4). The low sintering temperature allows co‐sintering of ceramics, polymers and lithium salts, leading to re‐densification of the composite structures with reprocessing. Reprocessed LLZO−PPC−LiClO4exhibits densified microstructures with ionic conductivities exceeding 10−4 S/cm at room temperature after 5 recycling cycles. All‐solid‐state lithium batteries fabricated with reprocessed electrolytes exhibit a high discharge capacity of 168 mA h g−1at 0.1 C, and retention of performance at 0.2 C for over 100 cycles. Life cycle assessment (LCA) suggests that recycled electrolytes outperforms the pristine electrolyte process in all environmental impact categories, highlighting cold sintering as a promising technology for recycling electrolytes.more » « less
-
Electrified aircraft have gained traction as a promising approach to emissions abatement in the aviation sector. This transition will require overcoming numerous technical challenges related to increasing battery energy density, as well as logistic challenges related to the lithium supply chain, which is already stressed due to high demand for electric vehicles. We have estimated that lithium demand for electrified aviation may raise lithium demand in the range of 10–250%. The uncertainty in these estimates show the importance of quantifying the impacts of electrified aviation and designing batteries to mitigate additional demand. In addition, most reviews on electrified aviation do not include information on the localized social and environmental impacts caused by lithium demand, despite their importance to enabling technology necessary for emissions reductions. This review seeks to fill this gap by presenting an overview of environmental and social research in context with one another to encourage researchers in the field to consider these dynamics as part of electrified aircraft design. Given that the high energy density batteries necessary to enable large-scale electrification of aircraft are still under development, continued progress in this field should emphasize sustainable governance for lithium extraction and a circular battery economy to reduce social and environmental stressors.more » « less
-
Ever-increasing demands for energy, particularly being environmentally friendly have promoted the transition from fossil fuels to renewable energy.1Lithium-ion batteries (LIBs), arguably the most well-studied energy storage system, have dominated the energy market since their advent in the 1990s.2However, challenging issues regarding safety, supply of lithium, and high price of lithium resources limit the further advancement of LIBs for large-scale energy storage applications.3Therefore, attention is being concentrated on an alternative electrochemical energy storage device that features high safety, low cost, and long cycle life. Rechargeable aqueous zinc-ion batteries (ZIBs) is considered one of the most promising alternative energy storage systems due to the high theoretical energy and power densities where the multiple electrons (Zn2+) . In addition, aqueous ZIBs are safer due to non-flammable electrolyte (e.g., typically aqueous solution) and can be manufactured since they can be assembled in ambient air conditions.4As an essential component in aqueous Zn-based batteries, the Zn metal anode generally suffers from the growth of dendrites, which would affect battery performance in several ways. Second, the led by the loose structure of Zn dendrite may reduce the coulombic efficiency and shorten the battery lifespan.5 Several approaches were suggested to improve the electrochemical stability of ZIBs, such as implementing an interfacial buffer layer that separates the active Zn from the bulk electrolyte.6However, the and thick thickness of the conventional Zn metal foils remain a critical challenge in this field, which may diminish the energy density of the battery drastically. According to a theretical calculation, the thickness of a Zn metal anode with an areal capacity of 1 mAh cm-2is about 1.7 μm. However, existing extrusion-based fabrication technologies are not capable of downscaling the thickness Zn metal foils below 20 μm. Herein, we demonstrate a thickness controllable coating approach to fabricate an ultrathin Zn metal anode as well as a thin dielectric oxide separator. First, a 1.7 μm Zn layer was uniformly thermally evaporated onto a Cu foil. Then, Al2O3, the separator was deposited through sputtering on the Zn layer to a thickness of 10 nm. The inert and high hardness Al2O3layer is expected to lower the polarization and restrain the growth of Zn dendrites. Atomic force microscopy was employed to evaluate the roughness of the surface of the deposited Zn and Al2O3/Zn anode structures. Long-term cycling stability was gauged under the symmetrical cells at 0.5 mA cm-2for 1 mAh cm-2. Then the fabricated Zn anode was paired with MnO2as a full cell for further electrochemical performance testing. To investigate the evolution of the interface between the Zn anode and the electrolyte, a home-developed in-situ optical observation battery cage was employed to record and compare the process of Zn deposition on the anodes of the Al2O3/Zn (demonstrated in this study) and the procured thick Zn anode. The surface morphology of the two Zn anodes after circulation was characterized and compared through scanning electron microscopy. The tunable ultrathin Zn metal anode with enhanced anode stability provides a pathway for future high-energy-density Zn-ion batteries.Obama, B., The irreversible momentum of clean energy.Science2017,355(6321), 126-129.Goodenough, J. B.; Park, K. S., The Li-ion rechargeable battery: a perspective.J Am Chem Soc2013,135(4), 1167-76.Li, C.; Xie, X.; Liang, S.; Zhou, J., Issues and Future Perspective on Zinc Metal Anode for Rechargeable Aqueous Zinc‐ion Batteries.Energy & Environmental Materials2020,3(2), 146-159.Jia, H.; Wang, Z.; Tawiah, B.; Wang, Y.; Chan, C.-Y.; Fei, B.; Pan, F., Recent advances in zinc anodes for high-performance aqueous Zn-ion batteries.Nano Energy2020,70.Yang, J.; Yin, B.; Sun, Y.; Pan, H.; Sun, W.; Jia, B.; Zhang, S.; Ma, T., Zinc Anode for Mild Aqueous Zinc-Ion Batteries: Challenges, Strategies, and Perspectives.Nanomicro Lett2022,14(1), 42.Yang, Q.; Li, Q.; Liu, Z.; Wang, D.; Guo, Y.; Li, X.; Tang, Y.; Li, H.; Dong, B.; Zhi, C., Dendrites in Zn-Based Batteries.Adv Mater2020,32(48), e2001854. Acknowledgment This work was partially supported by the U.S. National Science Foundation (NSF) Award No. ECCS-1931088. S.L. and H.W.S. acknowledge the support from the Improvement of Measurement Standards and Technology for Mechanical Metrology (Grant No. 22011044) by KRISS. Figure 1more » « less
-
Abstract Manufacturing sustainable sodium ion batteries with high energy density and cyclability requires a uniquely tailored technology and a close attention to the economical and environmental factors. In this work, we summarized the most important design metrics in sodium ion batteries with the emphasis on cathode materials and outlined a transparent data reporting approach based on common metrics for performance evaluation of future technologies. Sodium-ion batteries are considered as one of the most promising alternatives to lithium-based battery technologies. Despite the growing research in this field, the implementation of this technology has been practically hindered due to a lack of high energy density cathode materials with a long cycle-life. In this perspective, we first provide an overview of the milestones in the development of Na-ion battery (NIB) systems over time. Next, we discuss critical metrics in extraction of key elements used in NIB cathode materials which may impact the supply chain in near future. Finally, in the quest of most promising cathode materials for the next generation of NIBs, we overlay an extensive perspective on the main findings in design and test of more than 295 reports in the past 10 years, exhibiting that layered oxides, Prussian blue analogs (PBAs) and polyanions are leading candidates for cathode materials. An in-depth comparison of energy density and capacity retention of all the currently available cathode materials is also provided. In this perspective, we also highlight the importance of large data analysis for sustainable material design based on available datasets. The insights provided in this perspective, along with a more transparent data reporting approach and an implementation of common metrics for performance evaluation of NIBs can help accelerate future cathode materials design in the NIB field. Graphical abstractmore » « less