Phase pure PbZr 0.52 Ti 0.48 O 3 (PZT) films with up to 13 mol. % Nb were prepared on Pt-coated Si substrates using chemical solution deposition; charge compensation for Nb was accomplished by reducing the concentration of lead in the film. For high Nb doping levels, (1) superoxidation of the PZT film surface makes the PZT/Pt interface more p-type and, hence reduces electron injection over the Schottky barrier, (2) the bulk charge transport mechanism changes from electron trapping by Ti 4+ to hole migration between lead vacancies, and (3) the ionic conductivity due to migration of oxygen vacancies decreases. For [Formula: see text] Nb, electrical degradation was controlled via field-induced accumulation of oxygen vacancies near the cathode, which, in turn, leads to Schottky barrier lowering and electron trapping by Ti 4+ . In phase pure 13 mol. % Nb doped PZT films, on the other hand, the increase in the leakage current during electrical degradation was dominated by hole migration between lead vacancies ([Formula: see text]. A much lower lifetime and drastic increase in the leakage current upon electrical degradation was observed in mixed phase PNZT films, which was attributed to (1) a more electrically conductive pyrochlore phase and (2) a high concentration of lead vacancies.
more »
« less
Cracking behavior in lead zirconate titanate films with different Zr/Ti ratios
Crack initiation stresses for different lead zirconate titanate (PZT) film compositions were investigated. PZT/Pt/TiO2/SiO2/Si stacks with 2.0 μm thick {100} oriented PZT films at the morphotropic phase boundary (MPB) showed a characteristic strength of 1137 MPa, and the film thickness served as the limiting flaw size for failure of the film/substrate stack. In contrast, for Zr/Ti ratios of 40/60 and 30/70, the characteristic stack strength increased while the Weibull modulus decreased to values typical for that of Si. This difference is believed to be due to toughening from ferroelasticity or phase switching. X-ray diffraction showed that the volume fraction of c-domains increased in Ti-rich compositions. This would allow for more switching from c to a-domains under biaxial tensile stress. Zr/Ti concentration gradients were present for all compositions, which contributed to the observation of a rhombohedral phase off the MPB. Due to the reduced tendency toward cracking, off-MPB compositions are potentially of interest in actuators, albeit with the trade-off of needing a high actuation voltage.
more »
« less
- Award ID(s):
- 1841453
- PAR ID:
- 10439896
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 121
- Issue:
- 16
- ISSN:
- 0003-6951
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Microwave-induced plasma was used to anneal precursor powders containing five metal oxides with carbon and boron carbide as reducing agents, resulting in high entropy boride ceramics. Measurements of hardness, phase structure, and oxidation resistance were investigated. Plasma annealing for 45 min in the range of 1500–2000 °C led to the formation of predominantly single-phase (Hf, Zr, Ti, Ta, Mo)B2 or (Hf, Zr, Nb, Ta, Mo)B2 hexagonal structures characteristic of high entropy borides. Oxidation resistance for these borides was improved by as much as a factor of ten when compared to conventional commercial diborides. Vickers and nanoindentation hardness measurements show the indentation size effect and were found to be as much as 50% higher than that reported for the same high entropy boride configuration made by other methods, with average values reaching up to 38 GPa (for the highest Vickers load of 200 gf). Density functional theory calculations with a partial occupation method showed that (Hf, Zr, Ti, Ta, Mo)B2 has a higher hardness but a lower entropy forming ability compared to (Hf, Zr, Nb, Ta, Mo)B2, which agrees with the experiments. Overall, these results indicate the strong potential of using microwave-induced plasma as a novel approach for synthesizing high entropy borides.more » « less
-
Lead zirconate titanate (PZT) thin films offer advantages in microelectromechanical systems (MEMSs) including large motion, lower drive voltage, and high energy densities. Depending on the application, different substrates are sometimes required. Self-heating occurs in the PZT MEMS due to the energy loss from domain wall motion, which can degrade the device performance and reliability. In this work, the self-heating of PZT thin films on Si and glass and a film released from a substrate were investigated to understand the effect of substrates on the device temperature rise. Nano-particle assisted Raman thermometry was employed to quantify the operational temperature rise of these PZT actuators. The results were validated using a finite element thermal model, where the volumetric heat generation was experimentally determined from the hysteresis loss. While the volumetric heat generation of the PZT films on different substrates was similar, the PZT films on the Si substrate showed a minimal temperature rise due to the effective heat dissipation through the high thermal conductivity substrate. The temperature rise on the released structure is 6.8× higher than that on the glass substrates due to the absence of vertical heat dissipation. The experimental and modeling results show that the thin layer of residual Si remaining after etching plays a crucial role in mitigating the effect of device self-heating. The outcomes of this study suggest that high thermal conductivity passive elastic layers can be used as an effective thermal management solution for PZT-based MEMS actuators.more » « less
-
Abstract Scanning Probe Microscopy (SPM) based techniques probe material properties over microscale regions with nanoscale resolution, ultimately resulting in investigation of mesoscale functionalities. Among SPM techniques, piezoresponse force microscopy (PFM) is a highly effective tool in exploring polarization switching in ferroelectric materials. However, its signal is also sensitive to sample‐dependent electrostatic and chemo‐electromechanical changes. Literature reports have often concentrated on the evaluation of theOff‐fieldpiezoresponse, compared toOn‐fieldpiezoresponse, based on the latter's increased sensitivity to non‐ferroelectric contributions. Using machine learning approaches incorporatingboth Off‐andOn‐fieldpiezoresponse response as well asOff‐fieldresonance frequency to maximize information, switching piezoresponse in a defect‐rich Pb(Zr,Ti)O3thin film is investigated. As expected, one major contributor to the piezoresponse is mostly ferroelectric, coupled with electrostatic phenomena duringOn‐fieldmeasurements. A second component is electrostatic in nature, while a third component is likely due to a superposition of multiple non‐ferroelectric processes. The proposed approach will enable deeper understanding of switching phenomena in weakly ferroelectric samples and materials with large chemo‐electromechanical response.more » « less
-
Abstract Ferroelectric films suffer from both aging and degradation under high ac‐field drive conditions due to loss of polarization with time. In this study, the roles of defect chemistry and internal electric fields on the long‐term stability of the properties of piezoelectric films were explored. For this purpose, lead zirconate titanate (PZT) films with a Zr/Ti ratio of 52/48 doped with Mn‐ (PMZT) or Nb‐ (PNZT) were deposited on Pt coated Si substrates by the sol‐gel method. It was demonstrated that the magnitude of the internal field is much higher in PMZT films compared to PNZT films after poling in the temperature range of 25‐200°C under an electric field of −240 kV/cm. The development of the internal field is thermally activated, with activation energies from 0.5 ± 0.06 to 0.8 ± 0.1 eV in Mn doped films and from 0.8 ± 0.1 to 1.2 ± 0.2 eV in Nb doped films. The different activation energies for imprint suggests that the physical mechanism underlying the evolution of the internal field in PMZT and PNZT films differs; the enhanced internal field upon poling is attributed to (a) alignment of oxygen vacancy—acceptor ion defect dipoles (,) in PMZT films, and (b) thermionic injection of electron charges and charge trapping in PNZT films. In either case, the internal field reduces back switching, enhances the remanent piezoelectric properties, and dramatically improves the aging behavior. PMZT films exhibited the greatest enhancement, with reduced high temperature (180°C) aging rates of 2%‐3%/decade due to improved stability of the poled state. In contrast, PNZT films showed significantly larger high temperature aging rates (15.5%/decade) in the piezoelectric coefficient, demonstrating that the fully poled state was not retained with time.more » « less